Powder metallurgy copperized agent and method for producing the same

A technology of powder metallurgy and production method, which is applied in the field of powder metallurgy copper infiltrants and powder metallurgy materials, which can solve the problems of increasing processing costs, affecting product appearance and impact strength, forming corrosion cracks, etc., and achieving the effect of reducing quality costs

Inactive Publication Date: 2008-01-30
包敢锋
View PDF0 Cites 6 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

In this temperature range, the solubility of iron in copper is about 3.8%-4%, which leads to direct copper infiltration with Cu block and powder metallurgy parts. The copper infiltration efficiency is about 85%. Corrosion cracks will be formed on the surface and inside of the parts, affecting The appearance and impact strength of the product, which leads to a high volume (25%-35%) of defective products
Usually machining is used to remove defective products, which increases the processing cost

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0012] The invention relates to a copper infiltrating agent for powder metallurgy, which is prepared by mixing 1.75 kg of Fe powder (-100 mesh), 94.25 kg of Cu powder (-200 mesh) and 4 kg of Mn powder (-325 mesh) to form the base powder of the copper infiltrating agent , mixed with lubricant and molded into copper infiltrating agent block when used.

[0013] The production method is as follows: the prepared materials are mixed in a double-cone mixer at a speed of 19-21r / min for 30-35 minutes.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention relates to a powder metallurgy copperizing agent, which is characterized in that the copperizing agent essentially consists of the mass percentages of materials of: 1.7 percent to 2.1 percent of Fe powder, 3.9 percent to 4.3 percent of Mn powder, 93.6 percent to 94.4 percent of Cu powder. The producing method of the copperizing agent is that: the prepared material is mixed in a double tapered mixer at a rotating speed of 19 to 21r / min for 30 to 35min. the powder metallurgy copperizing agent of the invention does not erode products and affect the strength of products.

Description

technical field [0001] The invention relates to powder metallurgy. In particular, it relates to a copper infiltrating agent for powder metallurgy. It belongs to the technical field of powder metallurgy materials. Background technique [0002] The powder metallurgy copper infiltration process is a process for obtaining high-density and even dense powder metallurgy parts under ordinary pressing pressure (500Mpa-600Mpa). The impact force, sealability, wear resistance and machinability of parts produced by this process are much higher than those of warm pressing, repressing and refiring, so it occupies a considerable share in high-end powder metallurgy products. However, since the copper infiltration of powder metallurgy is carried out in the temperature range of 1090°C-1150°C, 1120°C is usually taken. In this temperature range, the solubility of iron in copper is about 3.8%-4%, which leads to direct copper infiltration with Cu block and powder metallurgy parts. The copper in...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C23C10/28B01F3/18
Inventor 包敢锋龙斌
Owner 包敢锋
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com