Steel plate wall and its mfg. method

A manufacturing method and steel plate wall technology, which can be applied to sheet pile walls, water conservancy projects, artificial islands, etc., can solve the problems of female joint material 73 deformation, different water-proof and reliable functions, and the inability to use automatic welding machines, etc., to achieve reduction Welding cost, easy automatic welding, and the effect of reducing water leakage

Inactive Publication Date: 2004-10-13
NIPPON STEEL CORP +1
View PDF10 Cites 6 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0014] In addition, in the invention described in Japanese Laid-Open Patent Publication No. 07-324329 (Patent Document 2), the joint is welded, but it is different from that for discarded water because it is water-proof for buildings, that is, water-proof for groundwater in the foundation. For the water-proofing of waste disposal sites, etc., the degree of water-proofing property only needs to match the degree of drainage facilities installed on the side of buildings, which is not the same as the purpose of the present invention is to seek higher water-proofing property and reliable function.
[0015] In addition, in the invention described in Japanese Laid-Open Patent Publication No. 07-324329 (Patent Document 2), since the female joint material 73 with a special shape is used, it is worried that the female joint material 73 will be deformed when driving in, and it is suspected that the groundwater in the excavated foundation The reliability of the vertical welding of the exposed joints in the wet state or in the water state, in addition, the above method cannot be used with automatic welding machines

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Steel plate wall and its mfg. method
  • Steel plate wall and its mfg. method
  • Steel plate wall and its mfg. method

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0162] figure 1 A flow chart showing an example of the construction procedure when using the steel sheet pile as the jointed steel material and the temporary steel material as the first invention of the present invention is carried out in the following order.

[0163] According to the construction capacity of the steel sheet pile driving machine and the number of units used, the construction of the steel sheet pile wall starts from any part of the water-resistant steel sheet wall ( figure 1 a).

[0164] In at least one place, drive temporary sheet piles ( figure 1 b), forming an area enclosed by part of the sheet pile wall and temporary sheet piles ( figure 1 c).

[0165] Excavating to remove sand and soil in enclosed areas ( figure 1 After d), clean the joints of the steel sheet pile walls in the area ( figure 1 e).

[0166] Then, install automatic welding machines in the area ( figure 1 f), for automatic welding ( figure 1 g).

[0167] After confirming that ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

A steel wall and a manufacturing method thereof are provided to improve waterproofing efficiency and construction efficiency, and to cut down construction cost by forming the automatic welding space of the joint part and linearly connecting plural asymmetrical U-shaped steel sheets. A steel sheet wall is constructed(a), and a temporary steel sheet is constructed(b). A closed section is formed and surrounded by the part of the steel sheet wall and the temporary steel sheet(c). Earth or sand is excavated and removed from the closed section(d), and a joint part of the steel sheet wall is washed and cleaned in the closed section(e). An automatic welding machine is set in the closed section(f), and welding is automatically performed(g). The temporary steel sheet is removed after securing waterproofing(h). The waterproof steel wall is constructed by repeating the steps.

Description

technical field [0001] The invention relates to a steel plate wall suitable for places requiring water isolation, such as waste disposal sites, underground walls of buildings, and road retaining walls, and a manufacturing method thereof. Background technique [0002] Steel sheet piles are often used for retaining walls in the construction of underground structures and temporary embankments in the construction of harbor and water facilities. The reason is that the high-rigidity wall made of steel, a high-quality material, not only can be built in a short construction period, but also has relatively good water-proof performance. [0003] Of course, the steel material itself of the steel sheet pile main body does not pass water at all, but in the fitted state, since water passes through the gap part existing in the joint part, the gap in the joint part has a great influence on the water resistance of the steel sheet pile. [0004] In general, even if the joint after driving is...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): E02D5/04E02D5/14E02D29/02
CPCE02D5/14E02D2600/20
Inventor 鹿野裕喜田浩中野启真池田昌弘吉田伦夫
Owner NIPPON STEEL CORP
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Eureka Blog
Learn More
PatSnap group products