Mud suction and drainage hose and preparation method thereof

A technology of mud glue and film, applied in the direction of hoses, pipes, mechanical equipment, etc., can solve the problems of easy corrosion, large corrosion of mud discharge and suction pipes, and increased cost, so as to improve the resistance to medium corrosion, improve corrosion resistance, and Good performance at low temperature

Active Publication Date: 2009-06-03
河北宇通特种胶管有限公司
View PDF0 Cites 19 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0002] In dredging projects such as harbors, rivers, and lakes, most dredgers pump out the sediment, and the discharge and suction pipes used with dredgers are more and more widely used. Most of the current discharge and suction pipes are made of metal steel pipes, cement Pipes, etc., due to the nature of their materials, the row of mud suction pipes has shortcomings such as not easy to bend, easy to corrode, and not wear-resistant. In this way, not only the construction is inconvenient, but also its service life is short, and the cost is greatly increased.
And it is applied to the sewage pipe, because the sewage is alkaline or acidic, the corrosion of the suction pipe will be greater

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Mud suction and drainage hose and preparation method thereof
  • Mud suction and drainage hose and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0071] The first step is to prepare raw materials and make inner rubber compound and outer rubber compound

[0072] Take 75 kg of natural rubber, 25 kg of styrene-butadiene rubber, 4 kg of zinc oxide, 3 kg of stearic acid, 80 kg of carbon black, 2 kg of sulfur, 1.0 kg of accelerator CZ, 20 kg of pine tar, 30 kg of light calcium, and 1.0 kg of paraffin kg, 2.0 kg of anti-aging agent A, 10 kg of Coumarone, crushed and mixed, and mixed with various raw materials through an internal mixer to make inner rubber compound;

[0073] Take 60 kg of natural rubber, 40 kg of styrene-butadiene rubber, 5 kg of zinc oxide, 4 kg of stearic acid, 60 kg of carbon black, 1 kg of sulfur, 2.0 kg of accelerator DM, 18 kg of pine tar, 80 kg of light calcium, and 1.5 kg of paraffin kg, 2.0 kg of anti-aging agent A, crushed and mixed, and mixed with various raw materials through an internal mixer to make the outer rubber compound;

[0074] The second step of heating:

[0075] Put the inner rubber com...

Embodiment 2

[0089] The first step is to prepare raw materials and make inner rubber compound and outer rubber compound

[0090] Take 75 kg of natural rubber, 25 kg of styrene-butadiene rubber, 5 kg of zinc oxide, 3 kg of stearic acid, 65 kg of carbon black, 2 kg of sulfur, 1.0 kg of accelerator CZ, 12 kg of pine tar, 15 kg of light calcium, paraffin wax 1 kg, 1.0 kg of anti-aging agent A, 5 kg of Coumarone, crushed and mixed, and mixed with various raw materials through an internal mixer to make inner rubber compound;

[0091] Take 60 kg of natural rubber, 40 kg of styrene-butadiene rubber, 8 kg of zinc oxide, 4 kg of stearic acid, 40 kg of carbon black, 1.5 kg of sulfur, 1.5 kg of accelerator DM, 20 kg of pine tar, 85 kg of light calcium, paraffin wax 1.5 kg, anti-aging agent A 2.0 kg, crushed and mixed, and mixed with various raw materials through an internal mixer to make the external rubber compound;

[0092] Step 5: Preparation of the reinforcement layer

[0093] After the cord is ...

Embodiment 3

[0098] The first step is to prepare raw materials and make inner rubber compound and outer rubber compound

[0099] Take 75 kg of natural rubber, 25 kg of styrene-butadiene rubber, 6 kg of zinc oxide, 3 kg of stearic acid, 50 kg of carbon black, 2 kg of sulfur, 1.0 kg of accelerator CZ, 10 kg of pine tar, 15 kg of light calcium, and 2 kg of paraffin kg, 1.0 kg of anti-aging agent A, 5 kg of coumarone, crushed and mixed, and mixed with various raw materials through an internal mixer to make inner rubber compound rubber;

[0100] Take 60 kg of natural rubber, 40 kg of styrene-butadiene rubber, 8 kg of zinc oxide, 5 kg of stearic acid, 40 kg of carbon black, 2 kg of sulfur, 1 kg of accelerator DM, 10 kg of pine tar, 60 kg of light calcium, and 1.0 kg of paraffin kg, 1.5 kg of anti-aging agent A, crushed and mixed, and mixed with various raw materials through an internal mixer to make the outer rubber compound;

[0101] Step 5: Preparation of the reinforcement layer

[0102] Aft...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention belongs to the technical field of hoses and manufacturing method thereof and discloses a mud suction and drainage hose and the preparation method thereof. The hose is mainly characterized in that the hose comprises an internal glue layer, an external glue layer and flanges at both ends; an enhancement layer is installed between the internal glue layer and the external glue layer; the internal glue layer comprises the following materials according to parts by weight: 75 parts of natural rubber, 25 parts of styrene-butadiene rubber, 4-8 parts of zinc oxide, 3-5 parts of stearic acid, 50-80 parts of carbon soot, 1-2 parts of sulfur, 0.5-2.0 parts of accelerant CZ,10-20 parts of pine tar, 15-30 parts of fine particle calcium carbonate, 1.0-2.0 parts of paraffin, 1.0-2.0 parts of age inhibitor A and 5-10 parts of coumarone, the external glue layer comprises the following materials according to parts by weight: 60 parts of natural rubber, 40 parts of styrene-butadiene rubber, 5-10 parts of zinc oxide, 3-5 parts of stearic acid, 40-60 parts of carbon soot, 1-2 parts of sulfur,1.0-2.0 parts of accelerant DM, 10-20 parts of pine tar, 60-90 parts of fine particle calcium carbonate,1.0-2.0 parts of paraffin and1.5-2.5 parts of age inhibitor A. Cord fabric is used and spirally intertwined between the internal glue layer and the external glue layer according to a degree ranging from 52 degrees to 57 degrees. Pressive strength and aging resistant performance are improved.

Description

technical field [0001] The invention belongs to the technical field of rubber hoses and manufacturing methods, and in particular relates to a mud suction hose and a preparation method thereof. Background technique [0002] In dredging projects such as harbors, rivers, and lakes, most dredgers pump out the sediment, and the discharge and suction pipes used with dredgers are more and more widely used. Most of the current discharge and suction pipes are made of metal steel pipes, cement Pipe etc., because the nature of its material has determined that this row of suction pipes has shortcomings such as not easy to bend, easy to corrode, not wear-resisting, like this, not only construction is inconvenient, and its service life is short, and cost increases greatly. However, if it is applied to the sewage pipe, the corrosion of the suction pipe will be greater because the sewage is alkaline or acidic. Contents of the invention [0003] The first technical problem to be solved by...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): F16L11/08C08L7/00C08K13/02C08L9/06
Inventor 赵聪郝伟
Owner 河北宇通特种胶管有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com