Crystalline jelly wax and its production process

A manufacturing method and technology of jelly wax, which is applied in the production of candles and fatty acids, etc., can solve the problems of poor burning effect of jelly wax and affect the use effect of jelly wax, achieve rich varieties and expression modes, small shrinkage ratio, and improve burning effect Effect

Inactive Publication Date: 2004-09-08
QINGDAO KINGKING APPL CHEM CO LTD
View PDF1 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] 2. The actual burning effect of this kind of jelly wax is not good, which affects the actual use effect of jelly wax

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0019] The manufacturing method is carried out as follows,

[0020] A. Pump the white oil into a reaction tank and heat it;

[0021] B. Then add 6.7 grams of thermoplastic styrene-butadiene rubber to every 85 grams of white oil. Its commercial code is KratonG1650, with a relative density of 0.91 and a hardness of 72. Stir at a temperature of 120°C until the thermoplastic styrene-butadiene rubber and white oil are fully mixed. (2~4 hours), stop stirring;

[0022] C. Lower the temperature to 100°C, then add 5 grams of myristic acid for every 88 grams of white oil, and stir evenly;

[0023] D. Pour the above-mentioned wax solution into the tire mold at 90°C;

[0024] E. Add wick;

[0025] F. cooling crystallization.

Embodiment 2

[0027] The manufacturing method is carried out as follows,

[0028] A. Pump the white oil into a reaction tank and heat it;

[0029] B. Then add 6.4 grams of thermoplastic styrene-butadiene rubber to every 88 grams of white oil. Its commercial code is KratonG1650, relative density is 0.91, and hardness is 72; the temperature is 105 ° C, stirring, and other thermoplastic styrene-butadiene rubber and white oil are fully mixed. (2~4 hours), stop stirring;

[0030] C. Lower the temperature to 110°C, then add 8 grams of myristic acid for every 88 grams of white oil, stir evenly; and add appropriate amount of spices and pigments to mix and stir;

[0031] D. Pour the above-mentioned wax solution into the tire mold at 100°C;

[0032] E. Add wick;

[0033] F. cooling crystallization.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
hardnessaaaaaaaaaa
Login to view more

Abstract

The crystalline jelly candle is compounded with white oil and thermoplastic styrene-butadiene rubber mixed fully and added myristic acid, and the styrene-butadiene rubber is compounded with styrene in 70wt% and butadiene in 30wt%. The addition of proper amount of myristic acid makes the jelly candle generate crystalline matter possessing excellent artistic effect of representing snowflake and being beautiful.

Description

Technical field [0001] The invention belongs to wax products; in particular, it relates to a novel crystalline jelly wax material and a manufacturing method of the wax product material. Background technique [0002] Existing jelly wax is disclosed in Chinese patent ZL00111030.6, and the jelly wax produced by this method and proportioning is transparent. It has the following disadvantages: [0003] 1. Since this kind of jelly wax is mainly used to make handicraft candles, this kind of transparent jelly wax has less changes in the appearance of candles, and cannot produce various crystallization effects such as snowflakes; [0004] 2. The actual burning effect of this jelly wax is not good, which affects the actual use effect of the jelly wax. [0005] So the above-mentioned deficiencies in jelly wax need to be solved urgently. Contents of the invention [0006] The object of the present invention is to provide a kind of crys...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C11C5/00
Inventor 陈索斌法芸
Owner QINGDAO KINGKING APPL CHEM CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap