Weft knitting shirt fabric and production process thereof

A production process and knitting technology, applied in weft knitting, knitting, textiles and papermaking, etc., can solve the problems of poor wearing performance, tight structure, poor dimensional stability, low recovery, etc., and achieve the effect of tight tissue structure

Active Publication Date: 2022-02-18
LUTAI TEXTILE
View PDF13 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

First of all, the tissue in this patent uses dials and needle cylinders to weave, and weaves and connects needle cylinders and dials in the 1st and 13th routes. It is a double-sided weave, not a single-sided weave. There are two types of single-sided weaves One is to weave only by the needle cylinder or the dial, the second is to use the needle cylinder and the needle cylinder to weave, but there is no connecting part between the needle cylinder and the needle disk; secondly, the double-sided tissue front It is completely two parts with the reverse side, only relying on the 1st and 13th roads to connect the front and rear sides with tucks, that is to say, there is no connection between the front and rear tissues between the 2-12 and 14-23 roads, but the front and rear are independent The part of this structure has tightness and poor dimensional stability, so it is not suitable for shirting fabrics
[0007]At present, knitted shirt fabrics have defects such as high elasticity and low recovery, and poor wearing performance. It is urgent to provide a weft knitted fabric with a tight structure and good resilience Shirt fabric and its production process

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Weft knitting shirt fabric and production process thereof
  • Weft knitting shirt fabric and production process thereof
  • Weft knitting shirt fabric and production process thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0032]The weft-knitted shirt fabric: use pure cotton combed 60-inch single yarn, 75-denier polyester and 20-denier low-temperature spandex as raw materials, and weave according to the dobby weave for low-temperature spandex and cotton yarn, and polyester for weaving; Production process: Low-temperature spandex, cotton yarn and polyester are sequentially dyed → weaving → pre-setting → finalizing → singeing → mercerizing → liquid ammonia → washing → non-ironing → tenter → pre-shrinking to obtain weft-knitted shirt fabric.

[0033] in:

[0034] The 100-turn thread length of the pure cotton combed is 15cm, the 100-turn thread length of the polyester is 13cm, and the 100-turn thread length of the low-temperature spandex is 5cm; the low-temperature spandex is selected from Lycra 1U072 of DuPont.

[0035] The low-temperature spandex and cotton yarn coils and polyester coils of the dobby weave are arranged at intervals in the longitudinal direction, and the weave distribution is as fo...

Embodiment 2

[0042] The weft-knitted shirt fabric: use pure cotton combed 100 / 2 English count plied cotton yarn, 100D polyester and 30D low-temperature spandex as raw materials, and weave according to the dobby weave for low-temperature spandex and cotton yarn, and polyester for weaving; Production process: Low-temperature spandex, cotton yarn and polyester are sequentially dyed → weaving → pre-setting → finalizing → singeing → mercerizing → liquid ammonia → washing → non-ironing → tenter → pre-shrinking to obtain weft-knitted shirt fabric.

[0043] in:

[0044] The 100-turn thread length of the pure cotton combed is 27cm, the 100-turn thread length of the polyester is 23cm, and the 100-turn thread length of the low-temperature spandex is 9cm; the low-temperature spandex is selected from Lycra 1U041 of DuPont.

[0045] The low-temperature spandex and cotton yarn coils and polyester coils of the dobby weave are arranged at intervals in the longitudinal direction, and the weave distribution ...

Embodiment 3

[0052] The weft-knitted shirt fabric is made of pure cotton combed 70-inch single yarn, 75-denier polyester and 30-denier low-temperature spandex as raw materials, and the low-temperature spandex and cotton yarn are used together, and polyester is used to weave according to the dobby weave; Production process: Low-temperature spandex, cotton yarn and polyester are sequentially dyed → weaving → pre-setting → finalizing → singeing → mercerizing → liquid ammonia → washing → non-ironing → tenter → pre-shrinking to obtain weft-knitted shirt fabric.

[0053] in:

[0054] The 100-turn thread length of the pure cotton combed is 13cm, the 100-turn thread length of the polyester is 15cm, and the 100-turn thread length of the low-temperature spandex is 8cm; the low-temperature spandex is selected from Lycra 1U041 of DuPont.

[0055] The low-temperature spandex and cotton yarn coils and polyester coils of the dobby weave are arranged at intervals in the longitudinal direction, and the wea...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
depthaaaaaaaaaa
depthaaaaaaaaaa
Login to View More

Abstract

The invention relates to the technical field of textiles, and concretely relates to a weft knitting shirt fabric and a production process thereof. The knitted shirt fabric is made of low-temperature spandex, cotton yarn and polyester, and is produced by weaving with the low-temperature spandex and the cotton yarn as one path and the polyester as one path according to mini-jacquard weave, and then carrying out an after-finishing process. According to the mini-jacquard weave, a low-temperature spandex and cotton yarn coil and a polyester coil are arranged at intervals in the longitudinal direction, and the weave distribution is that the minimum circulation unit in the longitudinal direction is composed of 12 transverse rows, and the minimum circulation unit in the transverse direction is composed of 6 coil wale rows. According to the invention, an innovative weft knitting weave structure is matched with low-temperature spandex weaving, the cotton yarns and the low-temperature spandex are woven according to the same rule, the cotton yarns and the low-temperature spandex are arranged at intervals with the polyester, the weave structure is compact, the finished fabric has excellent dimensional stability and elastic recovery, the characteristics of moisture absorption, air permeability and soft hand feeling of the fabric are retained, the stiff and smooth performance is good, and the shape preserving performance is good.

Description

technical field [0001] The invention relates to the technical field of textiles, in particular to a weft-knitted shirt fabric and a production process thereof. Background technique [0002] In recent years, people have higher and higher requirements for the comfort of clothing fabrics. Shirts are a necessity in people's lives. Shirt fabrics on the market are generally woven fabrics and knitted warp-knitted fabrics. The woven shirt fabric is crisp and stylish, but has poor moisture absorption and air permeability. Although it is comfortable to wear when the temperature is low, the human body sweats more when worn in high temperature weather. It is easy to deform after washing for the first time, and the wearing performance is poor. Although the comfort of knitted warp-knitted fabrics is stronger than that of woven fabrics, its lateral extension, elasticity and softness are not as good as weft-knitted fabrics. Since the warp knitting is connected horizontally by warp wales a...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): D04B1/14D04B1/16D04B1/18D04B1/10
CPCD04B1/14D04B1/16D04B1/18D04B1/10D10B2331/10D10B2201/02D10B2331/04
Inventor 吕伟郝梦梦曹媛媛卢光明牛金海梁明钰周章范陈新刚刘娇张慧颖
Owner LUTAI TEXTILE
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Eureka Blog
Learn More
PatSnap group products