Epoxidation silicon oil modified three kinds of composite material of epoxy resin
A technology for epoxidizing silicone oil and epoxy resin, which is applied in the field of epoxidizing silicone oil modified epoxy resin composite materials, can solve the problems of reducing material toughness, reducing mechanical strength and heat resistance, etc., and achieves the effect of high impact strength
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Image
Examples
Example Embodiment
[0024] Example 1
[0025] Take 100g of E-51 epoxy resin with epoxy value of 0.51mol / 100g and 0.1g of epoxidized silicone oil with epoxy value of 0.16mol / 100g in a beaker, stir, and then add p-, p'-diamino two Phenylmethane 25.26g, then heated to dissolve p-,p-diaminodiphenylmethane, stirred, degassed, inverted the mold, and cured according to the curing process of 80℃ / 3h+150℃ / 2h+175℃ / 1h to obtain Epoxidized silicone oil modified epoxy resin composite material, measured tensile strength is 41.31MPa, elongation at break is 5.42%, impact strength is 10.24KJ·m -2 , The glass transition temperature is 158℃.
Example Embodiment
[0026] Example 2
[0027] Take 100g of F-51 epoxy resin with epoxy value of 0.51mol / 100g and 80g of epoxidized silicone oil with epoxy value of 0.01mol / 100g in a beaker, heat and stir, and then add diaminodiphenyl sulfone 29.78 g, then heat to dissolve the diaminodiphenyl sulfone, then stir, degas, reverse the mold, and cure according to the curing process of 80°C / 1h+160°C / 2h+180°C / 2h to obtain an epoxy resin modified epoxy Resin composite material. The measured tensile strength is 43.47MPa, the elongation at break is 6.71%, and the impact strength is 11.62KJ·m -2 , The glass transition temperature is 163℃.
Example Embodiment
[0028] Example 3
[0029]Take 100g of epoxidized silicone oil with an epoxy value of 0.16mol / 100g and dissolve it in dimethylformamide, and place it in the reactor together with 32g of p-diaminodiphenylmethane, while the oil bath is heated and stirred , Then reflux and react at 140°C for 3 hours. After the reaction is completed, the reaction mixture is distilled under reduced pressure to distill off the dimethylformamide to obtain modified epoxidized silicone oil. Take 100g and the epoxy value of 0.44mol / 100g Stir 100g of E-44 epoxy resin in a beaker evenly, then add 5g of dicyandiamide, and cure according to the curing process of 80℃ / 1h+160℃ / 1h+180℃ / 0.5h to obtain epoxidized silicone oil modified epoxy Resin composite material. The measured tensile strength is 47.54MPa, the elongation at break is 11.38%, and the impact strength is 14.45KJ·m -2 , The glass transition temperature is 171℃.
PUM
Property | Measurement | Unit |
---|---|---|
Tensile strength | aaaaa | aaaaa |
Impact strength | aaaaa | aaaaa |
Glass transition temperature | aaaaa | aaaaa |
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap