Combined coupling agent, modified carbonaceous aggregate, preparation method of modified carbonaceous aggregate, and electric contact material

A carbonaceous aggregate and combined technology, which is applied in the field of coupling agent, electrical contact material, modified carbonaceous aggregate and its preparation, can solve the problem of poor interface bonding of binder resin and unstable current-carrying friction and wear performance , binder fluidity and other problems, to achieve the effect of good interface bonding, simple and easy preparation method, and low cost

Active Publication Date: 2021-08-24
安康市顺祥炭素有限公司
View PDF4 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, this type of material has the following disadvantages: ①Since the surface of carbonaceous aggregate graphite powder contains only a small amount of free hydroxyl groups, resulting in poor interfacial bonding with the binder resin; ②Due to the poor fluidity of the binder during the kneading process, its Inhomogeneous dispersion between materials, it is very easy to generate inevitable random microcracks at the interface of aggregate phase / binder phase
The above problems will lead to poor flexural strength of the carbon brush, unstable current-carrying friction and wear performance, poor wear resistance, etc., and even cause the motor to be burned

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Combined coupling agent, modified carbonaceous aggregate, preparation method of modified carbonaceous aggregate, and electric contact material
  • Combined coupling agent, modified carbonaceous aggregate, preparation method of modified carbonaceous aggregate, and electric contact material
  • Combined coupling agent, modified carbonaceous aggregate, preparation method of modified carbonaceous aggregate, and electric contact material

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0032] A combined coupling agent for carbonaceous aggregate modification, the proportion is titanate coupling agent: borate coupling agent: aluminate coupling agent is 3:1:1, the above titanic acid The ester coupling agent is titanate TTS, the borate coupling agent is borate LD-100P, and the aluminate coupling agent is aluminate DL-411.

[0033] A modified carbonaceous aggregate obtained by modifying the above combined coupling agent, the specific process is as follows:

[0034] (1) prepare carbonaceous aggregate powder by airflow mixing method;

[0035] (2) The configuration quality is a combined coupling agent solution with a carbonaceous aggregate powder mass fraction of 3%;

[0036] (3) Disperse the combined coupling agent solution in step (2) evenly on the surface of the carbonaceous aggregate powder by atomization, and mix uniformly to obtain the treated modified carbonaceous aggregate powder.

[0037] A resin-type sliding electrical contact material, including the fol...

Embodiment 2

[0043] A combined coupling agent for carbonaceous aggregate modification, the proportion is titanate coupling agent: borate coupling agent: aluminate coupling agent is 2:1:2, the above titanic acid The ester coupling agent is titanate TTS, the borate coupling agent is borate LD-100P, and the aluminate coupling agent is aluminate DL-411.

[0044] A modified carbonaceous aggregate obtained by modifying the above combined coupling agent, the specific process is as follows:

[0045] (1) prepare carbonaceous aggregate powder by airflow mixing method;

[0046] (2) The configuration quality is a combined coupling agent solution with a carbonaceous aggregate powder mass fraction of 3%;

[0047] (3) Disperse the combined coupling agent solution in step (2) evenly on the surface of the carbonaceous aggregate powder by atomization, and mix uniformly to obtain the treated modified carbonaceous aggregate powder.

[0048] A resin-type sliding electrical contact material, including the fol...

Embodiment 3

[0053] A combined coupling agent for carbonaceous aggregate modification, the proportion is titanate coupling agent: borate coupling agent: aluminate coupling agent is 1:1:1, the above titanic acid The ester coupling agent is titanate TTS, the borate coupling agent is borate LD-100P, and the aluminate coupling agent is aluminate DL-411.

[0054] A modified carbonaceous aggregate obtained by modifying the above combined coupling agent, the specific process is as follows:

[0055] (1) prepare carbonaceous aggregate powder by airflow mixing method;

[0056] (2) The configuration quality is a combined coupling agent solution with a carbonaceous aggregate powder mass fraction of 3%;

[0057] (3) Disperse the combined coupling agent solution in step (2) evenly on the surface of the carbonaceous aggregate powder by atomization, and mix uniformly to obtain the treated modified carbonaceous aggregate powder.

[0058] A resin-type sliding electrical contact material, including the fol...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
densityaaaaaaaaaa
Login to View More

Abstract

The invention discloses a combined coupling agent for modifying carbonaceous aggregate, wherein the combined coupling agent comprises a borate coupling agent and a titanate coupling agent, and the ratio of the borate coupling agent to the titanate coupling agent is 1:(1-3). The invention also provides a modified carbonaceous aggregate obtained by modification of the combined coupling agent and a preparation method of the modified carbonaceous aggregate. The invention also provides an electric contact material containing the modified carbonaceous aggregate. The invention provides the novel combined coupling agent, designs and prepares the modified carbonaceous aggregate and the resin type sliding electric contact material; the application range of the coupling agent is expanded, and a theoretical basis and a basis for application research are also provided for upgrading and updating of the resin type sliding electric contact material.

Description

technical field [0001] The invention belongs to the field of composite materials, and in particular relates to a coupling agent, a modified carbonaceous aggregate, a preparation method thereof, and an electrical contact material. Background technique [0002] Materials that make components that conduct current (electrical signals, electrical energy) in contact with each other are called electrical contact materials. Electrical contact material is the functional carrier for electrical appliances to complete the "connection-conduction-cutoff" current and signal generation and transmission. Its electrical contact performance is the key to the reliability of electrical and electronic engineering. It has "the heart of low-voltage electrical appliances" in the field of low-voltage electrical appliances. It is widely used in relays, circuit breakers, contactors, sensors, industrial control and other products. Electrical contact materials include fixed, sliding and separable contac...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C08K9/04C08K3/04C08K3/30C08L63/00H01H1/029H01H11/04
CPCC08K9/04C08K3/04C08K3/30H01H1/029H01H11/04C08K2003/3009C08L63/00
Inventor 涂川俊谭姣刘平巩佩徐宇轩
Owner 安康市顺祥炭素有限公司