2000MPa-grade hot-rolled steel plate for hot-stamped wheel rim and manufacturing method of 2000MPa-grade hot-rolled steel plate

A hot-rolled steel plate and hot-stamping technology, which is applied to the hot-rolled steel plate for hot-stamped wheel rims and its manufacturing field, can solve the problems of unsuitable wheel rims, not meeting the manufacturing requirements of automobile wheels, etc., and achieves good surface quality and reduced banding Microstructure and inclusion grade, effect of improving impact performance

Active Publication Date: 2021-01-26
ANGANG STEEL CO LTD
View PDF10 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, when traditional hot stamping steel is used for wheel manufacturing, there are generally problems in surface quality and impact performance, which do not meet the manufacturing requirements of automobile wheels, especially not suitable for the process that requires preforming to produce wheel rims before hot stamping.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • 2000MPa-grade hot-rolled steel plate for hot-stamped wheel rim and manufacturing method of 2000MPa-grade hot-rolled steel plate
  • 2000MPa-grade hot-rolled steel plate for hot-stamped wheel rim and manufacturing method of 2000MPa-grade hot-rolled steel plate
  • 2000MPa-grade hot-rolled steel plate for hot-stamped wheel rim and manufacturing method of 2000MPa-grade hot-rolled steel plate

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0032] Describe below in conjunction with specific embodiment:

[0033] See Table 1-3 for the specific composition, temperature regime, structure and performance of the steel plate of the five embodiments of the present invention. The mechanical properties of the steel plate after pre-deformation and hot stamping during the rim manufacturing process are shown in Table 4. The microstructure of embodiment 5 steel plate sees figure 1 , which are ferrite and pearlite; the structure of the steel plate after hot stamping is full martensitic structure, see figure 2 .

[0034] The chemical composition (wt, %) of the embodiment of the present invention of table 1

[0035]

[0036] The temperature system of the embodiment of the invention of table 2

[0037]

[0038] The organization and mechanical performance parameter of table 3 embodiment of the present invention

[0039]

[0040] Table 4 Mechanical properties after hot stamping of the embodiments of the present invent...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
tensile strengthaaaaaaaaaa
yield strengthaaaaaaaaaa
thicknessaaaaaaaaaa
Login to view more

Abstract

The invention discloses a 2000MPa-grade hot-rolled steel plate for a hot-stamped wheel rim and a manufacturing method of the 2000MPa-grade hot-rolled steel plate. The 2000MPa-grade hot-rolled steel plate comprises 0.36%-0.39% of C, 0.01%-0.10% of Si, 1.46%-1.70% of Mn, less than or equal to 0.010% of P, less than or equal to 0.004% of S, 0.015%-0.055% of Al, 0.041%-0.055% of Nb, 0.030%-0.050% of V, 0.26%-0.35% of Mo, 0.0041-0.006% of B, 0.035%-0.050% of of rare earth elements La+Ce, less than or equal to 0.003% of N, and the balance Fe and inevitable impurities.

Description

technical field [0001] The invention relates to a steel plate for automobiles, in particular to a hot-rolled steel plate for hot stamping wheel rims with good surface quality and impact performance and a manufacturing method thereof. Background technique [0002] In recent years, in order to meet the goals of safety, environmental protection and energy saving, automobile companies have put forward requirements for vehicle lightweight and collision safety. In order to meet the development needs of the automobile industry, iron and steel enterprises have continued to develop products such as high-strength steel, advanced high-strength steel, ultra-high-strength steel, and hot-formed steel, and correspondingly developed advanced deep-processing technologies for steel plates such as hot forming, hydroforming, and spinning. This ensures that high-performance materials are widely used in body manufacturing. As an important part of automobiles, the lightweight development of autom...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C22C38/02C22C38/04C22C38/06C22C38/12C22C33/04C21C7/00B22D11/115B21C37/02
CPCC22C38/002C22C38/005C22C38/02C22C38/04C22C38/06C22C38/12C22C33/04C21C7/0006C21C7/0056B22D11/115B21C37/02
Inventor 董毅时晓光孙成钱王俊雄韩楚菲刘仁东王进臣王洪海王鑫景鹤
Owner ANGANG STEEL CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap