A method for separating and extracting vanadium chromium from vanadium slag sodium roasting water leaching solution

A technology of sodium roasting and leaching solution, which is applied in the direction of improving process efficiency, etc., and can solve the problems that chromium cannot be recovered, reused, and dangerous

Active Publication Date: 2021-11-26
CENT SOUTH UNIV
View PDF2 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The process is simple, but there are a series of problems: (1) can not handle the solution with high concentration of vanadium and chromium
(2) Chromium cannot be recycled, and a large amount of hazardous solid waste is produced
The treatment of this mother liquor is usually the reduction-neutralization method: firstly, V(V) and Cr(VI) in the solution are reduced, and then neutralized and precipitated to obtain vanadium-chromium reduction slag, which has complex components and can be regenerated It is difficult to use and is a dangerous solid waste
(3) The solution after vanadium precipitation cannot be reused
Although primary ammonium N1923 step-by-step extraction can realize the separation and recovery of vanadium and chromium, the two-step extraction method for separating and extracting vanadium and chromium from the leachate has high cost and no economic applicability, and the separation and extraction of primary ammonium N1923 will produce a large amount of Sodium sulfate raffinate, this raffinate cannot be reused, and the treatment cost is high and difficult
Chinese patent 201711079106.5 first uses the calcium salt precipitation method to selectively and directly precipitate all the vanadium in the vanadium slag sodium roasting water leaching solution, and then uses the carbonate solution to leach the vanadium in the precipitate and recover it. The solution after the vanadium precipitation is electrodialysis- The crystallization method can realize the recovery of chromium and sodium carbonate; but the method is complicated and consumes a lot of alkali
Chinese patent 200610089232.4 discloses a process for extracting and separating vanadium and chromium with primary-secondary amines, using primary-secondary amines to selectively extract vanadium, leaving chromium in the water phase, then recovering chromium by reduction precipitation, and recovering vanadium by ammonium salt precipitation; The method can realize the separation and recovery of vanadium and chromium, but the alkali consumption is large, the waste water cannot be recycled, and the extraction process is difficult to control and the cost of the extraction agent is high.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A method for separating and extracting vanadium chromium from vanadium slag sodium roasting water leaching solution
  • A method for separating and extracting vanadium chromium from vanadium slag sodium roasting water leaching solution
  • A method for separating and extracting vanadium chromium from vanadium slag sodium roasting water leaching solution

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0044] Take 4L of vanadium slag sodium roasting water leaching solution containing V 30g / L, Cr 1.1g / L, pass into carbon dioxide to adjust the pH value of the leaching solution to 8.5, and then follow the NH 3 Add ammonium carbonate to 1 times the molar ratio of V and stir at room temperature for 3 hours, then filter and separate to obtain ammonium meta-acid crystals and filtrate A, and the recovery rate of vanadium is 78%; ammonium meta-acid is calcined at 500° C. for 2 h to obtain vanadium-containing 99.3% Vanadium oxide products, wherein the content of Cr is 0.03%.

[0045] Filtrate A and composition are 40% methyltrialkyl extractant (in formula 1, R 1 ~R 3 for C 8 ~C 10 straight-chain alkane group, R 4 for CH 3 , A - for CO 3 2- ) + 20% 2-octanol + 40% sulfonated kerosene (volume percent) organic phases were mixed, and then 3-stage countercurrent extraction was carried out under the condition that the flow ratio was 1:10 to obtain raffinate A1 and loaded organic pha...

Embodiment 2

[0048] Take 3L of vanadium slag sodium roasting water leaching solution containing V 30g / L, Cr 13g / L, pass into carbon dioxide to adjust the pH value of the leaching solution to 7.5, and then follow the NH 3 0.8 times of the / V mol ratio was added ammonium bicarbonate and stirred at 60° C. for 0.5 h, during which the pH of the solution was added to control the pH of the solution at about 8.0, and then filtered and separated to obtain ammonium meta-acid crystals and filtrate A, and the rate of recovery of vanadium was 61%; The ammonium acid was calcined at 500°C for 2 hours to obtain a vanadium pentoxide product containing 99.2% of vanadium, in which the content of Cr was 0.05%.

[0049] Filtrate A and composition are 5% methyl trioctyl extractant (in formula 1, R 1 ~R 3 is n-octyl; R 4 for CH 3 ;A - for CO 3 2- )+10% 2-octanol+85% aviation kerosene (volume percent) organic phases were mixed, and then 8 stages of countercurrent extraction were carried out under the condit...

Embodiment 3

[0052] Get 2L containing V 80g / L, Cr 40g / L vanadium slag sodium roasting water leachate, and then according to NH 3 0.6 times of / V mol ratio is added liquid ammonia, and feeds carbon dioxide to adjust the pH value of the leaching solution to be 9.5, stir at room temperature for 2h, then filter and separate to obtain ammonium meta-acid crystals and filtrate A, the recovery rate of vanadium is 49%; ammonium meta-acid is in Calcined at 500°C for 2 hours to obtain a vanadium pentoxide product containing 99.1% of vanadium, wherein the content of Cr is 0.07%.

[0053] Filtrate A and composition are 10% methyl trinonyl extractant (in formula 1, R 1 ~R 3 is n-nonyl, R 4 for CH 3 ;A - for CO 3 2- ) + 10% tridecanol + 80% No. 200 solvent naphtha (volume percentage) mixed with the organic phase, and then carry out 14 stages of countercurrent extraction under the condition that the flow ratio is 1:4 to obtain the raffinate A1 and the loaded organic phase B1 . After washing the lo...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a method for separating and extracting vanadium chromium from vanadium slag sodium roasting water leaching solution, adding ammonium salt to the vanadium slag sodium roasting water leaching solution, and controlling the pH of the solution system at pH 7.5-9.5, stirring reaction, and then solid-liquid separation to obtain ammonium metavanadate crystals and filtrate A; organic phase B and filtrate A are extracted to obtain raffinate A1 and loaded organic phase B1; loaded organic phase B1 is back-extracted with sodium hydroxide solution, Obtain the stripping liquid A2; the raffinate A1 is recycled; add the vanadium precipitation agent to the stripping liquid A2 and ball mill at room temperature, filter to obtain the vanadium-containing filter residue C1 and the chromium-containing filtrate A3; add the raffinate A1 to the vanadium-containing filter residue C1, Then ball mill and filter to obtain filter residue C2 and vanadium-containing filtrate A4; filter residue C2 is calcined and then used as a vanadium precipitation reagent, vanadium-containing filtrate A4 is separated and recovered by ammonium salt vanadium precipitation method, and chromium-containing filtrate A3 is obtained by evaporation and crystallization after impurity removal Sodium chromate products. The invention can realize the advantages of separation and recovery of vanadium and chromium, sodium element and recycling of solution after vanadium and chromium extraction.

Description

technical field [0001] The invention belongs to the field of metallurgical separation and circular metallurgy, and in particular relates to a method for separating and extracting vanadium chromium from vanadium slag sodium roasting water leaching solution. Background technique [0002] Vanadium slag is the main industrial raw material for vanadium extraction, and the vanadium slag in my country mainly comes from the pyrometallurgy process of vanadium-titanium magnetite. Vanadium-titanium magnetite is a compound ore in which iron, vanadium, titanium, chromium and other valuable elements coexist. Due to the similar properties of vanadium and chromium, the trend of vanadium and chromium in the pyrometallurgy process is basically the same. The vanadium slag obtained by pyrometallurgy is actually a chromium-containing vanadium slag. Usually, the content of vanadium in slag is much higher than that of chromium, so it is generally called vanadium slag. [0003] The most industrial...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C22B7/00C22B34/22C22B34/32C22B3/28C22B3/40
CPCC22B7/006C22B34/22C22B34/32Y02P10/20
Inventor 王明玉王学文胡斌张长达廖志琴赵士杰
Owner CENT SOUTH UNIV