Surface protection film for flexible display
A surface protection film and display technology, which is applied in the direction of instruments, chemical instruments and methods, film/sheet adhesives, etc., can solve the problems of surface protection film peeling off from the display surface, high force, etc., and achieve good pen feel, Excellent handling properties and excellent self-healing properties
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Image
Examples
Embodiment 1
[0122] Add 7.6 g of 1,4-butanediol and trimethylolpropane to 53.8 g of Polycarbonate diol (manufactured by Tosoh Co., Ltd., trade name: Nippollan 965) 1.9 g, 36.7 g of isophorone diisocyanate (IPDI), and 50 ppm of an organotin compound were stirred and mixed to prepare a material composition.
[0123] A silicon-treated PET film with a thickness of 125 μm was used as the first gap maintaining member and the second gap maintaining member, and a surface protection film laminate having a protective layer with a thickness of 150 μm was produced by the above production method.
Embodiment 2
[0125] Add 5.58 g of 1,4-butanediol, 3.68 g of trimethylolpropane, and 1,4-butanediol to 56.7 g of polycarbonate diol (manufactured by Tosoh Co., Ltd., trade name: Nippollan 965). A surface protection film laminate was obtained in the same manner as in Example 1 except that 34.0 g of norbornene diisocyanate (NBDI) and 50 ppm of an organotin compound were stirred and mixed to obtain a material composition.
Embodiment 3
[0127] 5.7 g of 1,4-butanediol, 3.8 g of trimethylolpropane, and IPDI were added to 53.8 g of polycarbonate diol (manufactured by Tosoh Co., Ltd., trade name: Nippollan 965) 36.7 g and 50 ppm of an organotin compound were stirred and mixed to obtain a material composition, and a surface protection film laminate was obtained in the same manner as in Example 1.
PUM
Property | Measurement | Unit |
---|---|---|
thickness | aaaaa | aaaaa |
thickness | aaaaa | aaaaa |
surface roughness | aaaaa | aaaaa |
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap