Bamboo material transversal surface functional composite board and production thereof

A composite board and cross-section technology, applied in chemical instruments and methods, wood layered products, layered products, etc., can solve the problems of not showing the natural beauty of bamboo, affecting the appearance of the surface, and single products, so as to achieve good purification and repair Indoor environment, the effect of realizing value-added benefits

Inactive Publication Date: 2005-05-11
辜健思
View PDF0 Cites 5 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The main disadvantages of the bamboo composite board prepared by this method are as follows: because the radial surface is upward, the bamboo joints will affect the appearance of the surface; the surface of the bamboo sheet will warp due to the change of heat and cold tide environment; the natural beauty of the bamboo cannot be displayed due to the veneer ; Bamboo slices need to be pressed into a flat plate under high temperature and high pressure, and the cost is relatively high; the product is relatively single and cannot meet the current market demand

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Bamboo material transversal surface functional composite board and production thereof
  • Bamboo material transversal surface functional composite board and production thereof
  • Bamboo material transversal surface functional composite board and production thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0028] Below in conjunction with accompanying drawing, the present invention will be further described:

[0029] A bamboo cross-section composite board, which at least includes a bamboo slab layer and a composite material layer glued together with it, and the bamboo slab layer is formed by sticking together several small bamboo pieces of equal length. The composite material layer is an activated carbon layer, a multifunctional carbon plate layer, a wood layer or a polymer material layer.

[0030] The preparation method of above-mentioned bamboo cross-section composite board:

[0031] It includes the following process steps: blanking and splitting, cooking, drying, sizing and assembling, drying, cutting and gluing.

[0032] The blanking and cutting refers to cutting the adult bamboo into a bamboo tube of a set length (such as figure 1 shown), and then cut longitudinally along the bamboo tube, and then separate the cut bamboo (such as figure 2 Shown) longitudinally cut into ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

A functional composite bamboo board is composed of the bamboo and composite material layer, and is prepared through cutting bamboo, splitting bamboo to obtain bamboo strips, steaming, baking, coating adhesive, splicing, drying, cutting, and splicing again.

Description

technical field [0001] The invention relates to a composite board made of bamboo as a raw material and a preparation method thereof. The product has superior performance and can be widely used in building decoration, furniture, handicraft products, bamboo floor tiles, vehicle floor materials and the like. Background technique [0002] The existing bamboo composite board cuts the bamboo diameter into bamboo slices, or crosses bamboo strips into mats, and then pressurizes the bamboo slices through high temperature and high pressure to make them dry and form them into flat plates. Arranging flat bamboo slices into planar bamboo slices and processing wood, and the obtained single-piece boards are cross-stacked and laminated and bonded. The main disadvantages of the bamboo composite board prepared by this method are as follows: because the radial surface is upward, the bamboo joints will affect the appearance of the surface; the surface of the bamboo sheet will warp due to the ch...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): B32B21/00
Inventor 辜健思
Owner 辜健思
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com