Durable antifake blue carbon powder for laser printer use and producing method thereof

A laser printer and durability technology, applied in optics, electrical recording, instruments, etc., can solve the problems of poor durability, no anti-counterfeit performance of color graphic materials, and difficulty in distinguishing the authenticity, etc., and achieve the effect of good durability

A laser printer and durability technology, applied in optics, electrical recording, instruments, etc., can solve the problems of poor durability, no anti-counterfeit performance of color graphic materials, and difficulty in distinguishing the authenticity, etc., and achieve the effect of good durability

CN1975587AInactive Publication Date: 2007-06-06周学良
0 Cites 2 Cited by

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0021] Select 80 parts of polyester resin, 5 parts of polypropylene wax, 3 parts of charge regulator, 7 parts of iron blue, 10 parts of ultraviolet fluorescent powder, 2 parts of dimethyl dichlorosilane and 7 parts of hexamethyl base disilazane. Among them the charge regulator is a metal chromium salicylate.

[0022] The polyester resin, polypropylene wax, iron blue, ultraviolet fluorescent powder and charge regulator are first poured into a mixer and mixed evenly to form a compound.

[0023] Then put the above-mentioned mixture into an extruder, extrude the above-mentioned mixture at a temperature of 90° C., and press it into a tablet.

[0024] Then, the flake mix was cooled to 40°C and crushed into pieces.

[0025] Thereafter, the above fragments were pulverized into pulverized powder with a particle diameter of 30 μm by a pulverizer.

[0026] After that, use a pressure of 7kg / m 2 The above-mentioned crushed powder is air-pulverized in a fluidized bed pulverizer, classif...

Embodiment 2

[0030] Select 85 parts of polyester resin, 8 parts of polypropylene wax, 6 parts of charge regulator, 8.5 parts of iron blue, 15 parts of ultraviolet fluorescent powder, 3 parts of dimethyldichlorosilane and 8 parts of hexamethyl base disilazane. Among them, the charge regulator is a metal azochrome compound.

[0031] The polyester resin, polypropylene wax, iron blue, ultraviolet fluorescent powder and charge regulator are first poured into a mixer and mixed evenly to form a compound.

[0032] Then put the above-mentioned mixture into an extruder, extrude the above-mentioned mixture at a temperature of 120° C., and press it into a tablet.

[0033] The flake mix was then cooled to 45°C and crushed into pieces.

[0034] Thereafter, the above fragments were pulverized into pulverized powder with a particle diameter of 40 μm by a pulverizer.

[0035] After that, use a pressure of 7kg / m 2 The above-mentioned crushed powder is air-pulverized in a fluidized bed pulverizer, classi...

Embodiment 3

[0039] Select 90 parts of polyester resin, 10 parts of polypropylene wax, 9 parts of charge regulator, 10 parts of iron blue, 20 parts of ultraviolet fluorescent powder, 4 parts of dimethyldichlorosilane and 10 parts of hexamethyl base disilazane. Among them the charge regulator is a metal chromium salicylate.

[0040] The polyester resin, polypropylene wax, iron blue, ultraviolet fluorescent powder and charge regulator are first poured into a mixer and mixed evenly to form a compound.

[0041] Then put the above-mentioned mixture into an extruder, extrude the above-mentioned mixture at a temperature of 150° C., and press it into a tablet.

[0042] Then, the flake mixture was cooled to 50°C and crushed into pieces.

[0043] Thereafter, the above fragments were pulverized by a pulverizer into pulverized powder having a particle diameter of 50 μm.

[0044] After that, use a pressure of 7kg / m 2 The above-mentioned crushed powder is air-pulverized in a fluidized bed pulverizer...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
Particle sizeaaaaaaaaaa
Particle sizeaaaaaaaaaa
Particle sizeaaaaaaaaaa
Login to View More

Abstract

This invention discloses a kind of durability guard against false blue carbon dust used for laser printer and its preparation method. It is produced by mixing, 80-90 portion polyester resin, 5-10 portion polypropylene wax, 3-9 portion electric charge conditioning agent , 7-10 portion iron blue , 10-20 portion ultraviolet fluorescent powder, 2-4 dimethyl two chlorine silane and 7-10 portion six methyl two silicons nitrogen alkane, and doing the following steps such as molding, smashing and sifting. Use this laser printer durability guard against false blue carbon dust print color picture culture and blue print, not only the color's durability is good, be able to satisfy the request that the file reporters, need to save for a long time, it can also differentiate out true-false, has the function of guards against the false, makes the false maker has no loophole to exploit. Especially be applied to print reporters such as signature, and file.

Description

technical field [0001] The invention relates to a carbon powder and a preparation method thereof. Specifically, it is durable anti-counterfeiting blue toner for laser printers used to print archival graphic materials or anti-counterfeiting marks. Suitable for ordinary laser printers or color laser printers. Background technique [0002] With the advancement of science and technology, the level of office automation is getting higher and higher, and archives documents including signatures and seals are gradually replaced by traditional manual operations with automatic printing by laser printers. The use of laser printers to automatically print archival documents requires that the toner must have color durability. Only in this way can the long-term preservation requirements of archival documents be met. [0003] At present, the main components of blue toner used in laser printers are organic pigments, and their color durability is poor. The blue imprints and color graphics pr...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine