Waterproof roll prepreg composition, waterproof roll prepreg and preparation method and application thereof

A technology of waterproofing membrane and composition, which is applied to building thermal insulation materials, roofs using flexible materials, building structures, etc. Oily, good adhesion effect

Active Publication Date: 2021-10-01
KESHUN WATERPROOF TECH CO LTD
View PDF6 Cites 3 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0008] The purpose of the present invention is to overcome the disadvantages of the existing wet-laid waterproof rolls, which are easy to cause pollution to the environment, and difficult to balance oil seepage performance and adhesive performance.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Waterproof roll prepreg composition, waterproof roll prepreg and preparation method and application thereof
  • Waterproof roll prepreg composition, waterproof roll prepreg and preparation method and application thereof
  • Waterproof roll prepreg composition, waterproof roll prepreg and preparation method and application thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0071] This example is used to illustrate that the waterproof membrane prepreg composition according to the present invention is prepared according to the formula and process parameters in Table 1, and the waterproof membrane prepreg is prepared according to the following method.

[0072] The preparation method of the waterproof roll material prepreg comprises the following steps:

[0073] (1) Stir the base asphalt at a speed of 1100 rpm at 130°C for 30 minutes to obtain delightened asphalt;

[0074] (2) Stirring the delightened asphalt, softener, and hard asphalt at a speed of 1300 rpm at 150°C for 30 minutes to obtain the first mixture;

[0075] (3) The first mixture and the inorganic filler were stirred for 1 hour at 170° C. at a speed of 1300 rpm to obtain a waterproof membrane prepreg Y1.

Embodiment 2

[0077] This embodiment adopts the same flow process as embodiment 1 to carry out, and the difference is that in this embodiment:

[0078] The formulations and process parameters of the waterproof membrane prepreg compositions used are different, see Table 1 for details.

[0079] The waterproof membrane prepreg Y2 was prepared.

Embodiment 3

[0081] In this example, a waterproof membrane prepreg was prepared using a formula and method similar to that of Example 1, except that polyethylene wax I was replaced with polyethylene wax II by equal weight to prepare a waterproof membrane prepreg Y3. See Table 1 for details.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
flash pointaaaaaaaaaa
flash pointaaaaaaaaaa
softening pointaaaaaaaaaa
Login to View More

Abstract

The invention relates to the field of asphalt waterproof coiled materials, and discloses a waterproof coiled material prepreg composition, a waterproof coiled material prepreg and a preparation method and application thereof. The composition contains more than two of the following components which are stored in a mixed manner or stored independently: compound asphalt, a softening agent and an inorganic filler, wherein the compound asphalt is a combination of matrix asphalt and hard asphalt in a content weight ratio of 1: (0.10-0.35), and the softening agent is at least one of polyethylene wax and polar amide wax. When the prepreg prepared from the composition provided by the invention is applied to a waterproof roll, the requirement for oil permeability of the waterproof roll can be met, and the waterproof roll has good adhesive property.

Description

technical field [0001] The invention relates to the field of asphalt waterproof coiled material, in particular to a waterproof coiled material prepreg composition, a waterproof coiled material prepreg, a preparation method and application thereof. Background technique [0002] At present, there are few studies on prepregs for wet-laid waterproof membranes with tires. The new national standard "Wet-laid Waterproof Membranes" passed in 2017 has tightened the test methods for oil permeability of membrane products in terms of product technical requirements. Prevent manufacturers from adding inferior quality engine oil and light components. [0003] At present, most waterproof membrane prepregs usually add polypropylene (PP) to the base asphalt to meet the national standard's requirements for membrane oil permeability. [0004] However, when PP is added to the base asphalt, PP is easy to precipitate at low temperature, thereby reducing the bonding performance between the coating...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C08L95/00C08L23/06C08L91/06C08K3/34C08K3/26E04B1/66E04D5/10
CPCC08L95/00E04B1/665E04D5/10C08L2205/035C08L2205/025C08K2003/265C08L23/06C08K3/34C08L91/06C08K3/26
Inventor 黄祖行龚兴宇任德强刘艳娜
Owner KESHUN WATERPROOF TECH CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com