Method and device for shortening pidgeon method reduction cycle and extending reduction jug durability

A technology for reducing tanks and tank walls, which is applied in the field of shortening the Pidgeon method reduction cycle and prolonging the service life of reduction tanks and devices, and can solve problems such as the service life of reduction tanks being only 2-3 months, tank wall collapse, and failure. Achieve the effects of shortening the reduction cycle, long service life, and enhancing creep resistance

Inactive Publication Date: 2008-01-23
刘伟杰
View PDF5 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

On the other hand, since the Pidgeon reduction tank works under high temperature and vacuum for a long time, the tank wall will gradually collapse due to high temperature creep, and then fail
At present, the average service life of the reduction tank is only 2-3 months

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Method and device for shortening pidgeon method reduction cycle and extending reduction jug durability
  • Method and device for shortening pidgeon method reduction cycle and extending reduction jug durability
  • Method and device for shortening pidgeon method reduction cycle and extending reduction jug durability

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0016] The invention overcomes the disadvantages of long reduction period and short service life of the traditional Pidgeon method by providing a reduction tank intensifier device for the horizontal reduction tank. However, the present invention does not change the existing technological process and equipment of the Pidgeon method, nor does it increase the difficulty of loading and unloading materials.

[0017] Fig. 1 and Fig. 2 are respectively the transverse and longitudinal sectional views of the reduction tank strengthener (one of the embodiments). The reduction tank strengthener (100) is composed of three reinforcing plates that are radially formed at an angle of 120 degrees to each other and made of heat-resistant good conductor and heat-resistant material. One of the reinforcement plates (101) has an inclined surface, and some slag leakage through holes (103) are prefabricated on the other two reinforcement plates (102). During installation, the inclined-plane reinforc...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention provides a reinforcement device arranged in reaction zone of horizontal Pidgeon Process reduction tank, which has well heat-conducting property to convey rapidly the heat from tank wall to low-temperature zone on tank center and benefit to heat all material quickly and evenly and cut reduction time with Pidgeon Process. It also balances the pressure on tank wall to prolong the creep resistance and service life of the tank. The double-bottom charge chute and a method to unload with predetermined slag through hole make it possible to load and unload material for reduction tank with reinforcement device.

Description

Technical field [0001] The present invention relates to the improvement of the traditional Pidgeon metal extraction process and equipment, more precisely, it shortens the metal reduction period and prolongs the reduction period by providing a method and device that can simultaneously enhance the heat transfer efficiency and creep resistance of the reduction tank The service life of the tank can be extended, thereby effectively improving the production efficiency and economic benefits of the Pidgeon process. [0002] The description of the present invention will take the refining of metal magnesium as an example. But it is also perfectly suitable for refining other volatile metals, such as calcium, strontium, zinc and so on. Background technique [0003] Invented in the 1940s, the Pidgeon metal extraction method (US Patent No. 2330143, Canadian Patent No. 415764, 415765 and 463416) is a method suitable for refining various volatile metals (such as magnesium, calcium, stronti...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C22B26/22
Inventor 刘伟杰
Owner 刘伟杰
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com