Method and apparatus for making crystalline pet pellets

Abstract

A method and apparatus for underwater pelletizing and subsequent drying of polyethylene terephthalate (PET) polymers and other high temperature crystallizing polymeric materials to crystallize the polymer pellets without subsequent heating. High velocity air or other inert gas is injected into the water and pellet slurry line to the dryer near the pelletizer exit. The slurry line has a substantially straight component, and air is preferably injected at the end of the straight component nearest the pelletizer exit and in a direction substantially coincident with the axis of the straight component. The air injection significantly increases the speed of the pellets into and out of the dryer such that the PET polymer pellets leave the dryer above at least 135° C., and preferably above 145° C., to self-initiate crystallization.

Description

RELATED APPLICATIONS [0001] This is a continuation application of co-pending application Ser. No. 10 / 717,630, filed Nov. 21, 2003, and hereby claims the priority thereof.FIELD OF THE INVENTION [0002] The present invention generally relates to a method and apparatus for underwater pelletizing and subsequent drying of polyethylene terephthalate (PET) polymers. More specifically, the present invention relates to a method and apparatus for underwater pelletizing PET polymers and subsequent drying the PET polymer pellets in a manner to self-initiate the crystallization process of the PET particles and produce pellets having a crystalline structure rather than an amorphous structure. BACKGROUND OF INVENTION AND PRIOR ART [0003] Underwater pelletizing systems for producing pellets of polymeric or other plastic materials has been known for many years. The starting materials such as plastic polymers coloring agents, additives, fillers and reinforcing agents, and modifiers, are mixed in knead...

AI Technical Summary

Benefits of technology

[0008] In order to achieve a processed PET polymer pellet having the desired crystallinity, the pellet must exit the underwater pelletizing system at a temperature higher than about 135° C. At temperatures at or above this temperature, PET pellets can self-initiate the crystallization process and ultimately provide a crystalline character instead of an amorphous one. Therefore, in accordance with the present invention, the underwater pelletizing system should produce PET pellets in a hot enough condition to self-initiate the desired crystallization. This elevated heat condition can be accomplished by reducing the residence time of the pellets in the water slurry in order to leave enough heat in the PET pellets during the pelletizing and drying stages so that the crystallization process is initiated from inside the pellets. If desired, the pellets can be stored in a heat retaining condition, such as in a heat insulating container, to complete the crystallization process. For example, coated steel or plastic containers should be acceptable, instead of the stainless steel boxes conventionally used.

Problems solved by technology

Typically, increasing the water flow through the water box of the underwater pelletizer and increasing the water temperature, along with pipe dimensional changes and reducing the distance between the pelletizer and dryer unit, does not help to sufficiently maintain the pellet temperature.

Images