Composite material of polypropylene in low smell and preparation method

A composite material, polypropylene technology, applied in the preparation of the composite material, low-odor polypropylene composite material field, can solve the problems affecting material properties, large differences, uneven distribution of micropore size, etc., to achieve simple preparation process, Excellent physical and mechanical properties and low cost

Inactive Publication Date: 2006-02-01
SHANGHAI PRET COMPOSITES
View PDF0 Cites 84 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

At the same time, we found that after the material was added with activated carbon as an adsorbent, due to the uneven distribution of micropore size in the activated carbon, the difference was huge, and the largest pore size was as large as about 1000 angst

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0044] Dry-mix polypropylene 53.65%, talcum powder 40%, molecular sieve 5%, heat stabilizer DSTP 0.9%, heat stabilizer 3114 0.3%, heat stabilizer 618 0.15% in a high-speed mixer for 3-5 minutes, and then In the twin-screw extruder, it is melt-extruded and granulated. The process is: 200-210°C in the first zone, 210-220°C in the second zone, 210-220°C in the third zone, and 205-215°C in the fourth zone; the residence time is 1-2 minutes, the pressure is 12-18Mpa.

Embodiment 2

[0046] Dry-mix polypropylene 55.65%, talcum powder 40%, molecular sieve 3%, heat stabilizer DSTP 0.9%, heat stabilizer 3114 0.3%, heat stabilizer 618 0.15% in a high-speed mixer for 3-5 minutes, and then In the twin-screw extruder, it is melt-extruded and granulated. The process is: 200-210°C in the first zone, 210-220°C in the second zone, 210-220°C in the third zone, and 205-215°C in the fourth zone; the residence time is 1-2 minutes, the pressure is 12-18Mpa.

Embodiment 3

[0048] Dry mix polypropylene 56.65%, talcum powder 40%, molecular sieve 2%, heat stabilizer DSTP 0.9%, heat stabilizer 3114 0.3%, heat stabilizer 618 0.15% in a high-speed mixer for 3-5 minutes, and then In the twin-screw extruder, it is melt-extruded and granulated. The process is: 200-210°C in the first zone, 210-220°C in the second zone, 210-220°C in the third zone, and 205-215°C in the fourth zone; the residence time is 1-2 minutes, the pressure is 12-18Mpa.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

A polypropene composition with low odor is proportionally prepared from polypropene, talc powder, molecular sieve (powdered silicoaluminate of alkali-metal), toughening agent poe, and thermal stabilizer.

Description

technical field [0001] The invention relates to a low-odor polypropylene composite material, and more particularly relates to preparing a low-odor polypropylene composite material by adding an odor inhibitor that can effectively suppress the unpleasant smell in the polypropylene composite material. The invention also relates to a method for preparing the composite material. Background technique [0002] In recent years, due to the rapid development of engineering modification technology of polypropylene materials, its application in the automotive field has become more and more extensive. However, as an important part of engineered polypropylene materials in the automotive field, various automotive interior parts made of engineered polypropylene materials, although they can meet the corresponding requirements in all aspects of performance, However, due to the fact that these materials emit certain unpleasant odors to varying degrees, they have been increasingly questioned b...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C08L23/12C08K5/524B29B9/12B29C47/40
Inventor 翁永华张祥福周文
Owner SHANGHAI PRET COMPOSITES
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap