Controllable solidifying type technologic clay sculpture material

A clay plastic material and solidification technology, applied in the field of material science, can solve problems such as restricted use, collapse, and deformation of handicrafts

Inactive Publication Date: 2008-06-04
TIANJIN UNIVERSITY OF SCIENCE AND TECHNOLOGY
View PDF0 Cites 4 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, due to the long drying time of traditional clay plastic materials (usually several days or even longer), it is easy to cause deformation and collapse of the molded handicrafts, especially for

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

example 1

[0005] Example 1 Mix 30 parts of PVC paste resin and 100 parts of epoxy resin evenly to form a translucent paste, add 80 parts of talcum powder while stirring, the system is basically putty, and then add light calcium carbonate while kneading 24 parts as the first component. Mix 30 parts of PVC paste resin and 100 parts of epoxy resin evenly to form a translucent paste, add 80 parts of talcum powder while stirring, the system is basically putty, and then add 24 parts of light calcium carbonate while kneading as the first component. Thoroughly stir 35 parts of PVC paste resin and 100 parts of curing agent (651#), and evenly mix to form a translucent paste. While stirring, add 50 parts of talcum powder and 70 parts of light calcium carbonate as the second component. The above two components are respectively sealed and packaged for storage at room temperature (-10°C-40°C), and the validity period is 60 days. When using, the first component and the second component are mixed uni...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention relates to a controllable and cured type technique clay sculpture material, which adopts epoxy resin, PVC paste resin, talc powder and light calcium carbonate as raw materials. The raw materials are mixed evenly and then stirred into putty shape composition 1; curing agent, the PVC paste resin and the talc powder are mixed evenly and stirred into semi-transparent paste, in which the light calcium carbonate is added, thus obtaining composition 2. The two compositions are mixed evenly in accordance with a certain ratio, thus obtaining the controllable and cured type technique clay sculpture material. The invention is characterized in that: the invention not only has the plasticity (being moulded into different shapes randomly) of the traditional technique clay sculpture material (clay), but also has long storing time; besides, the cured time can be controlled (a plurality of hours or a plurality of days) under low temperature (below 0 DEG C); the invention is characterized by constructability, innocuity, adjustable hardness of products and extremely high impact resistance (being uneasy to be broken), etc. The invention is the technique clay sculpture material with excellent comprehensive property.

Description

technical field [0001] The invention relates to a controllable solidification type craft clay plastic material, which belongs to the field of material science. Background technique [0002] There are many kinds of clay sculpture artworks and a long history. It is a popular art form of our people and has strong local characteristics of China. Traditional clay plastic materials use soil as raw material, add additives, and adjust viscosity with water, which has the characteristics of low cost. However, due to the long drying time of traditional clay sculpture materials (usually several days or even longer), it is easy to cause deformation and collapse of the molded handicrafts, especially for large clay sculpture products. Moreover, traditional clay plastic materials use water as the medium and cannot be operated under low temperature conditions (freezing below 0°C), thus limiting their use. [0003] Synthetic materials have the advantages of high strength, strong aging resis...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C08L63/00C08K3/36B44B11/00C08L27/06C08K3/26
Inventor 卢秀萍
Owner TIANJIN UNIVERSITY OF SCIENCE AND TECHNOLOGY
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap