Device and method for preparing glow discharge sputtering sample for microscopic characterization of material

Abstract

The invention relates to a device and a method for preparing a glow discharge sputtering sample for microscopic characterization of a material. The device comprises a glow discharge sputtering unit, aglow discharge energy supply source, an automatic gas circuit control unit, a spectrograph and a computer, wherein a glow discharge sputtering unit structure is more suitable for sample preparation through simulation optimization, and uniform sample sputtering on the surface of a sample in a large-size range is realized by applying a magnetic field to glow plasma; and the spectrograph is used formonitoring element spectral signals in the sputtering depth direction of the sample so as to realize accurate preparation of tissue structures of different layers. By combining the sample position mark and the acquisition of accurate space coordinate (x, y, z) information, the correspondence between the space coordinate of the sample preparation surface and the tissue structure is realized. Thus,large-size flat preparation of the sample at the millimeter-cm level can be achieved, no damage is caused to the material tissue structure, layer-by-layer preparation can be conducted in the depth direction of the surface of the sample, preparation is rapid, and the cost is low.

Description

technical field [0001] The invention belongs to the technical field of material analysis and characterization, and relates to a device and method for preparing glow discharge sputtering samples for material microscopic characterization. Background technique [0002] The current sample preparation techniques used for material microstructure characterization, such as mechanical polishing, electrolytic polishing, and focused ion beam (FIB), have the disadvantages of long time consumption, damage to the sample surface, difficult control of polishing conditions, small sample preparation area, and high cost. High-level shortcomings, can not fully meet the needs of large-scale, overall, real information acquisition of the sample microstructure. [0003] Glow discharge belongs to a kind of low-pressure gas discharge, as an effective atomization and excitation light source, it is mostly used for elemental analysis of solid materials. The sample atoms are stripped layer by layer from...

AI Technical Summary

Problems solved by technology

At the same time, this existing technology uses radio frequency glow discharge mass spectrometer for analysis and detection, instead of using glow discharge technology for sample preparation to achieve layer-by-layer erosion of material microstructure

[0006] At present, the most commonly used method for exfoliating the microstructure of mate