Dyeing pretreatment process for pineapple leaves-cotton blended knitted fabric

A technology for processing and knitted fabrics, which is applied in fiber processing, biochemical fiber processing, textiles and papermaking, etc. It can solve problems such as color difference, deep fiber background color, and high impurity content in pineapple leaf fibers, and achieve improved dyeing performance and level dyeing. Guaranteed, Unique Style Results

Inactive Publication Date: 2009-12-23
DONGHUA UNIV +2
View PDF0 Cites 3 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The disadvantage is that the extracted pineapple leaf fiber has a high content of impurities, which leads to a deep background color of the fiber after mercerizing, which is easy to cause color difference, which is not conducive to the printing and dyeing of pineapple leaf fabrics

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0014] Step 1. Soak (26s 160g) pineapple leaves and cotton blended knitted fabric in an oxygen bleaching solution with a temperature of 90° C. for 60 minutes. 125C), 1 g / L caustic soda (NaOH), 3 g / L hydrogen peroxide (H 2 o 2 ) mixed with ionized water.

[0015] Step 2. Soak the blended knitted fabric in an acetic acid solution with a temperature of 50° C. for 10 minutes. The acetic acid solution is composed of 1 g / L acetic acid (CH 3 COOH), 2 g / L deoxygenase (MD) and ionized water.

[0016] Step 3. Soak the blended knitted fabric in a soda ash solution with a temperature of 80° C. for 30 minutes. The soda ash solution is composed of hydrosulfite (Na 2 S 2 o 4 ), 6 g / L of soda ash (Na 2 CO 3 ) mixed with ionized water.

[0017] Step 4. Put the blended knitted fabric into a KMM-260 type singeing machine for gas singeing treatment, wherein the speed of the machine is 100 m / min, and the oil volume is 30.

Embodiment 2

[0019] Step 1, soaking (32s 145g) pineapple leaves and cotton blended knitted fabrics in an oxygen bleaching solution with a temperature of 100°C for 60 minutes, the oxygen bleaching solution is composed of 3 grams per liter of refining agent (TF- 125C), 3 g / L caustic soda (NaOH), 1 g / L hydrogen peroxide (H 2 o 2 ) mixed with ionized water.

[0020] Step 2. Soak the blended knitted fabric in an acetic acid solution with a temperature of 50° C. for 10 minutes. The acetic acid solution is composed of 3 g / L acetic acid (CH 3 COOH), 1 g / L deoxygenase (MD) and ionized water.

[0021] Step 3. Soak the blended knitted fabric in a soda ash solution with a temperature of 80° C. for 30 minutes. The soda ash solution is composed of hydrosulfite (Na 2 S 2 o 4 ), 12 g / L of soda ash (Na 2 CO 3 ) mixed with ionized water.

[0022] Step 4. Put the blended knitted fabric into a KMM-260 type singeing machine for gas singeing treatment, wherein the speed of the machine is 100 m / min, and ...

Embodiment 3

[0024] Step 1, soaking (40s 120g) pineapple leaves and cotton blended knitted fabrics in an oxygen bleaching solution with a temperature of 95°C for 60 minutes, the oxygen bleaching solution is composed of a refining agent (TF- 125C), 3 g / L caustic soda (NaOH), 3 g / L hydrogen peroxide (H 2 o 2 ) mixed with ionized water.

[0025] Step 2. Soak the blended knitted fabric in an acetic acid solution with a temperature of 50° C. for 10 minutes. The acetic acid solution is composed of 3 g / L acetic acid (CH 3 COOH), 1 g / L deoxygenase (MD) and ionized water.

[0026] Step 3. Soak the blended knitted fabric in a soda ash solution with a temperature of 80° C. for 30 minutes. The soda ash solution is composed of hydrosulfite (Na 2 S 2 o 4 ), 10 g / L of soda ash (Na 2 CO 3 ) mixed with ionized water.

[0027] Step 4. Put the blended knitted fabric into the KMM-260 type singeing machine for gas singeing treatment, wherein the vehicle speed is 100 m / min, and the oil volume is 25.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention provides a dyeing pretreatment process for pineapple leaves-cotton blended knitted fabric. The process is characterized by comprising the following steps: 1, soaking the pineapple leaves-cotton blended knitted fabric in oxygen bleaching solution at a temperature between 90 and 100 DEG C for 60 minutes; 2, soaking the blended knitted fabric in acetate solution at 50 DEG C for 10 minutes; 3, soaking the blended knitted fabric in soda solution at 80 DEG C for 30 minutes; and 4, feeding the blended knitted fabric into a KMM-260 singeing machine and performing gas singeing treatment,wherein the vehicle speed is 100 meters per minute, and the amount of oil is between 25 and 30. The process has the advantages of significantly promoting the dyeing properties of the pineapple leaves-cotton blended knitted fabric subjected to the pretreatment and guaranteeing color vividness, color fastness and level dyeing property thereof; in addition, the knitted fabric integrates the excellent performances of pineapple leaves and cotton and has a unique style.

Description

[0001] technical scope [0002] The invention relates to a pre-dyeing treatment process of pineapple leaf and cotton blended knitted fabrics. technical background [0003] According to the test report analysis, pineapple leaf fiber is the natural fiber with the best bactericidal properties found so far. After deep processing, the pineapple leaf fiber has a white appearance, soft and smooth, and can be blended with natural fibers or synthetic fibers. The woven fabric is easy to print and dye, sweat-absorbent and breathable, crisp and wrinkle-free, very comfortable to wear, especially suitable for tropical areas living people. In addition to the above advantages, pineapple leaf fiber also has strong natural bactericidal and antibacterial functions, which can effectively kill bacteria and inhibit the growth of fungi and microorganisms. The disadvantage is that the extracted pineapple leaf fiber has a high content of impurities, which leads to a deep background color of the fibe...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): D06L3/02D06M13/188D06M11/76D06C9/00D06M16/00C12S11/00D06M101/06D06L4/12D06L4/13
Inventor 翁荣弟刘爱莲柴红梅金光明徐永康陈光杰程隆棣余燕平张瑞寅
Owner DONGHUA UNIV
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products