Preparation method of antibacterial and mildew-proof agent for textiles

An antibacterial and antifungal agent and cross-linking agent technology, which can be used in botanical equipment and methods, fungicides, textiles and papermaking, etc. Improve effect time, improve binding performance, avoid elapsed effects

Inactive Publication Date: 2021-03-30
王沛
View PDF0 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0006] The technical problem to be solved by the present invention is to provide a preparation method of an antibacterial and antifungal agent for textiles, aiming at the problems of low antibacterial activity, poor heat resistance, and weak antibacterial endurance of the antibacterial and antifungal agent for textiles

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Preparation method of antibacterial and mildew-proof agent for textiles

Examples

Experimental program
Comparison scheme
Effect test

preparation example Construction

[0028] A preparation method of an antibacterial and antifungal agent for textiles, the preparation method comprising the steps of:

[0029] (1) Mix the composite material and 0.3mol / L hydrochloric acid solution at a mass ratio of 1:10 to 15, maintain the pressure at 2MPa for 70s, steam explode, collect the blasting mixture, and mix the blasting mixture and water at a mass ratio of 3:5 Mix, heat to 100°C, cook for 5-7 hours, cool to room temperature, let stand for 20 minutes, filter, and collect the filtrate;

[0030] (2) Stir and mix the filtrate and activated carbon at a mass ratio of 7:1 to 3, let stand for 1 hour, filter, collect the filtrate, put the filtrate and ethanolamine into the reactor at a mass ratio of 16 to 18:1, and adjust the pH to Neutral, preheat at 50-55°C for 30 minutes, then add a catalyst with 0.1-0.2% ethanolamine mass, raise the temperature to 80-85°C, and stir at 600r / min for 8-10h;

[0031] (3) After the stirring is completed, cool to room temperatur...

Embodiment 1

[0034] The composite material is mixed with honeysuckle, litsea cubeba and Houttuynia cordata in a mass ratio of 10:5:7, and crushed to obtain the composite material.

[0035] The catalyst is a mixture of 1,1'-bisdiphenylphosphinoferrocene palladium dichloride and sodium methoxide at a mass ratio of 4:2.

[0036] The mixture is formed by mixing chitosan and ganoderma polysaccharide in a mass ratio of 20:1.

[0037] The mixed particles are formed by mixing nanoporous titanium dioxide and graphene oxide at a mass ratio of 9:1.

[0038] The crosslinking agent is a mixture of glutaraldehyde and genipin at a mass ratio of 13:1.

[0039] The surfactant is made by mixing polyoxyethylene sorbitan monooleate and sorbitan fatty acid ester at a mass ratio of 8:3.

[0040] A preparation method of an antibacterial and antifungal agent for textiles, the preparation method comprising the steps of:

[0041] (1) Mix the composite material and 0.3mol / L hydrochloric acid solution at a mass ra...

Embodiment 2

[0046] The compound material is mixed with honeysuckle, litsea cubeba and Houttuynia cordata in a mass ratio of 10:4:7, and crushed to obtain the compound material.

[0047] The catalyst is prepared by mixing 1,1'-bisdiphenylphosphinoferrocene palladium dichloride and sodium methoxide at a mass ratio of 4:1.5.

[0048] The mixture is formed by mixing chitosan and ganoderma polysaccharide in a mass ratio of 20:1.

[0049] The mixed particles are formed by mixing nanoporous titanium dioxide and graphene oxide at a mass ratio of 9:1.

[0050] The crosslinking agent is a mixture of glutaraldehyde and genipin at a mass ratio of 13:1.

[0051] The surfactant is made by mixing polyoxyethylene sorbitan monooleate and sorbitan fatty acid ester at a mass ratio of 8:3.

[0052] A preparation method of an antibacterial and antifungal agent for textiles, the preparation method comprising the steps of:

[0053] (1) Mix the composite material and 0.3mol / L hydrochloric acid solution at a mas...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention belongs to the technical field of textiles, and particularly relates to a preparation method of an antibacterial and mildew-proof agent for textiles. Flos lonicerae, fruit of cubeb litsea tree and herba houttuyniae are used as basic raw materials, beneficial substances such as ester and acid and the like in the basic raw materials are obtained through explosion and cooking extraction, an antibacterial and mildew-proof basic material is obtained, then activated carbon is used for decoloration, the processed basic material and ethanolamine carry out amidation treatment on ester andthe like in the base material under the action of a catalyst; firstly, active groups are increased; and secondly, the bonding performance with other substances is improved, the mixed particles are used for adsorption, a cross-linking agent is used for cross-linking, and then wrapping is carried out, so that microencapsulation is realized, and the bonding performance with textiles is improved.

Description

technical field [0001] The invention belongs to the technical field of textiles, and in particular relates to a preparation method of an antibacterial and antifungal agent for textiles. Background technique [0002] Due to its loose and porous structure, textiles can easily absorb sweat and oil secreted by human metabolism, providing a favorable place for the attachment and reproduction of microorganisms. Some bacteria and viruses can survive for several hours to several days on the surface of textiles. A number of studies have shown that the use of antibacterial textiles for medical protection and personal hygiene will greatly improve the overall cleanliness of the environment, reduce the incidence of nosocomial infections, and ensure the safety of patients and medical staff. Therefore, the development and application of antibacterial and antiviral textiles are of great significance. [0003] Antibacterial agents refer to substances that can effectively inhibit the growth ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): D06M13/00D06M15/01D06M13/402D06M15/03D06M11/46D06M11/74D06M13/123D06M13/224D06M23/12A01N25/28A01N65/24A01P1/00A01P3/00
CPCA01N25/28A01N65/00A01N65/08A01N65/24D06M11/46D06M11/74D06M13/00D06M13/123D06M13/224D06M13/402D06M15/01D06M15/03D06M16/00D06M23/12
Inventor 王沛
Owner 王沛
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com