Luminescent resin glass particle

A technology of resin particles and resin glass, applied in the direction of luminescent materials, chemical instruments and methods, etc., can solve the problems of not having the function of luminescence, etc., and achieve the goal of improving ornamental performance and practicality, good light storage and luminescence, and easy promotion and application Effect

Pending Publication Date: 2022-04-12
蒋曌
View PDF0 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The invention provides a luminescent resin glass particle, which solves the problem that the existing luminescent resin particle does not have the function of luminescence

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment

[0018] A luminescent resin glass particle, including resin particles and a luminescent layer, the luminescent layer includes luminescent powder and resin glue, the luminescent layer is wrapped on the outside of the resin particle, the diameter of the resin particle is 5mm-8mm, and the resin The processing steps for pellets include:

[0019] S1: Stir the luminescent powder and the resin glue evenly, wherein the ratio of the luminescent powder to the resin glue is 6:4;

[0020] S2: Then put the screened resin particles into the blender, add the luminous raw material in the step S1, and fully stir evenly;

[0021] S3: Put the stirred resin particles into a dryer, wherein the temperature of the dryer is 80° C., and the drying time is 20-25 minutes;

[0022] S4: Put the dried resin particles into the resin glue again, then wrap the ceramic particles with fluorescent powder, and dry to obtain the finished product.

[0023] Specifically, in S1, in the ratio of percentages, the prop...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
diameteraaaaaaaaaa
particle diameteraaaaaaaaaa
particle diameteraaaaaaaaaa
Login to view more

Abstract

The invention belongs to the technical field of luminescent materials, and discloses a luminescent resin glass particle, which comprises a resin particle and a luminescent layer, the luminescent layer comprises luminescent powder and a resin adhesive, the luminescent layer wraps the outside of the resin particle, the diameter of the resin particle is 5mm-8mm, and the thickness of the luminescent layer is 10mm-10mm. The processing steps of the resin particles comprise: S1, uniformly stirring luminescent powder and a resin adhesive according to a ratio of 6: 4; s2, putting the screened resin particles into a stirrer, adding the luminous raw material in the step S1, and fully and uniformly stirring; s3, the stirred resin particles are put into a drying machine, the temperature of the drying machine is 80 DEG C, and the drying time is 20-25 minutes; s4, the dried resin particles are put into the resin adhesive again, then the ceramic particles are wrapped with the fluorescent powder and dried, and the finished product is obtained.The resin glass particles are combined with the fluorescent powder and the resin adhesive, the purposes of light storage and light emitting can be better achieved, the problem that resin glass in the existing market is single in function is solved, and application and popularization are facilitated.

Description

technical field [0001] The invention belongs to the technical field of luminescent materials, and in particular relates to luminescent resin glass particles. Background technique [0002] Resin glass is made of hard plastic with high transparency, made of polystyrene, the same thickness, higher impact strength than glass, and has better light transmission. At present, the existing resin glass does not have the function of luminescence, and at the same time Existing resin glass does not have decoration and appreciation. Contents of the invention [0003] In order to solve the problems raised in the above-mentioned background technology. The invention provides a luminescent resin glass particle, which solves the problem that the existing luminescent resin particle does not have the function of luminescence. [0004] In order to achieve the above object, the present invention provides the following technical solutions: a luminescent resin glass particle, including resin par...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C08L25/06C09K11/02
Inventor 蒋曌
Owner 蒋曌
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap