Flaot method for on-line coating self-cleaning coated glass

A technology for coated glass and float glass, which is applied to the field of on-line production of sprayed self-cleaning coated glass by float method, can solve the problems of architectural glass cleaning, environmental pollution, danger of cleaning personnel, complicated production process, etc., and achieves simple structure and energy saving. , safe and reliable operation

Active Publication Date: 2011-07-20
杭州蓝星新材料技术有限公司 +2
View PDF2 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The wide application of glass has also brought about the problem of how to keep the glass surface clean. The usual practice is to ask a cleaning company to clean the facade of the building on a regular basis. Great danger, on the other hand, use a large amount of cleaning agents to clean the glass surface, these cleaning agents are directly discharged into urban rivers through urban rainwater pipes without treatment, causing environmental pollution
[0003] In order to solve the above-mentioned problems of building glass cleaning and environmental pollution, self-cleaning coated glass has been produced at home and abroad, such as CN1312337 describes the preparation of TiO by sol-gel method 2 Self-cleaning coated glass, CN1267644 describes preparing TiO with magnetron sputtering 2 Self-cleaning coated glass, the production methods of the above patents either need to be implemented at high temperature, or implemented by physical methods, the production process is complicated, the cost is high, and the production efficiency is low

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0013] The method of the present invention is further described below with examples.

[0014] On a 450t / d float glass production line, the width of the glass plate is 3300mm, the thickness of the glass plate is 5mm, the speed of the glass plate is 450m / h, the temperature of the glass plate surface at the exit position of the annealing furnace is 80°C; the height of the spray gun from the glass plate surface is 300mm, and the spray angle is 80 °, two spray guns, the fog width is superimposed by 20%, and the spray guns move back and forth in the width direction of the glass plate at a speed of 1.1m / s. The spray liquid contains nano-titanium dioxide with a mass concentration of 1.2%, and the rest is methanol. Spray two Second, the thickness of the film layer is about 60nm after curing for 20min. The transmittance of this product is about 1% lower than that of the original glass. According to the building materials industry standard "Measurement Method for Photolysis Efficiency of...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
thicknessaaaaaaaaaa
particle diameteraaaaaaaaaa
thicknessaaaaaaaaaa
Login to view more

Abstract

The invention relates to a method of flat on-line coating self-cleaning coated glass. In the method, the lehr outlet of float glass production line is equipped with spraying equipment with a liquid storage pot and a spray gun, the spraying liquid filled in the liquid storage pot contains nano-titanium dioxide with the mass concentration of 0.1% to 3%, and the remainders are alcohols; the distancebetween the nozzle of the spray gun and the glass face is 200 to 350 mm; the traveling speed of the spray gun is 0.8 to 1.2 m / min; the spraying liquid is sprayed on the float glass surface at the temperature of 60 to 120 DEG C; the film curing lasts 10 to 120 minutes; the self-cleaning coated glass produced by using the method has the advantages of simple, stable and reliable technology, uniform film, low cost, high efficiency, and the like, and is applied to continuous production in large scale.

Description

technical field [0001] The invention relates to a method for on-line production of float glass by spraying self-cleaning coating. Specifically, a layer of nano-titanium dioxide coating is sprayed on the glass surface at the exit of an annealing kiln in a float glass production line by using the cold-end automatic spraying technology. Background technique [0002] With the improvement of living standards and aesthetic concepts, in the construction of modern cities, glass is used more and more in buildings. The entire facade of many modern high-rise buildings is decorated with glass. Due to the permeability and strong reflective effect of glass, the glass must maintain a clean surface in order to show the beauty of the building. The wide application of glass has also brought about the problem of how to keep the glass surface clean. The usual practice is to ask a cleaning company to clean the facade of the building on a regular basis. Great danger, on the other hand, uses a la...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Patents(China)
IPC IPC(8): C03C17/23C03B18/00
Inventor 刘起英应益明张玲娟莫建良施燕飞曹涯雁张铫房振华江雷张珩翟锦魏德法叶志会肖模龙
Owner 杭州蓝星新材料技术有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products