Preparation method of raw bamboo fiber needled-punched felt

A technology of bamboo fiber and production method, which is applied in the field of non-woven fabric manufacturing, can solve the problems of restricting the application and development of bamboo fiber, low monofilament strength of bamboo fiber, uneven web formation, etc., and achieve good antibacterial performance, smooth surface, and web formation uniform effect

Inactive Publication Date: 2009-11-11
福建鑫华股份有限公司
View PDF0 Cites 19 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] Due to the low strength, uneven thickness and fragility of bamboo fiber monofilament, it is difficult to card and un

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Example Embodiment

[0015] Example one:

[0016] The manufacturing method of the bamboo fiber needled felt of the present invention is realized by the following steps:

[0017] 1) Material preparation: prepare 30wt% bamboo fiber and 70wt% polyester fiber, the fineness of bamboo fiber and polyester fiber is 1-4D, and the length is 25-76mm;

[0018] 2) Opening and mixing: The raw bamboo fiber and polyester fiber are fed into the opening machine to maximize the fluffy state and mix them evenly;

[0019] 3) Carding: Feed the opened and mixed bamboo raw fiber and ester poly fiber to the carding machine for carding to form a fiber web. The feed line speed is 0.5m / min and the feed fiber amount is 2kg / m. 2 , The main cylinder frequency of the carding machine is 400r / min. During this process, the indoor temperature is controlled at 15°C and the relative humidity is controlled at 60%;

[0020] 3) Laying: Repeatedly overlap the fiber web obtained by carding to a weight of 200-450g / m 2 ;

[0021] 4) Acupuncture:...

Example Embodiment

[0024] Embodiment two:

[0025] The manufacturing method of the bamboo fiber needled felt of the present invention is realized by the following steps:

[0026] 1) Material preparation: prepare 95wt% of bamboo fiber and 5wt% of polypropylene fiber, the fineness of bamboo fiber and polypropylene fiber is 1-4D, and the length is 25-76mm;

[0027] 2) Opening and mixing: The raw bamboo fiber and polypropylene fiber are fed into the opening machine to maximize the fluffy state and mix them evenly;

[0028] 3) Carding: Feed the opened and mixed bamboo raw fiber and polypropylene fiber to the carding machine for carding to form a fiber web. The feed line speed is 1.5m / min and the feed fiber amount is 4kg / m. 2 , The main cylinder frequency of the carding machine is 800rpm / min. During this process, the indoor temperature is controlled at 28℃ and the relative humidity is controlled at 90%;

[0029] 3) Laying: Repeatedly overlap the fiber web obtained by carding to a weight of 200-450g / m 2 ; ...

Example Embodiment

[0033] Embodiment three:

[0034] The manufacturing method of the bamboo fiber needled felt of the present invention is realized by the following steps:

[0035] 1) Material preparation: prepare 60wt% bamboo raw fiber and 40wt% acrylic fiber, the fineness of bamboo raw fiber and acrylic fiber is 1-4D, and the length is 25-76mm;

[0036] 2) Opening and mixing: The raw bamboo fiber and acrylic fiber are fed into the opening machine to maximize the fluffy state and mix them evenly;

[0037] 3) Carding: feed the opened and mixed bamboo raw fiber and acrylic fiber to a carding machine for carding to form a fiber web, the feeding line speed is 1m / min, and the feeding fiber amount is 3kg / m 2 , The main cylinder frequency of the carding machine is 600rpm / min. During this process, the indoor temperature is controlled at 21℃ and the relative humidity is controlled at 75%;

[0038] 3) Laying: Repeatedly overlap the fiber web obtained by carding to a weight of 200-450g / m 2 ;

[0039] 4) Acupu...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
Finenessaaaaaaaaaa
Lengthaaaaaaaaaa
Thicknessaaaaaaaaaa
Login to view more

Abstract

The invention discloses a preparation method of raw bamboo fiber needled-punched felt. The raw bamboo fiber needled-punched felt is prepared by 30-95wt% of raw bamboo fiber and 5-70wt% of chemical fiber through opening, mixing, carding, lapping, needling, hot rolling and sizing procedures in sequence, wherein the carding procedure includes: the opened and mixed raw bamboo fiber and chemical fiber are fed into a carding machine for carding, so as to form a fiber web, the feeding line speed is 0.5-1.5m/min, the feeding fiber amount is 2-4kg/m, the main cylinder frequency of the carding machine is 400-800rpm/min, and the room temperature in the carding procedure is controlled to be 15-28 DEG C and relative humidity is controlled to be 60-90%, so as to effectively prevent raw bamboo fiber smash and breakage, thus solving the problems that the raw bamboo fiber is difficult to card and the formed web is not even in the prior art. By the method of the invention, the raw bamboo fiber needled-punched felt with evenly formed web, smooth surface, good antibacterial action and air permeability, and strong absorbability can be prepared.

Description

technical field [0001] The invention relates to the field of nonwoven fabric manufacture, in particular to a method for making bamboo fiber needle felt. Background technique [0002] Needle-punched felts manufactured by needle-punching technology in the non-woven field were mainly used in the field of flue gas dust removal in the past. In recent years, with the continuous development of the application of non-woven acupuncture technology, its application in the field of home textiles is also very extensive, such as interior decoration, clothing liners, shoemaking, etc. Its structure is mainly based on single-layer fiber structure , and form needle-punched felts or boards of different weights and thicknesses. The fibers used are usually chemical fibers, which have poor antibacterial properties, air permeability and moisture absorption properties. [0003] Bamboo fiber has excellent antibacterial properties, air permeability and hygroscopicity. Currently, the fibers made from...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): D04H1/48D06C7/02D04H1/4382D04H1/46
Inventor 郭秉臣黄清保杨道光粘伟诚洪明取
Owner 福建鑫华股份有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap