Mfg. method of cals photocatalyst for hydrogen prodn and method for generating hydrogen therewith
A manufacturing method and photocatalyst technology, which are applied in the directions of cadmium sulfide, chemical instruments and methods, hydrogen production, etc., can solve the problems of insufficient hydrogen activity and increase in the amount of hydrogen generated, and achieve enhanced sintering time, simple manufacturing process, and long catalyst life. Effect
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Examples
Example
[0051] Specific embodiments (manufacturing examples 1 to 7)
[0052] Mix 125ml of water and CdSO with stirring 4 ·2H 2 O and promoter K 2 Cr 2 O 7 And reactant H 2 S, make it have the composition described in Table 1 below, until precipitation appears. The resulting mixture was stirred and the precipitate was CdCrS precipitate.
[0053] After washing the precipitate with water to pH=7, it was thoroughly washed, and then vacuum-dried at 130°C under a nitrogen stream for 2 hours to obtain CdCrS powder.
[0054] To this dried CdCrS powder is added Ni(NO 3 ) 2 ·6H 2 O, after the Ni content reaches 1% by weight, 6-7 drops of concentrated hydrochloric acid are slowly added dropwise to it with sufficient stirring. The resulting slurry is treated with ultrasound for 3 minutes, dried at 130°C for 2 hours, and then placed in an oxidizing atmosphere at 360°C. After sintering for 4 hours and then sintering in a reducing atmosphere at 360°C for 4 hours, Ni(1 wt%) / Cd[Cr(0.2)]S...
Example
Preparation Example 8
[0055] Except for sintering in an oxidizing atmosphere at 360°C for 2 hours, and then sintering in a reducing atmosphere at 360°C for 2 hours, the same procedure as in Production Example 1 was carried out to obtain the photocatalyst Ni (1 wt%) / Cd[Cr (0.2)]S. (Manufacturing Example 9)
Example
Preparation Example 9
[0056] Except for sintering in an oxidizing atmosphere at 360°C for 2.5 hours, and then sintering in a reducing atmosphere at 360°C for 2.5 hours, the same procedure as in Production Example 1 was carried out to obtain the photocatalyst Ni (1 wt%) / Cd[Cr (0.2)]S. (Manufacturing Example 10)
PUM
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap