High-barrier biodegradable material as well as preparation method and application thereof
A degradable material and high barrier technology, which is applied in the direction of bio-packaging, sustainable manufacturing/processing, and sustainable packaging industry. Gas barrier properties and the effect of a wide range of raw material sources
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Image
Examples
Embodiment 1~4 and comparative example 1~4
[0038]The polyfurandicarboxylic acid / butylene diglycolate used is prepared by the following method: dimethyl furan-2,5-dicarboxylate, diglycolic acid and butanediol are in a mole ratio of 1:1:3 The ratio was added to the reaction kettle with nitrogen, mixed with mechanical stirring, then dibutyltin oxide was added as a catalyst and the reaction temperature was raised to 180 ° C; after prepolymerization for 3-4 hours, antimony trioxide was added to the reaction kettle , the reaction temperature was raised to 220° C. and vacuumed to 30-50 Pa. After continuing the reaction for 2 h, the reaction was terminated to obtain polyfurandicarboxylic acid / butylene glycol ester with a weight-average molecular weight of 70,000 g / mol.
[0039] In the above-mentioned polyfurandicarboxylic acid / butylene glycolate, the molar ratio of the first repeating unit of the structure shown in formula (I) and the second repeating unit of the structure shown in formula (II) is 1:1,
[0040]
[0041] The...
Embodiment 1
[0044] (1) Dry PBDF and PGA in a vacuum oven with a temperature of 60° C. for 10 hours; then 80 parts of dried PBDF, 20 parts of dried PGA, 1 part of Joncryl ADR-4468, 0.5 part of epoxy castor oil , 0.4 parts of silicon dioxide, 0.3 parts of hindered phenolic antioxidant 1010 and 0.3 parts of phosphite antioxidant 168 were added to the high-speed mixer, and stirred and mixed evenly at a temperature not higher than 40 ° C to obtain cold mixing material;
[0045] (2) adding above-mentioned cold mixing material to the twin-screw extruder hopper with a length-to-diameter ratio of 40:1, melt blending, extrusion granulation to obtain high-barrier biodegradable material pellets; the setting of the twin-screw extruder The fixed temperature is 190°C, 200°C, 210°C, 215°C, 215°C, 220°C, 220°C, 225°C, 225°C, 225°C, 220°C in sequence from the feed port to the head, and the screw speed is 200rpm.
Embodiment 2
[0047] The high-barrier biodegradable material pellets were obtained with reference to the preparation process of Example 1, the difference being:
[0048] The raw material formula is: 70 parts of dried PBDF, 30 parts of dried PGA, 1 part of Joncryl ADR-4468, 0.5 part of epoxidized soybean oil, 0.4 part of oleic acid amide, 0.3 part of hindered phenolic antioxidant 1010 and 0.3 parts of phosphite antioxidant 168;
[0049] The set temperature of the twin-screw extruder is 190°C, 200°C, 210°C, 220°C, 220°C, 225°C, 225°C, 230°C, 230°C, 230°C, 225°C from the feed port to the head. .
PUM
Property | Measurement | Unit |
---|---|---|
Melt index | aaaaa | aaaaa |
Abstract
Description
Claims
Application Information
![application no application](https://static-eureka.patsnap.com/ssr/23.2.0/_nuxt/application.06fe782c.png)
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap