Experimental method for building forming limit diagram of transformation induced plasticity steel plate

A phase transformation-induced plasticity, forming limit diagram technology, applied in special data processing applications, instruments, electrical digital data processing, etc., can solve the problems of material, time, and labor.

Inactive Publication Date: 2009-12-09
NORTHEASTERN UNIV
View PDF0 Cites 7 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] The purpose of the present invention is to solve the shortcomings of the existing establishment of plate and strip forming limit diagrams that require standard test devices, preparation of test pieces of different widths, and changes in lubrication conditions, which are labor-intensive, material-intensive, and time-consuming. The thickness and str

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Experimental method for building forming limit diagram of transformation induced plasticity steel plate
  • Experimental method for building forming limit diagram of transformation induced plasticity steel plate
  • Experimental method for building forming limit diagram of transformation induced plasticity steel plate

Examples

Experimental program
Comparison scheme
Effect test

preparation example Construction

[0042]The preparation method of TRIP steel plate in the embodiment of the present invention is divided into two kinds: 1, low-carbon low-silicon steel is smelted into steel ingot, composition is to contain C0.18~0.20%, Mn1.30~1.45%, Si0.60~ 0.70%, Al0.50~0.60%, P≤0.009%, S≤0.007%, Nb≤0.040%, and the balance is Fe. After the steel ingot is kept at 1200°C for 1.5 to 2 hours, it is forged into a 30mm thick forging billet. Hot rolled to a thickness of 3.5mm, then cold rolled to a thickness of 1.0mm to obtain a cold-rolled steel plate, the cold-rolled steel plate was kept in a chloride salt at 800°C for 5 minutes, then quenched into a nitrate at a temperature of 400°C for 5 minutes, and air-cooled to room temperature, and prepared into TRIP steel plate. 2. Smelting low-carbon high-manganese steel into steel ingots, the chemical composition of which is C600ppm, Mn23.8%, Si3.0%, Al2.7%, and the balance is Fe. After the steel ingot is kept at 1150°C for 1.5 to 2 hours, it is forged ...

Embodiment 1

[0050] Firstly, the phase transformation induced plastic steel plate is prepared by smelting low-carbon silicon steel into steel ingots, the composition of which is C0.19%, Mn1.32%, Si0.70%, Al0.51%, P0.0068%, S0.0068% by weight %, the balance is Fe. After the steel ingot is kept at 1200°C for 1.5-2hrs, it is forged into a 30mm thick forging billet, hot rolled to a thickness of 3.5mm, and then cold rolled to a thickness of 1.0mm to obtain a cold rolled steel plate, which is then cut into small pieces of reasonable size. Blocks were kept in chloride salt at 800°C for 5 minutes, then quenched into nitrate at 400°C for 5 minutes, and cooled to room temperature in air to prepare TRIP steel plates.

[0051] Measure the strain hardening exponent n of this steel plate to be 0.323, t=1.0mm, calculate FLD according to formula (1) 0 = 0.576. Engineering Principal Strains e for Establishing Forming Limit Diagrams for Phase Transformation-Induced Plastic Steel Sheets 1 with engineering...

Embodiment 2

[0059] Firstly, the phase transformation induced plastic steel plate is prepared by smelting low-carbon silicon steel into steel ingots, and its composition is C0.18%, Mn1.38%, Si0.67%, Al0.56%, P0.0075%, S0.0048% by weight %, Nb0.014%, and the balance is Fe. After the steel ingot is kept at 1200°C for 1.5-2hrs, it is forged into a 30mm thick forging billet, hot rolled to a thickness of 3.5mm, and then cold rolled to a thickness of 1.0mm to obtain a cold rolled steel plate, which is then cut into small pieces of reasonable size. Blocks were kept in chloride salt at 800°C for 5 minutes, then quenched into nitrate at 400°C for 5 minutes, and cooled to room temperature in air to prepare TRIP steel plates.

[0060] Measure the strain hardening exponent n of this steel plate to be 0.325, t=1.0mm, calculate FLD according to formula (1) 0 = 0.580. Engineering Principal Strain e established by Forming Limit Diagram of Phase Transformation Induced Plastic Steel Sheet 1 with engineer...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
Strain hardening exponentaaaaaaaaaa
Strain hardening exponentaaaaaaaaaa
Strain hardening exponentaaaaaaaaaa
Login to view more

Abstract

The invention discloses an experimental method for building forming limit diagram of transformation induced plasticity steel plates, relating to the building method of forming limit diagrams. The method of the invention comprises the following steps: (1) the thickness and the strain hardening index of the transformation induced plasticity steel plate are determined; (2) the limit strain value of the transformation induced plasticity steel plate under the condition of plane strain state is calculated; (3) a strain coordinate system is built, data is synthesized on the coordinate system so as to build the forming limit diagram of the transformation induced plasticity steel plate. The invention is an effective tool for solving the transformation induced plasticity steel plate material punching problem, can successfully predict transformation induced plasticity steel plate material invalidation, effectively estimates the forming performance and reduces the existing measuring workload for building a shaping limit diagram.

Description

technical field [0001] The invention relates to a method for establishing a forming limit diagram of a steel plate, in particular to a model method for establishing a phase transformation-induced plastic forming limit diagram for a steel plate. Background technique [0002] TRIP (Transformation Induced Plasticity) steel, also known as phase transformation induced plasticity steel, is a high-strength and high-plasticity steel developed in recent years. Used as an automobile steel plate, it can reduce the weight of the vehicle and reduce fuel consumption. At the same time, it has a strong energy absorption capacity, can resist plastic deformation during impact, and significantly improves the safety level of the automobile. It has obvious advantages. Sheet metal forming is an important part of metal forming, and it is widely used in manufacturing industries such as aerospace, automobile, light industry and household appliances. In the sheet metal forming process, people urgent...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): G06F17/50
Inventor 唐正友丁桦
Owner NORTHEASTERN UNIV
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap