A manufacturing method and technology of mesh cages, applied in manufacturing tools, supply devices, building components, etc., can solve problems such as high production difficulty and cracks, and achieve the effect of improving the success rate

Active Publication Date: 2022-08-05
山东晟阳新型建材有限公司
View PDF8 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

When the applicant first started to produce 100mm thick plates, almost all the molds had cracks, and the molds were all labeled as defective products. The yield rate was basically 0%, and the production difficulty was extremely high.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of combined mesh cage and method for making alc board using the same
  • A kind of combined mesh cage and method for making alc board using the same
  • A kind of combined mesh cage and method for making alc board using the same

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0037] see figure 1 and figure 2 , figure 1 and figure 2 The structural diagram of the combined mesh cage shown in this embodiment, the length of the mesh cage is set according to the length of the mold car and the production plan. The length of the general mold car is 6m, and the length of the ALC sheet with a thickness of 100mm is generally shorter. Two or three mesh cages are placed in the mold car as needed, and some mesh cages are used to make 100mm thick ALC sheets.

[0038] Further, each mesh cage includes several mesh sheets and steel brazing 3, the mesh density is designed according to the thickness of the ALC plate, the lower end of the steel brazing 3 is connected with the mesh, and the upper end is stuck on the outside of the brazing frame, and the steel brazing is rotated by rotating the steel brazing. 3. The lower part of the steel drill 3 can be separated from the mesh, and the drill frame is fixed on the upper end of the mounting frame 1. see figure 1 Th...

Embodiment 2

[0055] see Figure 4 , the die-cutting drill 10 comprises a cylindrical rod, and a number of barbs 101 are arranged on the outer wall of the rod body. The barbs 101 are thorn protrusions, which can destroy the die-cutting drill 10 when the die-cutting drill 10 is pulled out. The surrounding embryo body tissue can better release the internal stress inside the embryo body, which is convenient for subsequent cutting.

[0056] Other features not mentioned in this embodiment may be the same as those in Embodiment 1, and will not be described again.

Embodiment 3

[0058] see Figure 5 , the lower cone head 102 is also provided with a steel wire through hole 103 for fixing the cutting wire 4 .

[0059] Other features not mentioned in this embodiment may be the same as those in Embodiment 1, and will not be described again.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
hardnessaaaaaaaaaa
diameteraaaaaaaaaa
Login to View More

Abstract

A combination net cage, including more than two net cages, each net cage includes several nets and steel (3).Rotating steel (3) can be separated from the lower part of the steel (3) from the mesh.(10), the top of the cutting mold (10) is connected to the rack, and the lower part is connected to the cut rope.This combination net cage adds the cutting mold and cutting rope, and limits the ALC embryo to the hardness of a special range. It can use the cutting rope to cut the embryo in advance, release the internal stress of the ALC embryo in advance, and put the embryo body.The crack is limited to a specific unloading area, which can stabilize the 100mm thick plate, which greatly improves the success rate of 100mm thick ALC plate production.

Description

technical field [0001] The invention relates to the technical field of manufacturing new building materials, in particular to a combined mesh cage. Background technique [0002] ALC is the abbreviation of Autoclaved Lightweight Concrete, which is a kind of high-performance autoclaved aerated concrete (ALC). ALC board is made of fly ash (or silica sand), cement, lime, etc. as the main raw materials, and is a porous concrete forming board (including treated steel reinforcement) that is cured by high pressure steam. ALC board can be used as both wall material and roof board. It is a new type of building material with superior performance and has a wide range of applications at home and abroad. [0003] Among various ALC sheet sizes, 100mm thick sheets are rarely willing to do in the same industry in China, because in the production process of 100mm thick sheets, it is generally necessary to hang double nets and make them together with other sizes of ALC sheets. , Small cracks...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): E04C5/06B28B13/02B28B23/04B28B11/14B28B11/24
CPCE04C5/06B28B13/02B28B23/04B28B11/245B28B11/14
Inventor 刘虎城
Owner 山东晟阳新型建材有限公司