A steel rebar and a production method thereof

Inactive Publication Date: 2017-02-02
INST OF RES OF IRON & STEEL JIANGSU PROVINCE
View PDF3 Cites 23 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Benefits of technology

[0006]Therefore, a technical problem to be solved by the present invention is to overcome the technical defects in prior art that steel rebar has poor corrosion resistance performance in ocean environment and cannot me

Problems solved by technology

Meanwhile, the durability problem of steel rebar used as a main structural material becomes increasingly prominent.
The ocean environment is a relatively harsh corrosion environment in the nature, with its special conditions of high temperature, high humidity, and high salinity easily causing corrosion of steel.
Severe corrosion usually occurs in the reinforced concrete structures along the coast of China after 10-15 years on service, which results in damage to the structures, rendering the structures unable to meet their designed service life of 50 years.
Among coated corrosion resistant steel rebar products, epoxy coated steel rebar is researched earliest and used most widely, however, epoxy coated steel rebar has essential disadvantages reflected as: the coating has high brittleness, and is easily damaged and shed off during transporting and processing; defects in the coating might cause conce

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A steel rebar and a production method thereof

Examples

Experimental program
Comparison scheme
Effect test

embodiment 1

[0042]The present embodiment provides a steel rebar, comprising the following elements: C, Si, Mn, P, S, Cr, Mo, Sn, Rare Earth element, Fe and unavoidable impurities, wherein, the weight percentages of the ingredients are as shown in Table 1, the mechanical properties are as shown in Table 2, and the corrosion resistance performance is as shown in Table 3.

[0043]The present embodiment also provides a production method of steel rebar comprising the following steps:

S1: performing preliminary desulfurization of molten iron by using a KR method to control the sulfur content at no more than 0.01%. Because sulfur element as an impurity element would reduce mechanical properties and corrosion resistance performance of steel and normally cannot be removed in a convertor, therefore, in order to reduce the sulfur content in steel, preliminary desulfurization treatment needs to be performed in molten iron. Before performing desulfurization, the blast furnace slag needs to be removed in order t...

embodiment 2

[0044]The present embodiment provides a steel rebar, comprising the following elements: C, Si, Mn, P, S, Cr, Mo, Sn, Rare Earth element, Fe and unavoidable impurities, wherein, the weight percentages of the ingredients are as shown in Table 1, the mechanical properties are as shown in Table 2, and the corrosion resistance performance is as shown in Table 3.

[0045]The present embodiment also provides a production method of steel rebar comprising the following steps:

S1: performing preliminary desulfurization of molten iron by using a KR method to control the sulfur content at no more than 0.01%. Because sulfur element as an impurity element would reduce mechanical properties and corrosion resistance performance of steel and normally cannot be removed in a convertor, therefore, in order to reduce the sulfur content in steel, preliminary desulfurization treatment needs to be performed in molten iron. Before performing desulfurization, the blast furnace slag needs to be removed in order t...

embodiment 3

[0046]The present embodiment provides a steel rebar, comprising the following elements: C, Si, Mn, P, S, Cr, Mo, Sn, Rare Earth element, Fe and unavoidable impurities, wherein, the weight percentages of the ingredients are as shown in Table 1, the mechanical properties are as shown in Table 2, and the corrosion resistance performance is as shown in Table 3.

[0047]The present embodiment also provides a production method of steel rebar comprising the following steps:

S1: performing preliminary desulfurization of molten iron by using a KR method to control the sulfur content at no more than 0.01%. Because sulfur element as an impurity element would reduce mechanical properties and corrosion resistance performance of steel and normally cannot be removed in a convertor, therefore, in order to reduce the sulfur content in steel, preliminary desulfurization treatment needs to be performed in molten iron. Before performing desulfurization, the blast furnace slag needs to be removed in order t...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
Temperatureaaaaaaaaaa
Temperatureaaaaaaaaaa
Temperatureaaaaaaaaaa
Login to view more

Abstract

The present invention relates to a steel rebar comprising the following ingredients: 0.005%-0.030% of C, 0.3%-0.6% of Si, 1.2%-2.5% of Mn, 0.01% or less of P, 0.01% or less of S, 8.0%-10.0% of Cr, 1.0%-3.0% of Mo, 0.2%-0.4% of Sn, 0.01%-0.05% of Rare Earth element, and the remainder being Fe and unavoidable impurities. The present invention also provides a production method of steel rebar. The steel rebar of the present invention has excellent comprehensive mechanical properties and corrosion resistance performance, while meeting the requirements of anti-knock, the service life in sea water of the steel rebar is increased, thus it can be widely used in reinforced concrete structures in ocean environment.

Description

TECHNICAL FIELD[0001]The present invention relates to a steel rebar and a production method thereof, which pertains to the field of alloy steel.BACKGROUND OF THE INVENTION[0002]Along with consciousness enhancing of ocean strategy of various countries and development of modern ocean science and technology, constructions of infrastructure such as huge cross-river or cross-sea bridges, seaport wharfs, and offshore buildings are entering into a peak season. Meanwhile, the durability problem of steel rebar used as a main structural material becomes increasingly prominent. The ocean environment is a relatively harsh corrosion environment in the nature, with its special conditions of high temperature, high humidity, and high salinity easily causing corrosion of steel. Severe corrosion usually occurs in the reinforced concrete structures along the coast of China after 10-15 years on service, which results in damage to the structures, rendering the structures unable to meet their designed se...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C21D9/52C22C38/28C22C38/24C22C38/22C22C38/04C22C38/02C22C38/00C21D8/06C21C7/064C21C7/06C21C7/068C21C7/10C21C5/28B22D11/00C22C38/38
CPCC21D9/525C21D2211/005C22C38/28C22C38/24C22C38/22C22C38/04C22C38/02C22C38/008C22C38/005C22C38/004C22C38/002C21D8/065C21C7/064C21C7/06C21C7/068C21C7/10C21C5/28B22D11/001C21D2211/002C22C38/38C21D8/08C21C1/02C21C5/30C22C38/18C22C38/60
Inventor ZHANG, JIANCHUNMA, HANHUANG, WENKELI, YANGZUO, LONGFEI
Owner INST OF RES OF IRON & STEEL JIANGSU PROVINCE
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap