Propenyl elastomer composition and preparation method thereof
A technology of propylene-based elastomer and composition, which is applied in the field of propylene-based elastomer composition and preparation, can solve the problems of lack of competitiveness, low filling ability and high preparation cost, and achieves reduction of cost, improvement of reaction degree and improvement of stability Effect
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Examples
Example Embodiment
[0018] Example 1:
[0019] A propylene-based elastomer composition comprising 75 parts of propylene-based elastomer, 5 parts of foaming agent, 2 parts of ethylene propylene rubber, 3 parts of triallyl isocyanurate, and propylene The base elastomer includes 60 parts of propylene and 40 parts of ethylene. The performance characteristics of the propylene-based elastomer are based on ASTM D-1238, measured at 190°C / 2.16Kg, with a melt flow rate of 1.8-4.2g / 10min.
Example Embodiment
[0020] Example 2:
[0021] A propylene-based elastomer composition, in terms of parts by weight, comprises 86 parts of propylene-based elastomer, 9 parts of foaming agent, 5 parts of EPDM rubber, 9 parts of triallyl isocyanurate, and propylene The base elastomer includes 75 parts of propylene and 25 parts of ethylene. The performance characteristics of the propylene-based elastomer are based on ASTM D-1238, a melt flow rate of 1.8 to 4.2 g / 10 min measured at 190°C / 2.16 Kg.
Example Embodiment
[0022] Example 3:
[0023] A propylene-based elastomer composition comprising 80 parts of propylene-based elastomer, 7 parts of foaming agent, 4 parts of ethylene propylene rubber, and 6 parts of triallyl isocyanurate according to the ratio of parts by weight. The base elastomer includes 70 parts of propylene and 30 parts of ethylene. The performance characteristic of the propylene-based elastomer is a melt flow rate of 1.8-4.2 g / 10min measured according to ASTM D-1238, 190°C / 2.16Kg.
[0024] Further, the propylene-based elastomer has a molecular weight distribution (Mw / Mn) less than 3.2.
[0025] Further, the foaming agent is preferably sodium bicarbonate.
[0026] A preparation method of propylene-based elastomer composition includes the following steps:
[0027] a. Weigh propylene-based elastomer, foaming agent, EPDM and triallyl isocyanurate according to the weight ratio;
[0028] b. Put the material weighed in step a into the internal mixer for mixing;
[0029] c. After the second m...
PUM
Property | Measurement | Unit |
---|---|---|
The melt flow rate | aaaaa | aaaaa |
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap