High Strength Spring Steel and High Strength Heat Treated Steel Wire for Spring

Abstract

The present invention provides a high strength heat treated steel wire for spring having a tensile strength of 2000 MPa or more which is coiled in the cold state and can achieve both sufficient atmospheric strength and coilability and spring steel used for that steel wire, that is, a high strength heat treated steel wire for a spring characterized by comprising, by mass %, C: 0.5 to 0.9%, Si: 1.0 to 3.0%, Mn: 0.1 to 1.5%, Cr: 1.0 to 2.5%, V: over 0.15 to 1.0%, and Al: 0.005% or less, controlling N to 0.007% or less, further containing one or two of Nb: 0.001 to less than 0.01% and Ti: 0.001 to less 0.005%, and having a tensile strength of 2000 MPa or more, having cementite-based spheroidal carbides and alloy-based spheroidal carbides in a microscopic visual field satisfying an area percentage of carbides with a circle equivalent diameter of 0.2 μm or more of 7% or less and a density of carbides with a circle equivalent diameter of 1 grain/μm² or less, having a prior austenite grain size number of #10 or more, and having retained austenite of 15 mass % or less.

Description

TECHNICAL FIELD[0001]The present invention relates to spring steel which is cold-coiled and has a high strength and high toughness and to heat treated steel wire for a spring.BACKGROUND ART[0002]Due to trends toward weight reduction and higher performance of automobiles, springs have been strengthened and high strength steel having a tensile strength in excess of 1500 MPa after heat treatment has been applied to springs. In recent years, steel wire having a tensile strength in excess of 1900 MPa has also been demanded. The purpose is to secure a material hardness which does not cause problems when the material is used as a spring even though the material softens to some extent by heating in strain reduction annealing, nitriding, and the like when producing the spring.[0003]Further, by nitriding and shot-peening, it is known that the surface layer hardness increases and the durability in spring fatigue is remarkably improved, but the characteristics in the spring are not decided by s...

AI Technical Summary

Benefits of technology

[0010]The inventors discovered that by controlling the N, which was not focused on until now, even if adding alloy elements, it is possible to suppress the formation of undissolved carbides and possible

Problems solved by technology

However, if the steel wire for a cold-coiled spring increases in strength, it often breaks during cold coiling and cannot be formed into a spring shape.

Up until now, both strength and workability (coilability) could not be simultaneously obtained with this, so strength and workability had to be obtained by what may be said to be the indus