Adhesive resin composition and multilayer body
A bonding resin and bonding resin technology, applied in the direction of synthetic resin layered products, fabrics, adhesives, etc., can solve the problems of difficult operation, unstable thermal history of tackifiers, and pollution of the working environment of molding machines, etc., to achieve Excellent film-forming properties and good appearance
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Examples
Embodiment 1~8、 comparative example 1~9
[0202]
[0203] The resin component (A), the resin component (B) and the resin component (C) of the type and amount shown in Table 3 were mixed so that their total amount was 100% by weight, and then 0.2% by weight was added to 100% by weight of the total amount Parts of phenolic antioxidant (Ciba Specialty Chemicals Inc. production, IRGANOX1010), 0.1 parts by weight of phosphorus antioxidant (Ciba Specialty Chemicals Inc. production, Irgafos 168), 0.03 parts by weight of neutralizer (Kyowa Chemical Co., Ltd. production, ALCAMIZER DHT-4A), mixed with a high-speed mixer for 1 minute, and melted at a screw speed of 100 rpm and an extrusion rate of 10 kg / hour using a twin-screw extruder "PCM30φ" (set temperature 210°C) manufactured by Ikegai Co., Ltd. Kneading, extruding into strands, cutting into pellets after cooling, to obtain an adhesive resin composition.
[0204]
[0205] Using a 3-resin 3-layer T-die molding machine manufactured by PLACO Co., Ltd., 3-layer co-extrusion...
Embodiment 9
[0228] [Example 9, Comparative Examples 10 and 11]
[0229]
[0230] Except having set it as the resin composition shown in Table 4, it carried out similarly to Examples 1-8 and Comparative Examples 1-9, and obtained the adhesive resin composition.
[0231]
[0232] A three-layer laminated film was formed in the same manner as in Examples 1 to 8 and Comparative Examples 1 to 9 except that the film constitution and die temperature shown in III and IV below were set.
[0233] In addition, "NOVATEC SF8402" produced by Nippon Polychem Co., Ltd. was used as polyethylene resin (PE), "NOVATEC FY4" produced by Nippon Polychem Co., Ltd. was used as polypropylene resin (PP), and Mitsubishi Co., Ltd. was used as polyester resin (PET). For "PA500D" produced by Rayon, the adhesive resin composition shown in Table 4 was used for the adhesive resin layer.
[0234] Film III: PE / adhesive resin layer / PET=4 / 1 / 3 (thickness ratio)
[0235] Total thickness = 80μm
[0236] (Adhesive resin lay...
Embodiment 10~27、 comparative example 12~30
[0250]
[0251] Except having set it as the resin composition shown in Tables 5-7, it carried out similarly to Examples 1-8 and Comparative Examples 1-9, and obtained the adhesive resin composition.
[0252]
[0253] A three-layer laminated film was formed in the same manner as in Examples 1 to 8 and Comparative Examples 1 to 9 except that the film constitution and die temperature shown in V and VI below were set.
[0254] In addition, as the non-crystalline polyethylene terephthalate resin (PET), "6763" manufactured by Eastman Chemicals (Vicat softening temperature (ASTM D1525) is 82°C, glass transition temperature (Tg) is 81°C ), as the homopolypropylene (PP), "NOVATEC PPFY4" (MFR (230°C): 5 g / 10 min, density: 0.90 g / cm 3 ), as the linear polyethylene (PE), "NOVATEC LLDSF8402" (MFR (190°C): 3g / 10min, density: 0.93g / cm2) produced by Nippon Polyethylene Co., Ltd. was used 3 ), and the adhesive resin composition shown in Tables 5-7 was used for the adhesive resin layer.
...
PUM
Property | Measurement | Unit |
---|---|---|
thickness | aaaaa | aaaaa |
thickness | aaaaa | aaaaa |
Vicat softening point | aaaaa | aaaaa |
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap