Propylene polymer composition and use thereof
A technology of polymer and composition, applied in the field of propylene polymer composition, can solve the problems of lack of transparency, high price, application limitation, etc., and achieve a well-balanced and excellent effect
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Examples
Embodiment
[0142] Hereinafter, the present invention will be more specifically described based on examples, but the present invention is not limited by these examples.
[0143] The physical property test conditions and the like are as follows.
[0144] [Dynamic viscoelasticity measurement]
[0145]Using RDS-II manufactured by Rheometric Co., Ltd., under the torsion (torsion) mode between the width of 10 mm and the length of 38 mm, the measurement was performed at -100 ° C to 100 ° C at a temperature increase rate of 2 ° C / min and 10 rad / s, and each was obtained. Loss tangent tanδ and storage elastic modulus G'value at temperature.
[0146] [Stretching test]
[0147] Residual strain:
[0148] A dumbbell plate with a length of 50 mm, a length between the marked lines (L0) of 30 mm, and a shape of a width of 5 mm and a thickness of 1 mmt is applied to a 100% (until the distance between the clamps is 60 mm) strain at a distance of 30 mm between the clamps and a tensile speed of 30 mm / ...
Synthetic example 1
[0165] (Synthesis of Propylene-Ethylene-Butene Copolymer) (ii-1)
[0166] In a 2000ml polymerization apparatus fully replaced by nitrogen, 917ml of dry hexane, 85g of 1-butene, and triisobutylaluminum (1.0mmol) were added at room temperature, and the inner temperature of the polymerization apparatus was raised to 65°C, and The pressure in the system was increased to 0.77 MPa with propylene, and then the pressure in the system was adjusted to 0.78 MPa with ethylene. Next, 0.002 mmol of dimethylmethylene (3-tert-butyl-5-methylcyclopentadienyl) fluorenyl zirconium dichloride and 0.6 mmol of methyl aluminum oxide in terms of aluminum atoms were mixed. The toluene solution contacted with alkanes (manufactured by Tosoh Finechem Corporation) was added to the polymerizer, and polymerization was carried out for 20 minutes while the internal temperature was 65°C and the system pressure was maintained at 0.78 MPa by ethylene, and 20 ml of methanol was added to stop the polymerization rea...
Synthetic example 2
[0168] (Synthesis of Propylene-Ethylene-Butene Copolymer) (ii-2)
[0169] After adding 833ml of dry hexane, 200g of 1-butene, and triisobutylaluminum (1.0mmol) at room temperature to a 2000ml polymerization apparatus fully replaced by nitrogen, the internal temperature of the polymerization apparatus was raised to 40°C, and the Propylene increases the pressure in the system to 0.77MPa, and then uses ethylene to adjust the pressure in the system to 0.8MPa. Next, 0.001 mmol of dimethylmethylene (3-tert-butyl-5-methylcyclopentadienyl) fluorenyl zirconium dichloride and 0.3 mmol of methyl aluminum oxide in terms of aluminum atoms were mixed. The toluene solution contacted with alkanes (manufactured by Tosoh Finechem Corporation) was added into the polymerizer, and the polymerization was carried out for 20 minutes at an internal temperature of 40° C. and the internal pressure of the system was maintained at 0.8 MPa by ethylene, and 20 ml of methanol was added to stop the polymeriza...
PUM
Property | Measurement | Unit |
---|---|---|
melt flow index | aaaaa | aaaaa |
melting point | aaaaa | aaaaa |
enthalpy of fusion | aaaaa | aaaaa |
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap