Preparation formula of non-metallic mineral casting

A technology for non-metallic minerals and castings, applied in the field of mineral casting formulations and non-metallic mineral castings preparation formulations, can solve the problems of poor workability, low fluidity, and easy segregation of mixtures, and improve workability and fluidity. , the internal structure is dense, the internal structure is more effective

Pending Publication Date: 2022-03-25
常州高鼎新材料科技有限公司
View PDF3 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] The aggregate gradation used in the preparation of existing mineral castings is a discontinuous gradation. The disadvantages of this discontinuous gradation are that the mixture is easy to segregate, has poor workability and low fluidity.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Preparation formula of non-metallic mineral casting
  • Preparation formula of non-metallic mineral casting

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0028] see figure 1 As shown, the present invention provides a kind of technical scheme, and the formula for the preparation of this non-metallic mineral casting includes: epoxy resin A component 7.0%, epoxy resin B component 1.68%, fly ash 7.0%, quartz sand 35.0%, Crushed stone 37.0%, increasing the amount of fly ash will help improve the fluidity of the mixture.

[0029] The quartz sand is composed of the following three kinds of quartz sand particles measured according to the weight percentage of the total composition: 15.0% of particles with a particle size of 0.06mm, 7.0% of particles with a particle size of 1.18mm, and 13.0% of particles with a particle size of 2.0mm, using different specifications The size of the quartz sand particles, the mixture is not easy to segregate.

[0030] The crushed stone is composed of the following two kinds of crushed stone particles measured according to the weight percentage of the total composition: 20.0% of particles with a particle s...

Embodiment 2

[0044] see figure 1 As shown, the present invention provides a kind of technical scheme, and the prescription of this non-metallic mineral casting comprises: epoxy resin A component 8.0%, epoxy resin B component 1.92%, fly ash 8.0%, quartz sand 45.0%, Crushed stone 47.0%, increasing the amount of fly ash will help improve the fluidity of the mixture.

[0045] The quartz sand is composed of the following three kinds of quartz sand particles measured according to the weight percentage of the total composition: 18.0% of particles with a particle size of 0.3mm, 10.0% of particles with a particle size of 2.36mm, and 17.0% of particles with a particle size of 5.0mm, using different specifications The size of the quartz sand particles, the mixture is not easy to segregate.

[0046] The crushed stone is composed of the following two kinds of crushed stone particles measured according to the weight percentage of the total composition: 25.0% of particles with a particle size of 8.0mm, ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
particle sizeaaaaaaaaaa
particle sizeaaaaaaaaaa
particle sizeaaaaaaaaaa
Login to view more

Abstract

The invention discloses a preparation formula of a non-metallic mineral casting, and relates to the technical field of application of non-metallic mineral castings. The design is reasonable, the formula for preparing the non-metallic mineral casting comprises 7.0-8.0% of an epoxy resin component A, 1.68-1.92% of an epoxy resin component B, 7.0-8.0% of fly ash, 35.0-45.0% of quartz sand and 37.0-47.0% of gravel, adopted aggregate grading is continuous grading, a mixture is not prone to segregation, workability and fluidity are improved, the mixing amount of the fly ash is increased to 7-8% from 3-3.5%, and the mixing amount of the fly ash is increased to 7-8% from 3-3.5%. The ratio of the epoxy resin component A to the epoxy resin component B is 25: 6, so that the internal structure is denser, the compressive strength, the breaking strength and the elastic modulus are increased, the compressive strength is increased to 170 MPa, the breaking strength is increased to 35 MPa, and the elastic modulus is increased to 40 GPa.

Description

technical field [0001] The invention relates to a formula for mineral castings, in particular to a formula for preparing non-metallic mineral castings, and relates to the technical field of casting applications. Background technique [0002] The product of mineral casting is mineral casting, which is a future-oriented environmentally friendly material. As a structural part of a machine, it can replace traditional cast iron in some applications due to its price and performance advantages. One is called resin mineral casting with resin glue as binder, and the other is called polymer mineral casting with polymer nano powder as penetrating agent. [0003] The aggregate gradation used in the preparation of existing mineral castings is discontinuous gradation. The disadvantages of this discontinuous gradation are that the mixture is easy to segregate, has poor workability and low fluidity. Therefore, a non-metallic mineral casting preparation formula is proposed to address the ab...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C04B26/14
CPCC04B26/14C04B2201/50C04B18/08C04B14/06C04B14/02
Inventor 高原
Owner 常州高鼎新材料科技有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap