Room temperature curable silicone sealant

Inactive Publication Date: 2001-12-06
MOMENTIVE PERFORMANCE MATERIALS INC
View PDF0 Cites 37 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, increasing the filler content of the sealant composition also increases the viscosity of the composition, leading to difficulties in extrusion from the packaging.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Room temperature curable silicone sealant
  • Room temperature curable silicone sealant

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0040] The sealant composition of the Example was an acetoxy sealant comprising 67.2 percent by weight ("wt %") of a hydroxy-terminated poly(dimethylsiloxane) polymer, 20 wt % of a hydrocarbon fluid, 9 wt % untreated fumed silica, 3.5 wt % of catalyst solution and 0.3 wt % other additives. The catalyst solution silane contained acetoxy-functional silane crosslinking agents and a condensation cure catalyst. The hydrocarbon fluid (Conosol.TM. C-200 hydrocarbon fluid) had a nominal composition of about 60 wt % cycloparaffinic hydrocarbons, from 5 to 6 wt % n-paraffinic hydrocarbons, with the remainder being iso-paraffinic hydrocarbons, and exhibited an aromatic content of less than about 0.5 wt %. The sealant composition was tested for physical properties after curing for 7 days at 75.degree. C. and 50% relative humidity. The ASTM test methods used and test results are listed in the Tables below.

1 Property ASTM test # Result Application rate C1183 400 (grams / minute) Tack free time C679...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
Percent by massaaaaaaaaaa
Percent by massaaaaaaaaaa
Percent by massaaaaaaaaaa
Login to View More

Abstract

A silicone sealant composition containing: (a) a moisture curable organopolysiloxane component, comprising a mixture or reaction product of (i) an organopolysiloxane polymer having hydrolyzable substituent groups and (ii) a polyfunctional silicon compound having two or more hydrolyzable substituent groups, (b) a filler and (c) a hydrocarbon fluid comprising, based on 100 parts by weight of the hydrocarbon fluid, greater than 40 parts by weight cyclic paraffinic hydrocarbons and less than 60 parts by weight noncyclic paraffinic hydrocarbons, exhibits improved tensile, elongation and adhesive properties.

Description

[0001] This application claims priority to U.S. application Ser. No. 60 / 176,823, filed Jan. 19, 2001, which is incorporated by reference in its entirety.[0002] This invention relates to one part, room temperature vulcanizable silicone sealants, and in particular to such sealants having both improved flowability and improved properties upon cure.BRIEF DESCRIPTION OF THE RELATED ART[0003] Silicone compositions that are storable under dry conditions and which, on exposure to moisture, cure to produce elastomers, are widely used as sealants and caulks in building and construction applications. These compositions are often referred to as one part, room temperature vulcanizable ("RTV") compositions. They typically contain a moisture-curable polyorganosiloxane polymer, a filler, and a condensation cure catalyst. When used as sealants, they are typically packaged in a moisture impervious tube and applied to a substrate by extrusion from the packaging tube.[0004] One approach to improving th...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C08L83/04C09K3/10
CPCC08G77/16C08L83/04C09K3/1018C08L2666/28C08L2666/02C08L2666/54Y10S528/901Y10T428/31663
Inventor ATWOOD, ROBERT C.LIN, CHIU-SINGLUCAS, GARY M.
Owner MOMENTIVE PERFORMANCE MATERIALS INC
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com