Novel aluminum alloy and heat tinting process for the aluminum alloy product

A new type of aluminum alloy technology, applied in the field of aluminum alloy products, can solve the problems of single appearance color, inability to oxidize die-cast aluminum alloy profiles, difficult coloring, etc., achieve the effect of full coating and enhanced performance

Active Publication Date: 2009-07-29
东莞市东兴铝业有限公司
View PDF1 Cites 42 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] The purpose of the present invention is to solve the shortcomings of die-casting aluminum alloy profiles such as inability to oxidize, difficult coloring, single appearance color, etc., to provide a new type of aluminum alloy suitable for die-casting and capable of obtaining oxidation protection, and to provide a Oxidation coloring process of aluminum alloy products

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0028] Take 80 parts by weight of ADC12 and 20 parts by weight of Al6061, according to the conventional aluminum alloy manufacturing process, put them into the furnace to melt into a liquid state, then put the mixed liquid into the mold for die-casting, take out the profile after die-casting, remove the nozzle, and carry out the process on the profile Post-processing, including conventional processing methods such as peak removal, polishing, grinding and other processing, for future use.

[0029] Perform the following process operations on the processed profiles in turn:

[0030] A. Hanging of the profile, that is, hanging the aluminum alloy profile on a hanger; the hanger can be bent by using a general iron wire. The hanging profile must maintain a certain inclination (> 5°) to facilitate exhaust during electrophoresis or coloring, and reduce spots (bubbles). Points are generated on the decorative surface. Before assembling, place an aluminum sheet between the profile and t...

Embodiment 2

[0041] Take 50 parts by weight of ADC12 and 50 parts by weight of Al6063, according to the conventional aluminum alloy manufacturing process, put them together into a furnace to melt into a liquid state, then put the mixed liquid into the mold for die-casting, take out the profile after die-casting, remove the nozzle, and perform Post-processing, including conventional processing methods such as peak removal, polishing, grinding and other processing, for future use.

[0042] Perform the following process operations on the processed profiles in turn:

[0043] A. Hanging of the profile, that is, hanging the aluminum alloy profile on a hanger; the hanger can be bent by using a general iron wire. The hanging profile must maintain a certain inclination (> 5°) to facilitate exhaust during electrophoresis or coloring, and reduce spots (bubbles). Points are generated on the decorative surface. Before assembling, place an aluminum sheet between the profile and the aluminum screw to p...

Embodiment 3

[0054] Take 45 parts by weight of ADC12 and 55 parts by weight of Al6062, according to the conventional aluminum alloy manufacturing process, put them together into a furnace to melt into a liquid state, then put the mixed liquid into the mold for die-casting, take out the profile after die-casting, remove the nozzle, and perform Post-processing, including conventional processing methods such as peak removal, polishing, grinding and other processing, for future use.

[0055] Perform the following process operations on the processed profiles in turn:

[0056] A. Hanging of the profile, that is, hanging the aluminum alloy profile on a hanger; the hanger can be bent by using a general iron wire. The hanging profile must maintain a certain inclination (> 5°) to facilitate exhaust during electrophoresis or coloring, and reduce spots (bubbles). Points are generated on the decorative surface. Before assembling, place an aluminum sheet between the profile and the aluminum screw to p...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention relates to the technical field of aluminum alloy products, in particular to an aluminum alloy suitable for extrusion process and capable of obtaining the oxidizing protection and an oxidizing colored process thereof. The aluminum alloy suitable for extrusion process and capable of obtaining the oxidizing protection contains ADC12 and 6# aluminum, wherein the mass percentage of the ADC12 is 20% to 80%, mass percentage of the 6# aluminum is 80%-20%. The invention combines performance complement between the ADC12 and the 6# aluminum to obtain oxidation protection without changing the physical properties of die-casting aluminum alloy ADC12 and greatly enhance the use performance of the aluminum alloy, and leads the whole interior and exterior profiles to be colorful by adding pigments in the novel aluminum alloy so that hue of the profiles is no longer dull by different colors, so as to meet the requirement of consumers. The oxidizing colored process of the aluminum alloy products has the advantages of plumpy, uniform, level and smooth coatings and obviously better rigidity, adhesive force, erosion resistance, impact property and permeability than other coating techniques.

Description

Technical field: [0001] The invention relates to the technical field of aluminum alloy products, in particular to an aluminum alloy suitable for a die-casting process and capable of obtaining oxidation protection and an oxidation coloring process for the aluminum alloy product. Background technique: [0002] Aluminum alloy materials are widely used due to their good properties. According to the content and type of alloying elements in the aluminum alloy, the corresponding properties of various aluminum alloys are also very different. Among them, commonly used Al-Si-Cu-Mn series die-casting aluminum alloys such as No. 12 aluminum (ADC12) have good die-casting properties and are suitable for manufacturing die-casting profiles through die-casting processes. The profile made of ADC12 has good mechanical properties, but because ADC12 is difficult to be oxidized, the profile made of ADC12 cannot obtain an oxidation protection layer, which affects its service life, and it is also ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C22C21/00C25D11/04C25D11/16C25D11/06C25D13/00
Inventor 何旭坤
Owner 东莞市东兴铝业有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap