Stain-free water-based industrial guardrail paint

A water-based, industrial technology, applied in the field of industrial paint, can solve the problems of poor chemical resistance, low solid content, insufficient hardness of the paint film, etc., achieve excellent water and solvent resistance, excellent abrasion resistance and hardness, and improve self-cleaning performance Effect

Inactive Publication Date: 2021-01-29
湖州汇邦环保科技有限公司
View PDF4 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] At present, most of the guardrails mainly use solvent-based industrial coatings, which release volatile organic compounds (Volatile Organic Compounds, VOC) during production and use, resulting in pollution. At present, they have become the main source of pollution in cities after cars, endangering the human body healthy
Water-based coatings are environmentally friendly coatings, but traditional water-based coatings have disadvantages such as insufficient film hardness, easy scratches, poor chemical resistance, low solid content, and thin film thickness.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0022] A non-staining water-based industrial guardrail paint, which is composed of A component and B component in a weight ratio of 15:1, and is prepared by mixing the A component and B component during use;

[0023] The A component includes: 95 parts of acrylic polyurethane emulsion, 3 parts of titanium dioxide, 28 parts of water-based epoxy soybean oil modified alkyd resin, 0.15 parts of neutralizing agent, 0.35 parts of Defoamer, 5 parts of coalescent, 0.4 parts of wetting and dispersing agent, 2.8 parts of film forming agent, 1.2 parts of thickener, 27 parts of deionized water;

[0024] The B component includes, in parts by weight, 65 parts of polyurea curing agent and 35 parts of polyethylene glycol.

[0025] The film-forming aid is starch. The neutralizing agent is dimethylethanolamine. The defoamer is a silicone defoamer. The film-forming agent is propylene glycol ether. The thickener is a polyurethane thickener.

[0026] The preparation method of the non-contamina...

Embodiment 2

[0032] A non-staining water-based industrial guardrail paint, which is composed of component A and component B in a weight ratio of 12:1, and is prepared by mixing component A and component B during use;

[0033] The A component includes 120 parts by weight of acrylic polyurethane emulsion, 1 part of titanium dioxide, 35 parts of water-based epoxy soybean oil modified alkyd resin, 0.1 part of neutralizer, 0.5 part of disinfectant Foaming agent, 3 parts of film-forming aid, 0.5 part of wetting and dispersing agent, 2 parts of film-forming agent, 2 parts of thickener, 20 parts of deionized water;

[0034] The B component includes: 70 parts of polyurea curing agent and 30 parts of polyethylene glycol in parts by weight.

[0035] The film-forming aid is starch. The neutralizing agent is dimethylethanolamine. The defoamer is a silicone defoamer. The film-forming agent is propylene glycol ether. The thickener is a polyurethane thickener.

[0036] The preparation method of the n...

Embodiment 3

[0042] A non-staining water-based industrial guardrail paint, which is composed of component A and component B in a weight ratio of 18:1, and is prepared by mixing component A and component B during use;

[0043] The A component includes: 80 parts of acrylic polyurethane emulsion, 5 parts of titanium dioxide, 20 parts of water-based epoxy soybean oil modified alkyd resin, 0.2 part of neutralizing agent, 0.2 part of Defoamer, 8 parts of coalescent, 0.3 parts of wetting and dispersing agent, 3 parts of film forming agent, 1 part of thickener, 30 parts of deionized water;

[0044] The B component includes, in parts by weight, 60 parts of polyurea curing agent and 40 parts of polyethylene glycol.

[0045] The film-forming aid is starch. The neutralizing agent is dimethylethanolamine. The defoamer is a silicone defoamer. The film-forming agent is propylene glycol ether. The thickener is a polyurethane thickener.

[0046] The preparation method of the non-contaminating water-ba...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention relates to a stain-free water-based industrial guardrail paint, an acrylic polyurethane emulsion is selected and matched with water-based epoxidized soybean oil modified alkyd resin anda propylene glycol ethyl ether film-forming agent, the obtained paint has excellent wear resistance and hardness, a polyurea curing agent is used, and the paint has the ultra-fast drying characteristic and has excellent water resistance and solvent resistance; and self-cleaning performance is good. In order to further improve the self-cleaning performance of the paint, polyethylene glycol is further added, although the proportion of polyethylene glycol in a paint film is not high, polyethylene glycol is matched with a polyurea curing agent, the water contact angle of the paint film can be remarkably increased, and therefore the better hydrophobic effect is achieved.

Description

technical field [0001] The invention relates to the technical field of industrial paints, in particular to a non-staining water-based industrial guardrail paint. Background technique [0002] Guardrails are mainly used for the protection and protection of personal safety and equipment and facilities in residences, highways, commercial areas, public places and other occasions. Industrial guardrails are mainly made of steel, which has a lot of contact with personnel, and is easily scratched by tooling and shipping equipment, and the guardrails are seriously stained. Therefore, the effective coating protection of the guardrail is particularly important. [0003] At present, most of the guardrails mainly use solvent-based industrial coatings, which release volatile organic compounds (Volatile Organic Compounds, VOC) during production and use, resulting in pollution. At present, they have become the main source of pollution in cities after cars, endangering the human body healt...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C09D175/14C09D167/08C09D7/61C09D7/65C09D7/63C09D5/16
CPCC08K2003/2241C08L2205/035C09D5/1662C09D5/1687C09D175/14C08L67/08C08L75/02C08L71/02C08L3/02C08K5/06C08K3/22
Inventor 邰长金
Owner 湖州汇邦环保科技有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap