Archaized surface artistic concrete and preparation method thereof
A kind of concrete and artistic technology, which is applied in the field of antique surface artistic concrete and its preparation, can solve the problems of less research on artistic concrete, achieve the effect of increased perception and artistry, and better decorative effects
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Examples
Embodiment 1
[0026] An antique surface art concrete and a preparation method thereof, which are composed of the following raw materials by mass percentage: 30.08% cement, 30.08% quartz sand, 15.04% stone powder, 15.04% aggregate particles, 0.24% pigment, 0.75% water reducer, Defoamer 0.06%, water 8.72%.
[0027] In this embodiment, the cement is white Portland cement; the quartz sand is a mixture of two specifications of quartz sand of 48-100 mesh and 100-300 mesh, and the content of each component is: 48-100 mesh quartz Sand 72%, 100-300 mesh quartz sand 28%; stone powder is 0-2mm dolomite powder; aggregate particles are black stone particles with a particle size of 3-4mm; pigment is yellow iron oxide pigment; water reducer is polycarboxylic acid It is a water reducer; the defoamer is a silicone defoamer.
[0028] The preparation method comprises the following steps:
[0029] First put cement, quartz sand, stone powder, aggregate particles and pigments in the mixer for premixing for 3 m...
Embodiment 2
[0035] An antique surface art concrete and a preparation method thereof, which are composed of the following raw materials by mass percentage: 36.81% cement, 14.72% quartz sand, 22.09% stone powder, 14.72% aggregate particles, 0.18% pigment, 1.10% water reducer, Defoamer 0.06%, water 10.31%.
[0036] In this embodiment, the cement is white Portland cement; the quartz sand is a mixture of two specifications of quartz sand of 48-100 mesh and 100-300 mesh, and the content of each component is: 48-100 mesh quartz Sand 64%, 100-300 mesh quartz sand 36%; stone powder is sesame white granite stone powder of 0-2mm; aggregate particle is sesame gray granite particle with particle size of 4-6mm; pigment is black iron oxide pigment; water reducer is Polycarboxylate water reducer; defoamer is silicone defoamer.
[0037] The preparation method comprises the following steps:
[0038] Put cement, quartz sand, stone powder, aggregate particles and pigments in the mixer for pre-mixing for 4 ...
Embodiment 3
[0044] An antique surface art concrete and a preparation method thereof, comprising the following raw materials in terms of mass percentage: 22.83% cement, 29.68% quartz sand, 15.98% stone powder, 18.26% aggregate particles, 0.23% pigment, and 13.01% water.
[0045] In this embodiment, the cement is ordinary Portland cement; the quartz sand is a mixture of two specifications of quartz sand of 48-100 mesh and 100-300 mesh, and the content of each component is: 48-100 mesh quartz Sand 78%, 100-300 mesh quartz sand 22%; stone powder is 0-2mm dolomite powder; aggregate particle is 5-8mm particle size dolomite particle; pigment is black iron oxide pigment.
[0046] The preparation method comprises the following steps:
[0047] First put cement, quartz sand, stone powder, aggregate particles and pigments in a mixer for premixing for 3 minutes, then add water to the mixer and then perform secondary mixing for 8 minutes, and obtain a uniform mixture after the mixing is completed;
[...
PUM
Property | Measurement | Unit |
---|---|---|
Particle size | aaaaa | aaaaa |
Particle size | aaaaa | aaaaa |
Particle size | aaaaa | aaaaa |
Abstract
Description
Claims
Application Information
![application no application](https://static-eureka.patsnap.com/ssr/23.2.0/_nuxt/application.06fe782c.png)
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap