Cyclic torsion machining process capable of improving mechanical performance of metal material

A technology of metal materials and processing technology, which is applied in the field of cycle torsion processing technology, can solve the problems of reducing the use range of metal materials, low cycle torsion performance, and fracture of metal materials, so as to increase the use range, improve the degree of grain refinement, The effect of increasing strength

Inactive Publication Date: 2021-10-01
YANGTZE NORMAL UNIVERSITY
View PDF0 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Alloys often refer to two or more metals or metals and non-metals combined, and have metallic properties. Among them, the existing metal materials are usually processed and prepared by conventional techniques during the preparation process, but the preparation The mechanical properties of the prepared metal material have low cyclic torsion performance. During the cyclic torsion process of the metal material, it is easy to cause the metal material to break. At the same time, the strength of the prepared metal material decreases after cyclic torsion. Reduced range of use of metal materials

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Cyclic torsion machining process capable of improving mechanical performance of metal material

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0022] The following will clearly and completely describe the technical solutions in the embodiments of the present invention with reference to the accompanying drawings in the embodiments of the present invention. Obviously, the described embodiments are only some, not all, embodiments of the present invention. Based on the embodiments of the present invention, all other embodiments obtained by persons of ordinary skill in the art without making creative efforts belong to the protection scope of the present invention.

[0023] see figure 1 , an embodiment provided by the present invention: a cycle torsion process for improving the mechanical properties of metal materials, comprising the following steps: Step 1, smelting; Step 2, pouring; Step 3, rolling; Step 4, heating; Step 5 , cooling; step six, grain refinement; step seven, manufacturing; step eight, carburizing; step nine, quenching;

[0024] Among them, in the above step 1, the raw materials required for the preparatio...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a cyclic torsion machining process capable of improving the mechanical performance of a metal material. The cyclic torsion machining process capable of improving the mechanical performance of the metal material comprises the following steps: step 1, smelting; step 2, pouring; step 3, rolling; step 4, heating; step 5, cooling; step 6, grain refinement; step 7, manufacturing; step 8, carburizing; and step 9, quenching. According to the cyclic torsion machining process capable of improving the mechanical performance of the metal material, in the process of preparing the metal material, rolling and heat-preservation pressurizing treatment are carried out on a blank, so that increasing for the grain refinement degree of the metal material is benefited, and then improvement for cyclic torsion performance in the mechanical performance of the metal material is benefited; and meanwhile, in the subsequent process for preparing the metal material, carburizing treatment is carried out on the metal material, so that increasing for the strength of the metal material is benefited, the phenomenon that the metal material is fractured after the metal material is cyclically twisted is avoided, and then the application range of the metal material is widened.

Description

technical field [0001] The invention relates to the technical field of metal material processing, in particular to a cycle torsion processing technology for improving the mechanical properties of metal materials. Background technique [0002] Metallic materials generally refer to pure metals or alloys in industrial applications. There are about 70 kinds of pure metals in nature, among which iron, copper, aluminum, tin, nickel, gold, silver, lead, zinc and so on are common. Alloys often refer to two or more metals or metals and non-metals combined, and have metallic properties. Among them, the existing metal materials are usually processed and prepared by conventional techniques during the preparation process, but the preparation The mechanical properties of the prepared metal material have low cyclic torsion performance. During the cyclic torsion process of the metal material, it is easy to cause the metal material to break. At the same time, the strength of the prepared me...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C21D8/00C21D7/13C22F1/00C23C8/44
CPCC21D8/00C21D7/13C22F1/00C23C8/44Y02P10/20
Inventor 徐向俊戴甲洪向超
Owner YANGTZE NORMAL UNIVERSITY
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products