Moisture-curable leather polishing coating agent

A moisture-curing and finishing agent technology, which is applied in leather surface treatment, small raw hide/big raw hide/leather/fur treatment, small raw hide/large raw hide/leather skin/fur chemical treatment, etc. It can solve the problem that the gloss is not good enough , poor low-temperature bending resistance, low overall performance, etc., to achieve good visual effects, strong crystal feeling, and good low-temperature bending resistance

Active Publication Date: 2011-09-28
JIANGSU BAOZE POLYMER MATERIAL
View PDF0 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] With the wide application of leather materials, the performance requirements for surface finishing agents such as gloss and weather resistance (low temperature bending resistance) are also increasing. However, the currently developed moisture-curing leather finishing agents are not good enough in terms of gloss. And low temperature bending resistance is relatively poor, the overall performance is not high

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Moisture-curable leather polishing coating agent

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0017] A moisture-curing leather bright finish agent, each raw material component is weighed according to the following weight ratio: toluene diisocyanate 17.5%, diphenylmethane diisocyanate 4%, polyether polyol (molecular weight is 1000) 32% , Ternary lower alcohol 3.5%, butyl acetate 19.5%, xylene 23%, antioxidant 0.2%, stabilizer 0.1%, leveling agent 0.2%.

[0018] The production technology of this moisture curing type leather bright finishing agent, concrete steps are as follows:

[0019] ①: Put toluene diisocyanate, diphenylmethane diisocyanate, polyether polyol, ternary lower alcohol, antioxidant and half of the solvent (mixture of butyl acetate and xylene) into the reaction kettle and heat it to about 80°C. Stir for about 12 hours until the end of the reaction is detected;

[0020] ②: Add the remaining half of butyl acetate and xylene to the reaction kettle and stir for half an hour;

[0021] ③: Add stabilizer and leveling agent to the cooled reaction kettle and stir ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention relates to a moisture solidification type leather brightening finishing agent with high brightness and weathering resistance, comprising polyurethane prepolymer, wherein the polyurethane prepolymer is prepared by reacting diisocyanate, polyatomic alcohol with initiator in the presence of organic solvent; the polyurethane prepolymer includes dissociative isocyan acid radical, the polyatomic alcohol is the mixture of one or two of the group consisting of polyester polyatomic alcohol, polyether glycol. Compared with prior art, the invention not only has the better performance to resist twist at low temperature, but also can realize high brightness and strong crystal sense after finishing the invention on the leather, so the invention has greater visual effect.

Description

technical field [0001] The invention relates to a leather finishing agent, in particular to a room-temperature moisture-curable leather finishing agent, in particular to a room-temperature moisture-curable leather finishing agent with high gloss and excellent bending resistance. Background technique [0002] At present, bright finishing agent products in the synthetic leather market are becoming a popular trend in the future, and are widely used in luggage, clothing, and footwear products. [0003] After the general leather surface finishing agent is painted on the leather, it needs to be dried and then processed. However, the moisture-curing leather surface finishing agent is different. It is mainly composed of polyurethane prepolymer. After the leather is coated with this material, it does not need to be dried. It can be placed directly in the air (or appropriately increase the air humidity and temperature), the dry time is 2 to 4 hours, and it takes 8 to 12 hours to matur...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C14C11/00C08G18/10C08G18/48C08G18/76
Inventor 时云刚
Owner JIANGSU BAOZE POLYMER MATERIAL
Features
  • R&D
  • Intellectual Property
  • Life Sciences
  • Materials
  • Tech Scout
Why Patsnap Eureka
  • Unparalleled Data Quality
  • Higher Quality Content
  • 60% Fewer Hallucinations
Social media
Patsnap Eureka Blog
Learn More

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2025 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com