Method for spray coating alloy on heating surface of flue

A heating surface and flue technology, applied in metal material coating process, coating, fusion spraying, etc., to achieve the effect of improving process conditions, reducing steelmaking labor intensity, and reducing maintenance workload

Active Publication Date: 2009-07-22
MCC CAPITAL ENGINEERING & RESEARCH +1
View PDF4 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0005] The purpose of the present invention is to overcome the problem of a large amount of slag hanging in the production of the converter, and provide a new alloy spraying method for the heating surface of the converter vaporization cooling flue. Alloy spraying is used on the heating surface that is prone to slag formation, such as the fixed section of the mouth, so that the heating surface is not easy to slagging, completely solves the problem of slag formation, and improves the service life of the flue, making it more suitable for practical use and has industrial utilization value

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0032] The specific steps, features and effects of the alloy spraying method for the heating surface of the converter vaporization cooling flue according to the present invention will be described in detail below in conjunction with preferred embodiments.

[0033] The alloy spraying method for the heating surface of the converter vaporization cooling flue proposed by the present invention mainly includes the following steps: A. flue condition inspection, B. sandblasting and derusting, C. sandblasting coarsening, D. spraying the bottom layer, E. spraying Working layer, F. Spraying surface layer, G. Sealing, H. Baking and curing. The compressed air used for spraying should be dry and clean, and the moisture content should be less than 5.8g / m 3 , oil dust particle size ≤ 0.01μm, residual oil ≤ 0.001ppmw / w.

[0034] In a project with a volume of 50m 2 In the embodiment, the operating steps of a construction period are described as follows;

[0035] A. Check the condition of the...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
thicknessaaaaaaaaaa
thicknessaaaaaaaaaa
porosityaaaaaaaaaa
Login to View More

Abstract

This invention relates to a method for spray-coating the heating surface of the flue duct with alloy. The method comprises: (1) examining the flue duct status, and finishing the surface; (2) spraying quartz sand by 0.3 m3 sand blast machine for derusting the surface; (3) spraying metallic grit or brown corundum for coarsening the surface; (4) spray-coating Ni-Al alloy wires to obtain 40-60 mum thick vase layer; (5) spray-coating Ni-Cr-Mo alloy wires at 300-600 m / s to obtain 300-350 mum thick working layer; (6) spray-coating Ni-Cr-Ti alloy wires at arc temperature of 4000-5000 deg.C, environmental temperature of 1600-1700 deg.C and duct wall temperature of 600-700 deg.C to obtain 150-200 mum thick surface layer with binding strength of 30-50 MPa and porosity of 2-3; (7) sealing the pores with conventional sealant; (8) curing the pore-sealing layer at above 300 deg.C for 30 min.

Description

technical field [0001] The invention relates to an alloy spraying method, in particular to an alloy spraying method on the heating surface of a converter vaporization cooling flue. Background technique [0002] In the production of converters in the metallurgical industry, due to the adoption of processes such as slag splashing to protect the furnace, a large amount of slag will hang on the heating surfaces such as the converter vaporization cooling movable hood and the fixed section of the furnace mouth. The slag will reduce the cooling effect of the flue, and the cleaning hangs Slag often damages the water wall, which greatly shortens the life of the flue. The existing converter vaporization cooling flue has no technical measures to prevent slag hanging, so the service life of the heating section such as the movable hood and the fixed section of the furnace mouth is very short, and water leakage usually occurs in about half a year to a year. [0003] Alloy spraying techno...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C23C4/00C23C4/02C23C4/08C23C4/18C23C4/131
Inventor 张学锋朱惠民杨源满吴仕明贾京李玉芬张宏
Owner MCC CAPITAL ENGINEERING & RESEARCH
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com