Special-shaped copper-clad aluminium wire and method of production

A technology of copper-clad aluminum wire and production method, applied in the direction of rod/rod/wire/strip conductor, conductor, electrical components, etc., can solve the problem of not meeting the requirements of special-shaped composite wire, and achieve the effect of solving high price

Inactive Publication Date: 2005-08-17
葛成林
View PDF1 Cites 11 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] The present invention aims to solve the technical problems existing in the prior art that cannot meet the requirements of special-shaped composite wires, and provides a special-shaped copper-clad aluminum wire and its production method

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0015] a. Use purchased round copper-clad aluminum composite wires;

[0016] b. Rolling the composite wire with a pressure of 20-100 tons at a rolling speed of 100-800m / min to form a flat composite wire;

[0017] c. The mold is drawn and shaped, and the shape of the mold is the final product shape, such as oblate, square, rectangular, flat diamond or oval, etc.;

[0018] d. Quenching treatment, the quenching temperature is 260~350℃.

Embodiment 2

[0020] a. Coat the copper strip on an aluminum rod with a diameter of 8-20mm, and draw it with a speed of 50-150m / min and a reduction rate of 3-18% to a diameter of 3-10mm;

[0021] b. Rolling the composite wire with a pressure of 20-100 tons at a rolling speed of 100-800m / min to form a flat composite wire;

[0022] c. The mold is drawn and shaped, and the shape of the mold is the final product shape, such as oblate, square, rectangular, flat diamond or oval, etc.;

[0023] d. Quenching treatment, the quenching temperature is 260~350℃.

Embodiment 3

[0025] Others are the same as in Example 1 or 2, except that the drawing speed is 100-800 m / min through the drawing and shaping of the mold.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
diameteraaaaaaaaaa
Login to View More

Abstract

This invention discloses an allotype copper and aluminum wire, which comprises aluminum core and copper cover layer with non-round section. The process method comprises the following steps: processing round copper coil and aluminum compound wire; using twenty to one hundred tons of pressure to roll the wires with speed as 100-800m / min; shaping by mode pulling; match fire processing with temperature of 260-350 Deg. C.

Description

Technical field: [0001] The invention relates to a composite wire and a production method, in particular to a special-shaped (non-circular) copper-clad aluminum wire and a production method. Background technique: [0002] At present, people have developed a variety of composite wires to solve the problems of the preciousness of copper wires, the poor conductivity of aluminum wires and the increasingly scarce copper resources, such as copper-clad steel, copper-clad aluminum and other composite wires. The production method is basically the method disclosed in the Chinese invention patent application number 98112410.0 and the name is "a copper-aluminum composite wire and its production process", that is, "the fully annealed copper strip (or copper tube) is fully annealed with a metal wire wheel. After removing the passivation layer on the surface of the aluminum rod and the aluminum rod, the aluminum rod is wrapped into the copper tape by the cladding method, and the copper tape is ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): H01B5/00H01B5/02H01B13/00
Inventor 葛成林
Owner 葛成林
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com