Method for rolling and shaping stainless steel special-shaped ring forging

A special-shaped ring and stainless steel technology, applied in the direction of metal rolling, etc., can solve problems such as unfavorable equipment maintenance, inaccurate selection of deformation, folding, etc., to facilitate maintenance of equipment, reduce machining allowance, and reduce manufacturing costs. cost effect

Inactive Publication Date: 2008-10-08
GUIZHOU ANDA AVIATION FORGING
View PDF1 Cites 66 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

When using this process to roll special-shaped rings of different shapes, the roll type needs to be replaced again, and frequent change of roll type will increase manufacturing costs, prolong the production cycle, and is not conducive to equipment maintenance
[0004] The above-mentioned ring forming method does not disclose the specific process steps of rolling stainless steel special-shaped ring forgings. When rolling stainless steel special-s

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Method for rolling and shaping stainless steel special-shaped ring forging
  • Method for rolling and shaping stainless steel special-shaped ring forging
  • Method for rolling and shaping stainless steel special-shaped ring forging

Examples

Experimental program
Comparison scheme
Effect test

specific Embodiment approach

[0029] The content of the main chemical elements (percentage by weight) of the alloy is: 0.06% to 0.11% of C, 9.80% to 11.20% of Cr, 5.0% to 7.0% of Co, 0.10% to 0.70% of Si, 0.10% to 0.70% of Si, Mo content 0.50%~1.0%, Mn content 0.60%~1.15%, Nb content 0.05%~0.15%, V content 0.10%~0.35%, Ni content 0.20%~0.80%, N content 0.010%~ 0.035%, B content 0.004% ~ 0.012%, P content ≤ 0.028%, S content ≤ 0.02%, the balance is Fe.

[0030] The process steps of the alloy from the bar to the production of qualified special-shaped ring forgings are as follows:

[0031] Step 1: Billet making of a rectangular pre-rolled billet. Such as figure 1 As shown, the 10Cr-6Co-0.8Mo alloy bar 1 blanked according to the specification is heated to the deformation temperature of 1130 ° C ~ 1150 ° C in the forging heating furnace, and it is upset on the forging press to deform 50% ~ 55% to obtain a solid Round cake 2, then the solid round cake 2 is punched out of the central hole with a punch 4 to obt...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses a rolling and shaping method for a stainless steel heterotypic ring forging in order to obtain the alloy heterotypic ring forgings with excellent tissues and properties as well as realize accurate rolling. The method includes the following steps: alloy bar material is heated, carried out continuous upsetting and deformed by 50 to 55 percent, so as to be made into a solid cake and then is punched again to lead the alloy bar material to be made into a hollow round cake after the aperture dimension of the alloy bar material is 30 to 35 percent of the dimension of the outer diameter thereof; a rectangle pre-rolling blank is obtained after the hollow round cake is heated, rolled circularly and deformed by 40 to 45 percent; the pre-rolling blank is heated and arranged in a rolling die of a ring rolling machine and forms a heterotypic ring forging after being rolled and deformed by 50 to 55 percent in a section groove. When in expansion, the broadening speed of the pre-rolling blank along the radial direction is 2mm/s to 15mm/s with radial rolling force of 20000kg to 120000kg. The method is mainly used for the shaping of the heterotypic ring forging of an aeroengine. The method can be adopted to obtain the heterotypic ring forging that is arranged in a flow line along the outline of a part.

Description

technical field [0001] The invention relates to a rolling forming method of a ring forging, in particular to a rolling forming method of a stainless steel special-shaped ring forging. Background technique [0002] Aeroengine special-shaped ring forgings made of stainless steel (such as British 10Cr-6Co-0.8Mo and other material grades), such as casings and other parts, are required to have good performance and structural stability due to long-term work in harsh environments. [0003] The Chinese invention patent specification CN 1586754A published on March 2, 2005 discloses a method for rolling and forming a ring with an outer step section. The longitudinal section of the ring is a non-rectangular outer step shape, that is, the ring The piece belongs to a special shape of the special-shaped ring forging. The method includes blanking, billet making, rolling and subsequent processing. The special-shaped rings rolled by this method are realized by the pass directly formed by th...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): B21H1/06B21J1/04
Inventor 杨勇何冰荣继祥王超李志瑶陈新元邹伟周红何涛刘志棋崔一平
Owner GUIZHOU ANDA AVIATION FORGING
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap