Wear-resistant modified plastic and manufacturing process thereof

A manufacturing process and plastic technology, applied in the field of polymer modified plastics, can solve problems such as difficulty in moving doors and windows, and achieve the effects of reducing surface friction, less obvious scratches, and excellent wear resistance.

Pending Publication Date: 2021-07-16
泗阳联欣塑业有限公司
View PDF4 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] The purpose of the present invention is to provide a wear-resistant modified plastic and its manufacturing process to solve the problem that the plastic currently used on the movable door is difficult to move due to the long-term sliding back and forth of the plastic proposed in the background technology

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0021] A wear-resistant modified plastic, which is made by mixing the following raw materials in the mass ratio:

[0022] Including 50 parts of polyethylene PVC, 50 parts of polypropylene PP, 5 parts of graphite, 1 part of ceramic fiber, 1 part of plasticizer, 1 part of stabilizer, 1 part of dispersant and 20 parts of water. The ceramic fiber model is SYGX-421, the plasticizer is dioctyl phthalate and dimethyl succinate at a ratio of 1:0.5, the stabilizer is dibasic lead phosphite, and the dispersant is phenolic resin Made by mixing with ethyl acetate.

[0023] The material process of the above-mentioned embodiment is as follows,

[0024] (1) Add polyethylene PVC, polypropylene PP, graphite, ceramic fiber and water into the spiral mixer in proportion to heat and stir to obtain a mixed solution, wherein the stirring time is 30 minutes, the stirring rate is 700rpm, and the heating temperature is 150-200 ℃.

[0025] (2) Continue to add plasticizer, stabilizer and dispersant to...

Embodiment 2

[0029] A wear-resistant modified plastic, which is made by mixing the following raw materials in the mass ratio:

[0030] It includes 80 parts of polyethylene PVC, 80 parts of polypropylene PP, 10 parts of graphite, 5 parts of ceramic fiber, 5 parts of plasticizer, 5 parts of stabilizer, 5 parts of dispersant and 40 parts of water. Among them, the ceramic fiber model is SYG X-421, the plasticizer is made by mixing dioctyl phthalate and dimethyl succinate at a ratio of 1:1, the stabilizer is dibasic lead phosphite, and the dispersant is acetic acid Ethyl and propylene glycol block polyester blends.

[0031] The material process of the above-mentioned embodiment is as follows,

[0032] (1) Add polyethylene PVC, polypropylene PP, graphite, ceramic fiber and water into the spiral mixer in proportion to heat and stir to obtain a mixed solution, wherein the stirring time is 30 minutes, the stirring rate is 700rpm, and the heating temperature is 150-200 ℃.

[0033] (2) Continue to...

Embodiment 3

[0037] A wear-resistant modified plastic, which is made by mixing the following raw materials in the mass ratio:

[0038] It includes 65 parts of polyethylene PVC, 65 parts of polypropylene PP, 7.5 parts of graphite, 2.5 parts of ceramic fiber, 1.5 parts of plasticizer, 1.5 parts of stabilizer, 6.5 parts of anti-wear agent and 30 parts of water. Among them, the ceramic fiber model is SYGX-421, the plasticizer is made by mixing dioctyl phthalate and dimethyl succinate at a ratio of 1:0.75, the stabilizer is dibasic lead phosphite, and the dispersant is ethyl acetate Made from a blend of ester and propylene glycol block polyester.

[0039] The material process of the above-mentioned embodiment is as follows,

[0040] (1) Add polyethylene PVC, polypropylene PP, graphite, ceramic fiber and water into the spiral mixer in proportion to heat and stir to obtain a mixed solution, wherein the stirring time is 30 minutes, the stirring rate is 700rpm, and the heating temperature is 150-2...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a wear-resistant modified plastic and a manufacturing process thereof, and belongs to the field of polymer modified plastics, the wear-resistant modified plastic is prepared by mixing the following raw materials according to a proportion and granulating and molding in a granulator, and the materials comprise 50-80 parts of polyethylene PVC, 50-80 parts of polypropylene PP, 5-10 parts of graphite, 1-5 parts of ceramic fibers, 1-3 parts of a plasticizer, 1-3 parts of a stabilizer, 1-3 parts of a dispersant and 20-40 parts of water. The wear-resistant modified plastic has a high-strength wear-resistant effect, can be widely applied to the field of doors and windows, and has a good application prospect.

Description

technical field [0001] The invention relates to the technical field of polymer modified plastics, in particular to a wear-resistant modified plastic and its manufacturing process. Background technique [0002] Plastics are polymer compounds made of monomers through addition polymerization or polycondensation. The main component is resin, which is widely used in many fields; plastics are widely used because of their advantages such as lightness and good physical properties. Used in the current door and window field, the common ones are PE, PP, PVC and PPR, etc.; the threshold in the field of moving doors is often made of plastic, and some moving doors move the door body by setting pulleys and guide rails below, and the other part directly passes through the A chute is set under the door panel to move the door. When these structures are in use, the plastic is often fluffed and dented due to long-term friction, which greatly increases the friction between the door, window and g...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C08L27/06C08L23/12C08K13/04C08K3/04C08K7/04C08K5/12C08K5/11
CPCC08L27/06C08L23/12C08L2205/03C08K13/04C08K3/04C08K7/04C08K5/12C08K5/11
Inventor 夏鹏飞王瑞王雨丁萍
Owner 泗阳联欣塑业有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com