A kind of spray polyurea elastomer and preparation method thereof

A polyurea elastomer, modification technology, applied in the direction of polyurea/polyurethane coating, coating, anti-corrosion coating, etc., can solve the problems of spraying polyurea elastomer coating cracking, serious chemical erosion, aggravation, etc., to achieve good anti-corrosion Corrosion effect, high emulsification efficiency, good chemical resistance

Active Publication Date: 2022-03-01
东营海瑞宝新材料有限公司
View PDF7 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, in some special areas, such as wastewater collection ponds with high chemical content, especially in high acidity environments, chemical erosion is severe, and the corrosion and cracking of sprayed polyurea elastomer coatings are aggravated. Therefore, it is necessary to further improve its resistance. Chemical resistance, or make it have a certain self-healing ability to resist harsh environments and prolong its service life

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of spray polyurea elastomer and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0056] The present embodiment provides a kind of preparation method of spray polyurea elastomer, comprises the following steps:

[0057] Step S100, preparing self-healing microcapsules:

[0058] Mix and stir 1g hydrolyzed polystyrene-maleic anhydride nanoparticles and 99g deionized water to obtain the first dispersion; mix and stir 35g phenol, 35g acetaldehyde and 30g deionized water, and use 10% The sodium hydroxide solution adjusts its pH value to 9-10, and the first prepolymer is obtained after reacting for 3-5 hours; the first prepolymer and the first dispersion are mixed evenly, and the hydrochloric acid solution with a mass fraction of 10% Adjust its pH value to 3-5 to obtain the second dispersion; mix the second dispersion with 4g resorcinol and 4g ammonium chloride, and obtain the third dispersion after ultrasonic dissolution; drop 210g of dicyclopentadiene Add it to the third dispersion, heat up to 60-70°C after ultrasonic emulsification for 10-15 minutes, adjust its...

Embodiment 2

[0066] The present embodiment provides a kind of preparation method of spray polyurea elastomer, comprises the following steps:

[0067] Step S100, preparing self-healing microcapsules:

[0068] Mix and stir 1g hydrolyzed polystyrene-maleic anhydride nanoparticles and 99g deionized water to obtain the first dispersion liquid; mix and stir 35g cresol, 35g formaldehyde and 30g deionized water, and use 10% The sodium hydroxide solution adjusts its pH value to 9-10, and the first prepolymer is obtained after reacting for 3-5 hours; the first prepolymer and the first dispersion are mixed evenly, and the hydrochloric acid solution with a mass fraction of 10% Adjust its pH value to 3-5 to obtain the second dispersion; mix the second dispersion with 4g tea polyphenols and 4g ammonium chloride, and obtain the third dispersion after ultrasonic dissolution; add 210g of dicyclopentadiene dropwise In the third dispersion liquid, heat up to 60-70°C after ultrasonic emulsification for 10-15...

Embodiment 3

[0076] The present embodiment provides a kind of preparation method of spray polyurea elastomer, comprises the following steps:

[0077] Step S100, preparing self-healing microcapsules:

[0078]1g of hydrolyzed polystyrene-maleic anhydride nanoparticles and 99g of deionized water were mixed and stirred evenly to obtain the first dispersion; 35g of phenol, 35g of paraformaldehyde and 30g of deionized water were mixed and stirred evenly, with a mass fraction of 10% The pH value of the sodium hydroxide solution is adjusted to 9 to 10, and the first prepolymer is obtained after 3 to 5 hours of reaction; the first prepolymer and the first dispersion are mixed uniformly, and the mass fraction is 10% hydrochloric acid The pH value of the solution was adjusted to 3-5 to obtain the second dispersion; the second dispersion was mixed with 4g resorcinol and 4g ammonium chloride, and the third dispersion was obtained after ultrasonic dissolution; 210g dicyclopentadiene Add it dropwise to ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
quality scoreaaaaaaaaaa
Login to View More

Abstract

The present invention relates to the technical field of spray-coated polyurea elastomer, and provides a spray-coated polyurea elastomer and a preparation method thereof. The preparation includes the following steps: step S100, preparing self-repairing microcapsules: using solid particle emulsifier, phenol, aldehyde, Prepare self-healing microcapsules by reacting deionized water, polyphenols, ammonium chloride, and dicyclopentadiene; step S200, preparing component A: polyetheramine, self-healing microcapsules, fiber filler, diethyltoluenediamine, The Grubb catalyst is mixed and stirred evenly; step S300, preparation of component B: mixing isocyanate and polyether polyol, and reacting to obtain an isocyanate prepolymer; step S400, preparation of sprayed polyurea elastomer: through a spraying machine, the components A and Component B is sprayed on the surface of the substrate at a volume ratio of 1:1, and reacted to obtain a sprayed polyurea elastomer. The sprayed polyurea elastomer provided by the invention has self-repair function, and has good mechanical properties and chemical corrosion resistance.

Description

technical field [0001] The invention relates to the technical field of sprayed polyurea elastomers, in particular to a sprayed polyurea elastomer and a preparation method thereof. Background technique [0002] Spraying polyurea elastomer is a new type of environmentally friendly coating technology and the latest development of structural waterproof technology. It uses special spraying equipment to spray solvent-free polyurea system onto the substrate to quickly form sprayed polyurea elastomer. Coatings, sprayed polyurea elastomer coatings show the advantages of high resistance to environmental influences, high chemical resistance and fast curing, its elastomeric properties protect the substrate from mechanical stress, while its high chemical resistance protects the substrate Material is protected from chemical attack. However, in some special areas, such as wastewater collection ponds with high chemical content, especially in high acidity environments, chemical erosion is s...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C09D175/02C09D5/08C09D7/65C09D7/62
CPCC09D175/02C09D5/08C09D7/65C09D7/62C09D7/70C08L2205/035C08L2205/16C08L61/06C08L35/06C08L77/10C08K9/10C08K5/01C08K9/04C08K7/14
Inventor 李强王晓刚朱忠杰
Owner 东营海瑞宝新材料有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More