Fast-drying solvent type epoxy resin intermediate paint

An epoxy resin and solvent-based technology, applied in the field of fast-drying solvent-based epoxy resin intermediate paint, can solve the problems of slow drying performance, inability to adapt to flowing water coating, poor bonding force between primer and topcoat, etc., and achieve anti-corrosion Good performance, excellent wetting performance, and the effect of improving film-forming performance

Inactive Publication Date: 2009-03-18
中涂化工(上海)有限公司
View PDF0 Cites 15 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

For thicker exterior paints, especially polyurethane topcoats, quick-drying solvent-based epoxy resin intermediate paints are very necessary. However, the current i

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0026] A kind of fast-drying solvent-type epoxy resin intermediate paint, the formula (weight percentage) of this intermediate paint is as follows:

[0027] main agent

[0028] Bisphenol A type epoxy resin 20

[0029] Titanium dioxide (rutile type) 3

[0030] Iron Oxide Red 1

[0031] barite powder 11

[0032] Talc powder 25

[0033] Polyethylene wax 4

[0034] Organic bentonite 1

[0035] Xylene 10

[0036] Toluene 25

[0037] Hardener

[0038] Polyamide resin 60

[0039] 2,4,6-tris(dimethylaminomethyl)phenol 3

[0040] Xylene 37

[0041] Main agent: curing agent = 4:1 (weight)

Embodiment 2

[0043] A kind of fast-drying solvent-type epoxy resin intermediate paint, the formula (weight percentage) of this intermediate paint is as follows:

[0044] main agent

[0045] Bisphenol A epoxy resin 15

[0046] Titanium Blue 15

[0047] Titanium Green 15

[0048] Precipitated Barium Sulfate 15

[0049] Calcium carbonate 15

[0050] Hydrogenated castor oil 1

[0051] Stearic acid treated montmorillonite 1

[0052] Organosilane (Tetramethylsilane) 1

[0053] Isopropanol 10

[0054] Butanol 12

[0055] Hardener

[0056] Polyamide resin (polyamide-1010) 40

[0057] Benzyldimethylamine 1

[0058] Isobutanol 30

[0059]Methyl ethyl ketone 29

[0060] Main agent: curing agent = 20:1 (weight)

Embodiment 3

[0062] A kind of quick-drying solvent type epoxy resin middle layer paint, the formula (weight percent) of this middle layer paint is as follows:

[0063] main agent

[0064] Bisphenol A epoxy resin 25

[0065] Organic Permanent Red 20

[0066] Organic Purple 15

[0067] Quartz Powder 15

[0068] Hydrogenated Castor Oil 2

[0069] Fatty acid amide (stearic acid amide) 2

[0070] Unsaturated fatty acid amide (oleic acid amide) 2

[0071] Methyl acetate 10

[0072] Ethyl acetate 9

[0073] Hardener

[0074] Polyamide resin (polyamide-46) 50

[0075] Benzyldimethylamine 2

[0076] Methyl acetate 25

[0077] Ethyl acetate 23

[0078] Main agent: curing agent = 10:1 (weight)

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention relates to fast-dry solvent type intermediate epoxy resin paint, which comprises a main agent and a curing agent, wherein the ratio of the main agent to the curing agent is between 20 to 1 and 5 (weight). Compared with the prior art, the intermediate epoxy resin paint has good drying property as well as simple and convenient coating operation, adapts to flow coating of the prior containers, can be thickly coated to the specified film thickness at one time, has good anticorrosion property, and has good binding force with a last-pass primer and a next-pass primer; and for thicker outer finish, particularly polyurethane finish, the intermediate epoxy resin paint has good usability, can not froth, and has good anticorrosion property.

Description

technical field [0001] The invention relates to a non-aqueous medium epoxy resin intermediate paint suitable for container exterior coating, in particular to a fast-drying solvent-type epoxy resin intermediate paint. Background technique [0002] At present, the container manufacturing industry is mainly concentrated in China. China has brought together more than 80% of the global container manufacturing activities. As the world's coating industry is accelerating its transfer, my country, as one of the world's largest coating production countries, has taken the lead in the development of the container industry. The field of container coatings has achieved a leading position. Since 1994, China's container export volume has ranked first in the world. So far, China's container industry has dominated the world for eight consecutive years, with an average growth rate of 25%. The container is an international means of transportation between the inland and the sea. Therefore, the c...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C09D163/00C09D7/12
Inventor 沈澜
Owner 中涂化工(上海)有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap