Manufacturing process for synthesizing sculpture by using natural perfume

A technology for making crafts and natural flavors, applied in decorative art, decorative structures, etc., can solve the problems of easy aging, not environmental protection, and sculptures without fragrance, etc., and achieve the effect of good pressure resistance and simple production

Inactive Publication Date: 2021-01-01
介休市恒瑞制香有限公司
View PDF5 Cites 3 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0002] Our commonly used sculpture materials mainly include stone, metal, wood, ceramics, etc. The other is chemical composites such as resin, fiberglass, etc. The former is stable in performance but heavy, difficult to manufacture, and has high technical requirements, while the latter is light. , but the material performance is not stable, there are disadvantages such as easy aging and not environmental protection, and the sculptures made have no certain fragrance, so it is difficult to meet people's needs

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0013] A production process of synthetic sculpture with natural spices, the sculpture is made of mixture, the mixture includes the following raw materials: sandalwood, agarwood, thuja, angelica, clove, frankincense, spirit herb, benzoin, osmanthus, Spices such as fennel, nard pine, atractylodes, magnolia, borneol, etc.; the production process includes the following steps:

[0014] (1) Grind sandalwood, agarwood, thuja, angelica, clove, frankincense, spirit vanilla, benzoin, cinnamon, fennel, nard pine, atractylodes, magnolia, borneol and other spices, and adjust different proportions according to different proportions. scented powder, set aside;

[0015] (2) beating hemp silk into fiber powder with a length of 1mm-10mm, for subsequent use;

[0016] (3) Add 30% natural binder and 15% fiber powder in (2) to the powder of (1) to mix into 500g of mixed powder, and add 300g of pure water to stir in the mixer together, and the stirring time is Standby after 45min;

[0017] (4) Wr...

Embodiment 2

[0021] A production process of synthetic sculpture with natural spices, the sculpture is made of mixture, the mixture includes the following raw materials: sandalwood, agarwood, thuja, angelica, clove, frankincense, spirit herb, benzoin, osmanthus, Spices such as fennel, nard pine, atractylodes, magnolia, borneol, etc.; the production process includes the following steps:

[0022] (1) Grind sandalwood, agarwood, thuja, angelica, clove, frankincense, spirit vanilla, benzoin, cinnamon, fennel, nard pine, atractylodes, magnolia, borneol and other spices, and adjust different proportions according to different proportions. scented powder, set aside;

[0023] (2) beating hemp silk into fiber powder with a length of 1mm-10mm, for subsequent use;

[0024] (3) Add 30% natural binder and 15% fiber powder in (2) to the powder of (1) to mix into 500g of mixed powder, and add 320g of pure water to stir in the mixer together, and the stirring time is Standby after 45min;

[0025] (4) Wr...

Embodiment 3

[0029] A production process of synthetic sculpture with natural spices, the sculpture is made of mixture, the mixture includes the following raw materials: sandalwood, agarwood, thuja, angelica, clove, frankincense, spirit herb, benzoin, osmanthus, Spices such as fennel, nard pine, atractylodes, magnolia, borneol, etc.; the production process includes the following steps:

[0030] (1) Grind sandalwood, agarwood, thuja, angelica, clove, frankincense, spirit vanilla, benzoin, cinnamon, fennel, nard pine, atractylodes, magnolia, borneol and other spices, and adjust different proportions according to different proportions. scented powder, set aside;

[0031] (2) beating hemp silk into fiber powder with a length of 1mm-10mm, for subsequent use;

[0032] (3) Add 30% natural binder and 15% fiber powder in (2) to the powder of (1) to mix into 500g of mixed powder, and add 350g of pure water to stir in the mixer together, the stirring time is Standby after 45min;

[0033] (4) Wrap t...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
lengthaaaaaaaaaa
Login to view more

Abstract

The invention discloses a manufacturing process for synthesizing sculpture by using natural perfume. A sculpture is prepared from a mixture; and the mixture is prepared from sandalwood, agilawood, thuja sutchuenensis, angelica sinensis, clove, frankincense, lysimachia foenum-graecum hance, benzoin, shaved cinnamon bark, anise, rhizoma nardostachyos, rhizoma atractylodis, flos magnoliae, borneol and other perfume. The manufacturing process comprises the following steps of: respectively grinding the perfume into powder, and mixing powder with different fragrances according to different proportions for later use; beating hemp threads into fiber powder with the length of 1mm-10mm for later use; adding 30% of a natural adhesive and 15% of fiber powder into the powder, mixing to obtain mixed powder, adding 300g-350g of purified water, adding the mixed powder and the purified water into a stirrer, and stirring for 45 minutes for later use; and wrapping the mixed and stirred material in a wooden framework or a wooden sculpture, injecting the mixture into a sculpture mold, performing compression molding, demolding, and drying in the shade. Compared with the prior art, the sculpture has theadvantages that the sculpture is simple to manufacture, and has relatively good compression resistance, crack resistance and deformation resistance.

Description

technical field [0001] The invention relates to the technical field of sculpture production technology, in particular to a production process of synthetic sculpture with natural spices. Background technique [0002] Our commonly used sculpture materials mainly include stone, metal, wood, ceramics, etc. The other is chemical composites such as resin, fiberglass, etc. The former is stable in performance but heavy, difficult to manufacture, and has high technical requirements, while the latter is light. , but the material performance is unstable, and there are disadvantages such as easy aging and not being environmentally friendly, and the sculptures made do not have a certain fragrance, so it is difficult to meet people's needs. Contents of the invention [0003] The technical problem to be solved by the present invention is to overcome the above technical defects and provide a manufacturing process for synthetic sculpture with natural spices. [0004] In order to solve the...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): B44C3/06
CPCB44C3/06
Inventor 郭建美
Owner 介休市恒瑞制香有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap