Looking for breakthrough ideas for innovation challenges? Try Patsnap Eureka!

A kind of preparation method and application of acid process cold box resin for casting

A cold core box and resin technology, which is used in casting molding equipment, cores, molds, etc., can solve the problems of burrs, toxic triethylamine, and poor surface quality in castings, so as to improve strength, reduce harmful components, and improve production efficiency. Efficient effect

Active Publication Date: 2021-09-24
安徽省含山县威建铸造厂(普通合伙)
View PDF10 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The core sand of the triethylamine cold box method has good fluidity and the casting surface is smooth, but triethylamine is poisonous, and precautionary measures should be strengthened
However, because the resin and catalyst used are harmful to the human body; the poured castings often produce burrs, and the surface quality is poor
Therefore, the development of this core making method is relatively slow

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of preparation method and application of acid process cold box resin for casting

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0019] The first step, weigh the following raw materials according to the parts by weight: 42 parts of modified benzoxazine resin, 33 parts of chloroether resin, 15 parts of L-lysine diisocyanate, 22 parts of maleic anhydride, polyester resin 11 parts of softening agent, 3 parts of catalyst dibenzoyl peroxide and 1 part of sand surface modifier 2-methacrylic acid chromium chloride; the second step, resin slurry: add chlorine ether resin and maleic anhydride In the pulverizer, pulverize for 30 minutes, then pour the mixture into a high-speed mixer, add diisocyanate, catalyst, and polyester resin softener into the high-speed mixer according to the formula, and fully stir for 10 minutes to obtain a resin slurry; the third step , the resin slurry and the modified benzoxazine resin are fully mixed and stirred evenly to obtain final product. The preparation method of the modified benzoxazine is as follows: 12.8 parts of phenol, 8 parts of paraformaldehyde and 18 parts of 4- 01.1 par...

Embodiment 2

[0023]The first step, weigh the following raw materials according to the parts by weight: 39 parts of modified benzoxazine resin, 31 parts of chloroether resin, 13 parts of toluene diisocyanate, 19 parts of maleic anhydride, 9 parts of polyester resin softener , 1 part of catalyst azobisisobutyronitrile and 0.5 part of sand surface modifier vinyl benzyl aminoethyl trimethoxysilane hydrochloride; the second step, resin slurry: dichloroether resin, maleic butene di Add the acid anhydride into the pulverizer, pulverize for 20 minutes, then pour the mixture into a high-speed mixer, add diisocyanate, catalyst, and polyester resin softener into the high-speed mixer according to the formula, and fully stir for 10 minutes to obtain a resin slurry; Three steps, the resin slurry and the modified benzoxazine resin are fully mixed and stirred evenly, and the preparation method of the modified benzoxazine is as follows: 11.5 parts of phenol, 7 parts of paraformaldehyde and 17 parts of 0.6 ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a method for preparing an acid-process cold box resin for casting and its application. The invention belongs to the technical field of casting materials. The cold box resin for casting prepared by the preparation method disclosed in the invention has high production efficiency and energy saving , the sand core has high dimensional accuracy, low gas generation, long life of the core box, small deformation, smooth surface of the casting, high dimensional accuracy and small gas generation, non-toxic and tasteless, and has unique high temperature characteristics. The sand core made of cold box resin is It has secondary hardening characteristics when pouring at high temperature. It adopts acid curing gas source, such as acetic acid, oxalic acid, etc., and it is naturally decomposed, non-toxic and harmless, so it can prevent castings from defects such as hot cracks and burrs. Cold box resin no-bake sand has relatively low Low gas generation and good collapsibility.

Description

technical field [0001] The invention relates to the technical field of casting materials, in particular to a preparation method and application of an acid-process cold box resin for casting. Background technique [0002] Cold box resin sand is different from hot box resin sand. Cold box resin sand hardens the core sand in the core box by blowing gas or aerosol hardener at room temperature. Triethylamine cold box method, the binder is composed of thermoplastic liquid phenolic resin, toluene diisocyanate and amine catalyst. Generally speaking, the ratio of liquid phenolic resin and toluene dipolyisocyanate is 1:1, and the total amount of the two binders is 1.5% to 2.0% of the sand mass. After core shooting, triethylamine gas mist is blown in to harden the sand core. The core sand of the triethylamine cold box method has good fluidity and the surface of the casting is smooth and clean, but triethylamine is poisonous, and precautionary measures should be strengthened. "Cold bo...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): B22C1/22C08F259/04C08F222/06C08G14/12
CPCB22C1/2226B22C1/2233B22C1/2266C08F259/04C08G14/12C08F222/06
Inventor 徐正平徐正东
Owner 安徽省含山县威建铸造厂(普通合伙)
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More