A kind of building sun-proof and heat-insulating coating and preparation method thereof

A technology for sun protection, heat insulation and coating, applied in epoxy resin coatings, coatings and other directions, can solve problems such as the insufficient thermal insulation performance of coatings

Active Publication Date: 2022-02-25
JIANGSU MIRAFUL NANO MATERIAL CO LTD +1
View PDF7 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0006] (1) By adding Al(NO 3 ) 3 Dissolve in ethanol solution, add Y(NO 3 ) 3 and tributyl borate, after drying, aging, drying and heat treatment, dry gel coarse powder a is obtained, and then boric acid microparticles are obtained by jet crushing, water glass is added to deionized water, and the acidic styrene cation exchange Resin exchange column, adding boric acid microparticles and inorganic fillers and stirring to obtain dry gel coarse powder b, and then airflow crushing to obtain the modified silica airgel, by adding the modified silica airgel Into the coating, it solves the problem that the thermal insulation performance of the coating cannot meet the current high-level green building's demand for building energy conservation;

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of building sun-proof and heat-insulating coating and preparation method thereof
  • A kind of building sun-proof and heat-insulating coating and preparation method thereof
  • A kind of building sun-proof and heat-insulating coating and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0045] This embodiment is a kind of architectural sun-proof and heat-insulating coating, comprising the following steps:

[0046] S1: Mix water-based acrylic resin, modified silica airgel, zinc phosphate, organic fluorine epoxy resin and silicone resin to obtain a blend;

[0047] S2: Add the blended material into a stirring tank, stir evenly, filter, then add to a ball mill for grinding to obtain a ground crude product;

[0048] S3: Adding mica powder, aluminum tripolyphosphate and dispersant to the ground crude product, then fine processing, high-speed ball milling until the system is uniform, and the building sunscreen and heat insulation coating is obtained.

[0049] Wherein the preparation process of modified silica airgel is as follows:

[0050] S21: Al(NO 3 ) 3 Dissolve in ethanol solution, add Y(NO 3 ) 3 and tributyl borate, and heated and refluxed in a water bath at 100°C for 5 hours to form a clear sol, which was then placed in a constant temperature water bath a...

Embodiment 2

[0058] This embodiment is a kind of architectural sun-proof and heat-insulating coating, comprising the following steps:

[0059] S1: Mix water-based acrylic resin, modified silica airgel, zinc phosphate, organic fluorine epoxy resin and silicone resin to obtain a blend;

[0060] S2: Add the blended material into a stirring tank, stir evenly, filter, then add to a ball mill for grinding to obtain a ground crude product;

[0061] S3: Adding mica powder, aluminum tripolyphosphate and dispersant to the ground crude product, then fine processing, high-speed ball milling until the system is uniform, and the building sunscreen and heat insulation coating is obtained.

[0062] Wherein the preparation process of modified silica airgel is as follows:

[0063] S21: Al(NO 3 ) 3 Dissolve in ethanol solution, add Y(NO 3 ) 3 and tributyl borate, and heated and refluxed in a water bath at 90°C for 4 hours to form a clear sol, which was then placed in a constant temperature water bath at...

Embodiment 3

[0071] This embodiment is a kind of architectural sun-proof and heat-insulating coating, comprising the following steps:

[0072] S1: Mix water-based acrylic resin, modified silica airgel, zinc phosphate, organic fluorine epoxy resin and silicone resin to obtain a blend;

[0073] S2: Add the blended material into a stirring tank, stir evenly, filter, then add to a ball mill for grinding to obtain a ground crude product;

[0074] S3: Adding mica powder, aluminum tripolyphosphate and dispersant to the ground crude product, then fine processing, high-speed ball milling until the system is uniform, and the building sunscreen and heat insulation coating is obtained.

[0075] Wherein the preparation process of modified silica airgel is as follows:

[0076] S21: Al(NO 3 ) 3 Dissolve in ethanol solution, add Y(NO 3 ) 3 and tributyl borate, and heated and refluxed in a water bath at 100°C for 4 hours to form a clear sol, which was then placed in a constant temperature water bath a...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
reflectanceaaaaaaaaaa
reflectanceaaaaaaaaaa
reflectanceaaaaaaaaaa
Login to view more

Abstract

The invention discloses a sun-proof and heat-insulating coating for buildings and a preparation method thereof. The blend is obtained by mixing water-based acrylic resin, modified silica airgel, zinc phosphate, organic fluorine epoxy resin and silicone resin , put the blend into the mixing tank, stir evenly and then filter, and mix the boric acid microparticles and inorganic fillers into the SiO 2 In the sol precursor, it fills the defects in the nonlinear optical crystal, and then regulates the infrared radiation performance, and undertakes the function of enhancing the infrared radiation performance of the atmospheric window band. Adding a dispersant makes the molecular chain of the dispersant fully stretch in the aqueous solution. In SiO 2 A surface adsorption layer of a certain thickness is formed on the surface of the airgel particles, which produces a steric hindrance effect, thereby achieving the promotion of the development of high-grade green buildings and the improvement of SiO 2 The purpose of dispersion stability of airgel system.

Description

technical field [0001] The invention relates to the field of architectural coatings, in particular to an architectural sun-proof and heat-insulating coating and a preparation method thereof. Background technique [0002] At present, there are various measures for building heat insulation, which are mainly realized through roofs, walls, glass, etc. Among the many measures, roofs and walls occupy the vast majority. Now most of them are painted with reflective insulation on their surfaces. Thermal coatings to reduce the impact of sunlight on the temperature of buildings, and at the same time achieve the purpose of reducing the surface temperature of buildings, thereby reducing the indoor temperature and making the room reach a relatively comfortable temperature. This is also one of the effective measures for high efficiency and environmental protection at present; [0003] In the construction field, reflective heat insulation coatings are commonly used for sun protection and he...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Patents(China)
IPC IPC(8): C09D133/00C09D183/04C09D163/00C09D7/61C09D7/62C09D7/65C08F265/02C08F220/20
CPCC09D133/00C09D183/04C09D7/61C09D7/62C09D7/65C09D7/70C08F265/02C08K2003/327C08K2003/328C08L83/04C08L51/003C08L63/00C08K3/34C08K3/32C08K9/02C08K7/26C08F220/20
Inventor 刘溧钱东琴王俊
Owner JIANGSU MIRAFUL NANO MATERIAL CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap