Powdered frit decorative porcelain
A technology for colored porcelain and glaze powder, applied in the field of glaze pastel colored porcelain, can solve the problems of small selection range of pigments, narrow color tone range, problems in craftsmanship and cost, etc.
Inactive Publication Date: 2008-08-20
缪明辉
View PDF0 Cites 6 Cited by
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
In order to reduce the dissolution of lead and cadmium, people try to use underglaze color and glaze color to replace overglaze pastel, but because the firing temperature is as high as 1300 ℃ and 1200 ℃ respectively, the range of pigment selection is small, and the range of hue is too narrow. It is inferior to overglaze colors in terms of hue and type, and has problems in terms of manufacturability and cost, making it difficult to be accepted by the market. Therefore, overglaze colors with relatively low firing temperatures are still the main decoration method for daily-use porcelain.
Method used
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View moreExamples
Experimental program
Comparison scheme
Effect test
Embodiment 1
[0017] Put 10% of chromium oxide into the glaze pigment A by total weight, after decoration and firing, the product is green.
Embodiment 2
[0019] Put 10% of chromium oxide into the glaze pigment B by total weight, after decoration and firing, the product is yellow-green.
Embodiment 3
[0021] The cobalt oxide is put into the glaze pigment A with 10% of the total weight, and after decoration and firing, the product is blue-purple.
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More PUM
Login to View More
Abstract
The invention relates to a glaze famille-rose porcelain which adopts glaze pigment without lead and coloring oxide according to weight portion ratio of 9:1, and water color pigment and oil color pigment which are made by fine grinding the glaze pigment without lead and the coloring oxide in a mill is used for the porcelain glaze decoration, and the product is manufactured by firing under the temperature of 780 DEG C to 850 DEG C. The glaze famille-rose porcelain which replaces a lead flux of the traditional glaze coloring with the glaze and reduces all poisonous substances is characterized in that the glaze famille-rose porcelain is environment-friendly and safe in use and colorful in hue. The glaze famille-rose porcelain is suitable for various glaze decoration of transparent ancient color, grease paint, and mixed glaze, etc., on art porcelains, furnishing porcelains and domestic porcelains..
Description
technical field [0001] The invention belongs to the technical field of porcelain surface decoration, and relates to glaze pastel porcelain, which is suitable for various types of overglaze decorations such as transparent ancient paint, oil paint and pastel paint on artistic porcelain, display porcelain and daily-use porcelain. Background technique [0002] Pastel porcelain, also known as soft-color porcelain, was created in the late Kangxi period of the Qing Dynasty. It is a kind of glaze color and is one of the four famous porcelains in China. The traditional craft is to draw a pattern on the glaze of white porcelain first, then fill in a layer of "glass white" (a painting material containing lead, silicon, and arsenic, which mainly acts as a flux), and then paint with color material. It is baked in a color oven. Because the overglaze decorative color material of traditional famille rose porcelain uses lead-containing compounds as fluxes, excessive amoun...
Claims
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More Application Information
Patent Timeline
Login to View More
IPC IPC(8): C04B41/86
Inventor 缪明辉
Owner 缪明辉
Who we serve
- R&D Engineer
- R&D Manager
- IP Professional
Why Patsnap Eureka
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com