Daily use cosmetics using halogen cement product as substrate and its preparing method

A technology for cosmetics and brine cement, which is applied in the field of preparation to achieve the effects of solving processing problems, promoting metabolism and alleviating skin allergies

Inactive Publication Date: 2005-01-12
JIUDA PINZHONG SALTS SICHUAN
View PDF0 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

So far, it has not been reported that the effective use of bittern cement and its products as a matrix of daily cosmetics

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0023] A daily cosmetic based on bittern cement products, which is characterized in that it is prepared from the following raw materials in the weight ratio: 20% bittern cement products, 20% ointment base, 1% traditional Chinese medicine extract, 20% Moisturizer, 1% preservative, 35% water and 3% essence.

[0024] The bittern cement product is made by washing the bittern cement and filtering it through a 20-mesh sieve, then baking the slurry at a temperature of 200°C, and crushing the obtained solid into a powder form through a 300-mesh sieve solid.

[0025] Described bittern cement refers to the well mine salt production by-product containing the metal ion of following percentage by weight: Na + : 2.31%, Ca 2+ : 0.89%, Mg 2+ : 0.67%, K + : 1.47%, Li + : 0.16%.

[0026] The ointment base is selected from: petrolatum, petrolatum plus stearic acid, petrolatum plus glyceryl monostearate, or stearic acid plus glyceryl monostearate.

[0027] Described humectant is selected f...

Embodiment 2

[0031] A daily-use cosmetic based on bittern cement products, which is characterized in that it is prepared from the following raw materials in the weight ratio: 80% bittern cement products, 1% vaseline, 2% traditional Chinese medicine extracts, 1% Glycerin, 1% Benzoic Acid, 15% Water and 1% Fragrance.

[0032] Add glycerin to the above-mentioned raw material vaseline, grind it evenly, add traditional Chinese medicine extract, benzoic acid, and essence while grinding it, add bittern cement products after grinding it evenly, add water and stir until uniform to obtain the product.

[0033] The bittern cement product is a powder made by washing the bittern cement, filtering it through a 300-mesh sieve, and then baking the slurry at a temperature of 30°C. The obtained solid is crushed and then passed through a 100-mesh sieve shaped solid.

[0034] Described bittern cement refers to the well mine salt production by-product containing the metal ion of following percentage by weight...

Embodiment 3

[0036] A daily cosmetic based on bittern cement products, which is characterized in that it is prepared from the following raw materials in the weight ratio: 41.8% bittern cement products, 15% vaseline, 2% stearic acid, 5% Chinese medicine extract, 3% glycerin, 0.2% ethyl paraben, 30% water and 3% essence.

[0037] Add glycerin to the above-mentioned vaseline and stearic acid and grind until uniform, add Chinese medicine extract, ethylparaben and essence while grinding, add bittern cement products after grinding, add water and stir until uniform to obtain the product.

[0038] The bittern cement product is a powder made by washing the bittern cement, filtering it through a 100-mesh sieve, and then baking the slurry at a temperature of 80°C. The obtained solid is crushed and then passed through a 20-mesh sieve shaped solid.

[0039] Described bittern cement refers to the well mine salt production by-product containing the metal ion of following percentage by weight:

[0040] ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

A cosmetic is prepared from bittern clay as matrix, ointment matrix, the extract of Chinese-medicinal materials, humectan, antiseptic, water and essence through proportionally and sequentially mixing.

Description

Technical field: [0001] The invention relates to a daily cosmetic, in particular to a daily cosmetic based on a brine cement product, a by-product of mine salt production. The present invention also relates to a preparation method of the product. Background technique: [0002] Halogen cement is a natural mineral that coexists with salt and is stored in more than 0 to 3,000 meters underground. For a long time, as a by-product of salt, there are usually only two ways to deal with bittern cement: one is to randomly pile up on the surface, which causes a waste of land resources and is not sustainable; the other is to discharge it into rivers, which often causes river water pollution and river siltation. Both of the above two traditional treatment methods have caused an impact on the environment. According to a large amount of data and experiments, besides containing a certain amount of salt, bittern cement is also rich in a variety of rare minerals. These rare minerals can be...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Inventor 蔡晓波张廷兰
Owner JIUDA PINZHONG SALTS SICHUAN